High temperature-resisting, fire-retardant and flame-retardant paint
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A fire-retardant, high-temperature-resistant technology, used in fire-resistant coatings, coatings, conjugated diene coatings, etc., can solve the problems of unsatisfactory fire resistance, easy softening and peeling of paint, etc. Good results
Inactive Publication Date: 2016-04-06
QINGDAO DAFANG WISDOM NETWORK TECH CO LTD
View PDF0 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The existing paint is easy to soften and fall off under high temperature, and t
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Example Embodiment
[0010] Example 1
[0011] A high-temperature, fire-retardant and flame-retardant paint made of the following mass parts of raw materials:
[0012] 8 parts of xylene, 10 parts of diethyl maleate, 5 parts of phenoxycarboxylic acid, 7 parts of thermoplastic polyimide, 6 parts of silica bath clay, 35 parts of styrene butadiene rubber, 12 parts of n-butyl stearate Parts, 7 parts of chlorinated paraffin, 6 parts of antimony oxide, 5 parts of zeolite powder, 7 parts of asbestos, 6 parts of magnesium hydroxide, 2 parts of water glass, 10 parts of acrylic resin.
Example Embodiment
[0013] Example 2
[0014] The above-mentioned high-temperature resistant, fire-retardant and flame-retardant paint is made of the following raw materials:
[0015] 10 parts of xylene, 12 parts of diethyl maleate, 6 parts of phenoxycarboxylic acid, 9 parts of thermoplastic polyimide, 7 parts of silica bath clay, 37 parts of styrene butadiene rubber, 14 parts of n-butyl stearate Parts, 8 parts of chlorinated paraffin, 6.5 parts of antimony oxide, 7 parts of zeolite powder, 8 parts of asbestos, 6.6 parts of magnesium hydroxide, 4 parts of water glass, 13 parts of acrylic resin.
Example Embodiment
[0016] Example 3
[0017] A high-temperature, fire-retardant and flame-retardant paint made of the following mass parts of raw materials:
[0018] 11 parts of xylene, 14 parts of diethyl maleate, 7 parts of phenoxycarboxylic acid, 11 parts of thermoplastic polyimide, 8 parts of silica bath clay, 40 parts of styrene butadiene rubber, 16 parts of n-butyl stearate Parts, 9 parts chlorinated paraffin, 7 parts antimony oxide, 8 parts zeolite powder, 10 parts asbestos, 7 parts magnesium hydroxide, 6 parts water glass, 15 parts acrylic resin.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses high temperature-resisting, fire-retardant and flame-retardant paint. The high temperature-resisting, fire-retardant and flame-retardant paint is prepared from the following raw materials in parts by mass: 8 to 11 parts of xylene, 10 to 14 parts of diethyl maleate, 5 to 7 parts of phenoxy carboxylic acid, 7 to 11 parts of thermoplastic polyimide, 6 to 8 parts of diatomite, 35 to 40 parts of butadiene styrene rubber, 12 to 16 parts of n-butyl stearate, 7 to 9 parts of chlorinated paraffin, 6 to 7 parts of antimony oxide, 5 to 8 parts of zeolite powder, 7 to 10 parts of asbestos, 6 to 7 parts of magnesium hydroxide, 2 to 6 parts of sodium silicate and 10 to 15 parts of acrylic resin. The high temperature-resisting, fire-retardant and flame-retardant paint provided by the invention is high temperature-resisting, is not easy to degum, has no cracking, is economic and environment-friendly and has good fire retardancy and flame retardancy.
Description
technical field [0001] The invention relates to the technical field of chemical industry, in particular to a high-temperature-resistant, fire-resistant and fuel-resistant paint. Background technique [0002] Paint plays an important role in our lives. Because objects are exposed to the atmosphere, they are eroded by oxygen, moisture, etc., causing metal corrosion, wood decay, and cement weathering. Paint the surface of the object to form a protective film, which can prevent or delay the occurrence and development of these damage phenomena, and prolong the service life of various materials. The existing paint is easily softened and peeled off by high temperature, and its fireproof performance is not ideal, which causes many troubles for usability. Contents of the invention [0003] In order to solve the above existing problems, the present invention provides a high temperature resistant and not easy to detach. No cracking, economical and environmentally friendly, high tem...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more