Film formation composition and sets containing the same

A composition and film-forming technology, applied in the direction of skin care preparations, cosmetics, cosmetic preparations, etc., to achieve the effect of easy removal

Inactive Publication Date: 2016-02-03
CLOUDTAIN INT BIOTECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although these natural gums share many similar properties, there are still considerable differences

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Film formation composition and sets containing the same
  • Film formation composition and sets containing the same
  • Film formation composition and sets containing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Embodiment 1: Preparation and property comparison of the 3-component colloid of the present invention.

[0042] This example attempts to prepare film-forming compositions with different three-ingredient distribution ratios. The composition ratio of the samples of this embodiment is shown in the table below, and the film forming speed and tear-off ease of each sample are recorded in each table (evaluated according to Table 1 below). In this embodiment, polyolefins are commercially available products: PVA205 (polyvinyl alcohol) and PVPK-90 (polyvinylpyrrolidone). According to the product description, the weight average molecular weight of PVA205 is 27,000-35,000, the degree of alkalization is 86-89, and the viscosity at room temperature is 5-6; the weight average molecular weight of PVPK-90 is 3.6 million.

[0043] Film-forming agent is to adopt commercially available product Fixomer in the present embodiment TM A-30 Polymer (Lubrizol, according to its instructions for ...

Embodiment 2

[0059] Embodiment 2: Preparation and property comparison of the 4-component colloid of the present invention.

[0060] This example attempts to prepare film-forming compositions with different distribution ratios of the four components, and attempts to add pigments, whitening, maintenance (such as moisturizing, anti-aging, etc.) and other substances. The composition ratio of the samples of this embodiment is shown in the following table, and the film forming speed and tear-off ease of each sample are recorded in each table (evaluated according to Table 1 above). In this embodiment, polyolefins are commercially available products: PVA205 (polyvinyl alcohol) and PVPK-90 (polyvinylpyrrolidone). Film-forming agent is to adopt commercially available product Fixomer TM A-30 Polymer (Lubrizol, according to its instructions, the product contains: methacrylate-methacrylic acid copolymer) and / or the commercially available product EPITEX TM 66 (Dow Home, Institutional and Personal Care...

Embodiment 3

[0070] Embodiment three: preparation and property comparison of the colloid of the present invention.

[0071] Based on the above experimental content, it can be seen that the 3-component colloid of the present invention has good properties, and the further tested 4-component and 5-component colloids also have improved film forming speed and tear-off ease. In this embodiment, the effects of film-forming agent and surfactant on film-forming speed and tear-off ease will be further tested.

[0072] The composition ratio of the samples in this embodiment is shown in the table below, and the film-forming speed and tear-off ease of each sample are recorded in the table (evaluated according to Table 1 above). In this embodiment, polyolefins are commercially available products: PVA205 (polyvinyl alcohol) and PVPK-90 (polyvinylpyrrolidone). The film-forming agent is a commercially available product AquaSF-1OSPolymer (Lubrizol, according to its instructions for use, this product conta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides a film formation composition and sets containing the same. The film formation composition comprises polyolefin, filmogen and an interfacial agent in a particular mix ratio. The film formation composition has excellent film formation speed and strength so as to be a medium used for transferring materials to the user's surface.

Description

technical field [0001] The present invention relates to a film-forming composition and a set containing it, in particular to a film-forming composition composed of several polymers and a set containing it. Background technique [0002] The use of colloids is very common in beauty products. Many natural gums with high biocompatibility are known in the field, such as: Carrageenan (Carrageenan), Sanxian Gum (Xantham Gum), Locust Bean Gum (Locust Bean Gum), Gellan Gum (Gellan Gum), sodium alginate, konjac powder, Gelatin, gum arabic, agar, dextrin, zein, β-glucan, starch, glycogen, cellulose, hyaluronic acid (Hyaluronan, hyaluronic acid), chitin (Chitn), etc. Due to their excellent biocompatibility, these natural gums are widely used as carriers or substrates in various medical or cosmetic purposes. [0003] Although these natural gums share many similar properties, there are considerable differences. Therefore, according to different applications, it is necessary to select, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L29/04C08L39/06C08L33/10C08L33/08C08K5/053C08J5/18A61K8/81A61K8/73A61K8/65A61K8/92A61K8/86A61K8/37A61K8/34A61Q19/00A61Q3/02
Inventor 廖妍羚许羽伶
Owner CLOUDTAIN INT BIOTECH