Production method for alloy filament

A production method and alloy wire technology are applied in the field of 4J42 alloy wire manufacturing, which can solve the problems affecting the scientificity and rationality of the production process, and achieve the effects of improving the purity and the uniformity of the structure, good plasticity and improving the surface quality.

Inactive Publication Date: 2016-01-27
丹阳市凯鑫合金材料有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no systematic research on the production process of 4J42 alloy wire specifically for the electrode cap used in electric discharge tubes, which directly affects the scientificity and rationality of the production process of this product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] A kind of production method of 4J42 alloy wire for discharge tube electrode, concrete steps are as follows:

[0040] 1. Vacuum melting:

[0041] (1) Preparation of raw materials: The charge is Jinchuan Ni plate and ultra-low carbon material, which are baked and used for later use;

[0042] (2) Loading: Load the baked raw material Jinchuan Ni plate and ultra-low carbon charge into the vacuum induction melting furnace;

[0043] (3) Refining: low-power chemical material, after melting 70%, increase the power to melt at a high speed, and enter the refining period after reaching the refining temperature of 1600°C after full melting, and keep refining for at least 30 minutes;

[0044](4) Casting: Turn to low vacuum (103-10-1Pa) in the later stage of refining, stir with high power for one minute to tap the steel, and pour the electrodes. The steel drum used should be clean, free from cold steel and residue, and there should be no unburned black ash and oily smoke on the plug...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a 4J42 alloy filament for a discharge tube electrode and a production method for the alloy filament. The production method comprises the following steps: pouring a 4J42 raw material into a vacuum furnace for making steel and forming an ingot; performing forging cogging and hot rolling to form a wire rod; performing acid washing processing on the wire rod subjected to hot rolling; polishing and trimming after acid washing, and performing first drawing; performing annealing processing on a semi-finished product subjected to first drawing; performing acid washing and grinding on the semi-finished product subjected to annealing processing; performing secondary drawing after no crack is determined to exist; performing hot-processing annealing on the wire rod subjected to secondary drawing; detecting the case of the wire rod surface again, performing crude-filament finish drawing, performing hot processing after each time of the wire rod being drawn and entering a next specification, and stopping untie the wire rod reaches the finished-product dimension. According to the technical scheme, based on the real demands on the discharge tube electrode, various factors influencing 4J42 plasticity and rolling yield during production are researched and found, and the defects that 4J42 is bad in plasticity, low in rolling yield and the like in the subsequent processing process are solved by improving the 4J42 production technology.

Description

technical field [0001] The invention relates to a production method of 4J42 alloy wire, in particular to a production method of 4J42 alloy wire for discharge tube electrodes. Background technique [0002] 4J42 alloy belongs to the expansion alloy in the precision alloy, the nickel content is about 42%, the rest is mainly iron, and has a stable low expansion coefficient (the average expansion coefficient at room temperature is 1.6X10 -6 / °C), it is widely used in aerospace, precision instruments, and electronics industries, and its main purpose is to produce electrodes for discharge tubes. Discharge tubes are used to protect the safe operation of communication systems, traffic signal systems, computer data systems, external cables and electronic instruments of various electronic equipment. At present, no other material can replace this traditional vacuum sealing material. Although the market demand for 4J42 is huge, the product quality of most domestic manufacturers fluctua...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/10B22D23/10B21C37/04
Inventor 荆正伟钟静
Owner 丹阳市凯鑫合金材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap