Composite porous membrane material filled with silica particles and its preparation method and application

A technology of silica and membrane materials, which is applied in the direction of electrical components, circuits, battery pack components, etc., can solve the problems of high porosity, micro-short circuit, low battery charge retention rate, etc., and achieve the effect of resisting mechanical impact

Active Publication Date: 2017-07-11
JIANGXI ADVANCED NANOFIBER S&T CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since this electrospun nanofiber separator is a non-woven fabric stacked by fibers, it has too high porosity and too large surface pore size, resulting in a low charge retention rate of the battery and frequent micro-short circuits. Especially when the thickness of the battery separator is low, such as below 30 microns, the probability of this situation is quite high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A containing SiO 2 A composite membrane material of micro-nano particles, which uses electrospun polyimide (PI) nanofiber nonwovens as the substrate, and the pores of the substrate are filled with SiO 2 Micronanoparticles (SiO 2 -NP);

[0037] Its preparation method is as follows:

[0038] (1) Nano SiO 2 Water-based suspension (SiO 2 / H 2 O-1) configuration: 80.0 grams of silicon dioxide powder (mainly distributed in diameter of 80 nm), 0.8 grams of ammonium polyacrylate, 8.0 grams of butyl acrylate-isooctyl acrylate copolymer, 300.0 grams of distilled water, put them in a beaker at one time, Emulsified at a speed of 8000 rpm to form a water-based suspension of nano-silicon dioxide (SiO 2 / H 2 O-1).

[0039] (2) SiO 2 Preparation of / PI nanocomposite high-temperature resistant and high-safety battery separator: the above-configured SiO 2 / H 2 The O-1 silica water-based suspension was spread flat on a glass plate to form a suspension film with a thickness of 4...

Embodiment 2

[0042] A containing SiO 2 A composite membrane material of nanoparticles, which uses electrospun polyimide (PI) nanofiber nonwovens as the substrate, and the pores of the substrate are filled with SiO 2 Nanoparticles (SiO 2 -NP);

[0043] Its preparation method is as follows:

[0044] (1) Submicron SiO 2 Water-based suspension (SiO 2 / H 2 O-2) Configuration: 80.0 grams of silicon dioxide powder (mainly distributed in diameter of 500 nm), 0.6 grams of ammonium polyacrylate, 8.0 grams of butyl acrylate-isooctyl acrylate copolymer, 300.0 grams of distilled water, put them in a beaker at one time, Emulsify at a speed of 8000 rpm to form a submicron silica water-based suspension (SiO2) with an absolute viscosity of 20 mPa·S 2 / H 2 O-2).

[0045] (2) SiO 2 Preparation of / PI micro-nano composite high-temperature-resistant high-safety battery separator: the above-configured SiO 2 / H 2 The O-2 silica water-based suspension was spread flat on a glass plate to form a suspensi...

Embodiment 3

[0048] A containing SiO 2 A composite membrane material of nanoparticles, which uses electrospun polyimide (PI) nanofiber nonwovens as the substrate, and the pores of the substrate are filled with SiO 2 Nanoparticles (SiO 2 -NP);

[0049] Its preparation method is as follows:

[0050] (1) Micron SiO 2 Water-based suspension (SiO 2 / H 2 O-3) Configuration: 80.0 grams of silicon dioxide powder (mainly distributed in diameter of 800 nm), 0.5 grams of ammonium polyacrylate, 8.0 grams of butyl acrylate-isooctyl acrylate copolymer, 300.0 grams of distilled water, put them in a beaker at one time, Emulsify at a speed of 10,000 revolutions per minute to form a micron silicon dioxide water-based suspension (SiO 2 / H 2 O-3).

[0051] (2) SiO 2 Preparation of / PI micro-nano composite high-temperature-resistant high-safety battery separator: the above-configured SiO 2 / H 2 The O-3 silica water-based suspension was spread on a glass plate to form a suspension film with a thickne...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a micro-nano composite multi-curvature membrane material, which uses polyimide (PI) nanofiber non-woven fabric as a base material, and the pores of the base material are filled with micro-nano silica particles; the micro-nano silica particles Nanosilica particles have a diameter between 50-800nm, accounting for 20-50% of the total weight of the micro-nano composite multi-curved membrane material; the thickness of the PI nanofiber non-woven fabric is between 9-38μm, and the pores The rate is between 60‑80%. The micro-nano composite multi-curved hole membrane material provided by the invention is resistant to high temperature, thermal shrinkage, high voltage and high current impact, and mechanical impact resistance, and is suitable for use as a safety battery separator and a safety supercapacitor separator to manufacture various high-capacity and High power lithium battery or supercapacitor. The invention also provides a preparation method of the micro-nano composite multi-curvature membrane material and its application as a battery separator.

Description

technical field [0001] The invention belongs to the field of battery separators and relates to a porous membrane material, in particular to a membrane containing SiO 2 A composite porous membrane material of micro-nano particles, a preparation method thereof, and an application as a battery separator. Background technique [0002] As the power battery of new energy vehicles, lithium-ion batteries have been developed rapidly and will become an indispensable daily necessities for human beings. However, since the currently used lithium battery separator is a polyolefin porous membrane material with poor temperature resistance, at a higher temperature, or in the case of overcharging, overdischarging and mechanical damage, lithium-ion batteries are prone to smoke, Fire, even explosion and other hidden dangers that endanger the safety of users. Therefore, improving the safety of lithium-ion batteries is the key to promoting the application of lithium-ion batteries in automotive ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)