Epoxy resin material with strong corrosion resistance and method for preparing integral core-penetrating plate by using same

An epoxy resin matrix, epoxy resin technology, applied in the field of building materials, can solve the problems of deformation of the entire table, the basic material can not be anti-corrosion, time-consuming, labor-intensive and financial-intensive

Active Publication Date: 2016-02-03
南通联鑫新材料科技有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The countertops in high-end laboratory furniture are still used in the market today, such as cement tiles, melamine boards with anti-corrosion rubber, laminated physical and chemical boards, natural marble, and ceramic boards. One of the common points of the above boards is That is, there is only a very thin layer of anti-corrosion on the surface of the material, and the base material cannot be anti-corrosion. If the surface is damaged, the entire countertop will be deformed, bent, and cracked until the countertop is replaced. This may cause damage to personnel and equipment, and the countertop needs to be replaced. Time-consuming, laborious and costly, resulting in a great waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy resin material with strong corrosion resistance and method for preparing integral core-penetrating plate by using same
  • Epoxy resin material with strong corrosion resistance and method for preparing integral core-penetrating plate by using same
  • Epoxy resin material with strong corrosion resistance and method for preparing integral core-penetrating plate by using same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Embodiment 1 A method for preparing an epoxy resin integrated through-core board, comprising the following steps:

[0032] Step 1. Stir and preheat 19.2 parts of bisphenol A epoxy resin matrix, 20 parts of epoxy resin curing agent triethylamine and 58 parts of 500-mesh quartz sand at a speed of 65-75 rpm to 75-85°C , 80~85℃, 65~75℃, standby;

[0033] Step 2. Put the preheated bisphenol A epoxy resin matrix into the reaction kettle preheated to 70-80°C, add the preheated quartz sand, stir for 1-2 hours, and then put in the preheated triethylamine amine;

[0034] Step 3, after stirring the mixture obtained in Step 2 for 1 to 2 hours, put in 1 part of epoxy resin thinner toluene and 1.3 parts of red color paste;

[0035] Step 4. After stirring the mixture obtained in the previous step for 0.2-1 hour, put in 0.5 parts of silane coupling agent, react for 10-30 minutes and pour it into a mold preheated to 100-130°C while it is hot, heat insulation and raise the temperature ...

Embodiment 2

[0036] Embodiment 2 A method for preparing an epoxy resin integrated through-core board, comprising the following steps:

[0037] Step 1. Stir and preheat 20 parts of brominated bisphenol A epoxy resin matrix, 19.2 parts of epoxy resin curing agent boron trifluoride and 56 parts of 400-mesh quartz sand at a speed of 65 to 75 rpm to 75 ~85℃, 80~85℃, 65~75℃, standby;

[0038] Step 2. Put the preheated brominated bisphenol A epoxy resin matrix into the reaction kettle preheated to 70-80°C, add half the weight of the preheated quartz sand, stir for 1-2 hours, and then put it into the preheated The final epoxy resin curing agent boron trifluoride and the remaining quartz sand;

[0039] Step 3, after stirring the mixture obtained in Step 2 for 1 to 2 hours, put in 0.5 parts of epoxy resin diluent xylene and 3.8 parts of black color paste;

[0040] Step 4. After stirring the mixture obtained in Step 3 for 0.2-1 hour, put in 0.5 parts of silane coupling agent, react for 10-30 minute...

Embodiment 3

[0049] Embodiment 3 A method for preparing an epoxy resin integrated through-core board, comprising the following steps:

[0050] Step 1, 9.2 parts of bisphenol A epoxy resin matrix, 10 parts of brominated bisphenol A epoxy resin matrix, 20 parts of epoxy resin curing agent acetic anhydride and 56 parts of 600-mesh quartz sand at 65 to 75 rpm Stir and preheat to 75-85°C, 80-85°C, 65-75°C at a certain speed, and set aside;

[0051] Step 2. Put the preheated bisphenol A epoxy resin matrix and brominated bisphenol A epoxy resin matrix into a reaction kettle preheated to 70-80°C, add half the weight of preheated quartz sand, and stir After 1 to 2 hours, put in the preheated epoxy resin curing agent m-phenylenediamine and the remaining quartz sand;

[0052] Step 3. After stirring the mixture obtained in the previous step for 1 to 2 hours, put in 1 part of epoxy resin diluent ethyl acetate and 3.3 parts of blue color paste;

[0053] Step 4. After stirring the mixture obtained in t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an epoxy resin material with strong corrosion resistance, and a method for preparing an integral core-penetrating plate by using the same. The epoxy resin material comprises the following components: an epoxy resin matrix, an epoxy resin curing agent, quartz sand, an epoxy resin diluent, a coupling agent and color paste. The method for preparing the core-penetrating plate comprises the following steps: pre-heating the epoxy resin matrix, the epoxy resin curing agent and the quartz sand, respectively; putting the pre-heated epoxy resin matrix in a pre-heated reaction kettle, adding the pre-heated quartz sand with half in weight, stirring the mixture, and then inputting the pre-heated epoxy resin curing agent and residual quartz sand; after stirring the mixture, inputting the epoxy resin diluent and the color paste; and after stirring the mixture, inputting a crosslinking agent, injecting the mixture into a pre-heated die after reaction, isolating heat and carrying out crystallization and deforming reactions sequentially, then reducing the temperature to 170-200 DEG C and preserving the temperature for 3-4 hours, and finally, cooling the mixture to room temperature to obtain a product. The product disclosed by the invention is durable. If damages are produced on the surface, the product can be directly repaired like a new one.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to an epoxy resin material with strong corrosion resistance and a method for preparing an integral through-core board by using the epoxy resin material. Background technique [0002] The countertops in high-end laboratory furniture are still used in the market today, such as cement tiles, melamine boards with anti-corrosion rubber, laminated physical and chemical boards, natural marble, and ceramic boards. One of the common points of the above boards is That is, there is only a very thin layer of anti-corrosion on the surface of the material, and the base material cannot be anti-corrosion. If the surface is damaged, the entire countertop will be deformed, bent, and cracked until the countertop is replaced. This may cause damage to personnel and equipment, and the countertop needs to be replaced. It is time-consuming, laborious and expensive, resulting in a gre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L63/02C08L63/04C08K3/36C08G59/50C08G59/40C08G59/42
Inventor 陈卫锋陈卫华
Owner 南通联鑫新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap