Binder for casting and preparation method thereof

A technology of binder and casting, applied in the field of binder for casting and its preparation, can solve the problems of easy generation of volatile gas, short service life of organic binder, low temperature resistance, etc. Good bond strength, the effect of broadening the application range

Active Publication Date: 2016-02-03
陆河南方机械铸造有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved is: in order to solve the shortcomings of organic binders such as short service life, low temperature resistance and easy generation of volatile gas, to provide a high temperature decomposition resistant casting binder and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Binder for casting and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A binder for castings, which consists of the following components in parts by weight: 40 parts of furfuryl alcohol resin, 25 parts of bisphenol A epoxy resin, 13 parts of hydroxyethyl methylcellulose, ethylene glycol di 9 parts of acetate, 6 parts of diethyl aminomalonate, 16 parts of diluent, 2 parts of palm oil, 3 parts of magnesium oxide, 5 parts of antimony trioxide, 5 parts of sodium peroxide, 10 parts of absolute ethanol and 8 parts of ionized water.

[0019] The diluent is 1,6-hexanediol diglycidyl ether.

[0020] The above-mentioned preparation method of a casting binder, the preparation steps are as follows:

[0021] Step 1: Put furfuryl alcohol resin, bisphenol A type epoxy resin and diluent in the reaction kettle and stir and mix. The temperature of the reaction kettle is set at 40°C;

[0022] Step 2: then add ethylene glycol diacetate and diethyl aminomalonate successively and continue stirring;

[0023] Step 3: Then add palm oil and keep stirring to mix ...

Embodiment 2

[0026] A binder for castings, which consists of the following components in parts by weight: 60 parts of furfuryl alcohol resin, 42 parts of bisphenol A epoxy resin, 20 parts of hydroxyethyl methylcellulose, ethylene glycol di 7 parts of acetate, 14 parts of diethyl aminomalonate, 24 parts of thinner, 4 parts of palm oil, 9 parts of magnesium oxide, 12 parts of antimony trioxide, 11 parts of sodium peroxide, 18 parts of absolute ethanol and 14 parts of ionized water.

[0027] The diluent is phenyl glycidyl ether.

[0028] The above-mentioned preparation method of a casting binder, the preparation steps are as follows:

[0029] Step 1: Put furfuryl alcohol resin, bisphenol A type epoxy resin and diluent in the reactor and stir and mix, and the temperature of the reactor is set at 55°C;

[0030] Step 2: then add ethylene glycol diacetate and diethyl aminomalonate successively and continue stirring;

[0031] Step 3: Then add palm oil and keep stirring to mix evenly;

[0032] ...

Embodiment 3

[0034] A binder for castings, which consists of the following components in parts by weight: 50 parts of furfuryl alcohol resin, 34 parts of bisphenol A epoxy resin, 16 parts of hydroxyethyl methylcellulose, ethylene glycol di 13 parts of acetate, 10 parts of diethyl aminomalonate, 20 parts of diluent, 3 parts of palm oil, 6 parts of magnesium oxide, 8 parts of antimony trioxide, 8 parts of sodium peroxide, 14 parts of absolute ethanol and 11 parts of ionized water.

[0035] The diluent is phenyl glycidyl ether.

[0036] The above-mentioned preparation method of a casting binder, the preparation steps are as follows:

[0037] Step 1: Put furfuryl alcohol resin, bisphenol A type epoxy resin and diluent in the reaction kettle and stir and mix. The temperature of the reaction kettle is set at 42°C;

[0038] Step 2: then add ethylene glycol diacetate and diethyl aminomalonate successively and continue stirring;

[0039] Step 3: Then add palm oil and keep stirring to mix evenly;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a binder for a casting. The binder comprises furfuryl alcohol resin, bisphenol A epoxy resin, hydroxyethylmethylcellulose, ethylene glycol diacetate, aminomalonic acid diethyl ester, a diluent, palm oil, magnesium oxide, antimonony oxide, sodium peroxide, anhydrous ethanol and deionized water according to a weight part ratio. The invention also discloses a preparation method of the binder. The binder has high high-temperature resistance, is suitable for materials with high requirements on a modeling sand temperature and further widens an application scope.

Description

technical field [0001] The invention belongs to the field of casting processing, and in particular relates to a binder for castings and a preparation method thereof. Background technique [0002] A binder is a substance that firmly bonds various solid materials together by interfacial action (chemical force or physical force). Adhesives are widely used in construction, machining, electronic products and other fields. Foundry binder is to form granular or powder molding materials into a continuous adhesive film with a certain strength to form a mold. With the advancement of technology, foundry binders have developed from the original natural binder-clay to today's synthetic binders such as organic, inorganic and composite binders. Among them, the organic binder has the advantages of convenient use, good adhesion, and low cost, and is the most widely used. However, the organic binder also has a short service life and is not resistant to high temperatures, especially at high ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L71/14C08L63/00C08L1/28C08L91/00C08K13/02C08K5/103C08K5/17C08K3/22B22C1/16B22C1/22
Inventor 姚振红
Owner 陆河南方机械铸造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com