Manufacturing method of gold and silver double-color pattern crystal standing table

A production method and pattern technology, which are applied in special decorative structures, metal material coating processes, and processes for producing decorative surface effects, etc., can solve problems such as monotony and lack of three-dimensional effects, and achieve improved three-dimensional sense and appearance fluctuation. Small, reproducible results

Active Publication Date: 2016-04-13
南通好汉邦新材料科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Simple gold/silver plating on the crystal surface is too monotonous and has no three-dimensional effect. People h

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] After cleaning a circular crystal table, magnetron sputtering a layer of 200nm thick chrome-copper seed layer, wherein the chromium layer is 50nm thick, and the copper layer is 150nm thick; spin-coat a A layer of photoresist with a thickness of 50 μm covers the first mask plate with fine patterns, and selectively lithography the central area of ​​the table to expose the first mask pattern. It should be noted that the area of ​​the central area is based on the first The area selection of pattern in the mask plate; Electroplate silver on the window of the first mask pattern, wherein the electrolytic solution of silver plating comprises silver sulfite 30g / L, sodium thiosulfate 150g / L, sodium sulfite 20g / L, lemon Acid 35g / L, succinimide 40g / L, nicotinic acid 5g / L, the pH of the electroplating solution is 5, and the current density is 0.3A / dm 2 After the electroplating is completed, the thickness of the silver layer obtained is 55 μm, and the top of the silver layer is frost...

Embodiment 2

[0025] After cleaning an oval crystal table, magnetron sputtering a layer of 200nm thick chrome-copper seed layer, wherein the chromium layer is 70nm thick, and the copper layer is 130nm thick; spin-coat a A layer of photoresist with a thickness of 50 μm covers the first mask plate with fine patterns, and selectively lithography the central area of ​​the table to expose the first mask pattern. It should be noted that the area of ​​the central area is based on the first The area selection of pattern in the mask plate; Electroplating silver on the window of the first mask pattern, wherein the electrolyte of electroplating silver comprises silver sulfite 18g / L, sodium thiosulfate 100g / L, sodium sulfite 10g / L, lemon Acid 20g / L, succinimide 20g / L, nicotinic acid 1g / L, the pH of the electroplating solution is 6.1, and the current density is 0.3A / dm 2 . After the electroplating is completed, the thickness of the silver layer obtained is 52 μm, and the top of the silver layer is fros...

Embodiment 3

[0028] After cleaning a square crystal table, magnetron sputtering a layer of 200nm thick chrome-copper seed layer, wherein the chromium layer is 50nm thick, and the copper layer is 150nm thick; spin coat a layer on the table with the sputtered seed layer The photoresist with a thickness of 50 μm covers the first mask plate with a fine pattern, and selectively photolithography is carried out in the central area of ​​the table to expose the first mask pattern. It should be noted that the area of ​​the central area depends on the size of the first mask Area selection of patterns in the stencil; electroplating silver on the window of the first mask pattern, wherein the electrolyte for electroplating silver includes silver sulfite 22g / L, sodium thiosulfate 132g / L, sodium sulfite 18g / L, citric acid 30g / L, 30g / L succinimide, 4g / L nicotinic acid, the pH of the electroplating solution is 6.4, and the current density is 0.3A / dm. After the electroplating is completed, the thickness of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Current densityaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method of a gold and silver double-color pattern crystal standing table. The method comprises the following steps that a chromium copper seed layer is obtained through magnetron sputtering; photoresist spin coating is carried out, selective photoetching is carried out in the middle zone of the standing table, and a first mask pattern is exposed; electrosilvering is carried out on a window of the first mask pattern till the top end of a silver layer exceeds the plane of a photoresist mask, and dull polish treatment is carried out on the top end of the silver layer till the top end of the silver layer is flush with the surface of photoresist; a second mask pattern is used for carrying out selective photoetching in the annular edge area of the standing table, and a second mask pattern is exposed; electrogilding is carried out on a window of the second mask pattern, and an electrogilding layer is obtained; and the standing table is arranged in acetone, glue removing is carried out through ultrasounds, and cleaning and drying are carried out. The crystal standing table obtained through the manufacturing method is rich and diverse in pattern and color. The third dimension of a product is high, the method repeatability is good, and the manufacturing method is suitable for industrial batch production.

Description

technical field [0001] The invention relates to the field of crystal handicrafts, in particular to a method for making a gold and silver double-color pattern crystal table. Background technique [0002] With the improvement of people's consumption ability, more and more crystal handicrafts have entered people's lives. There are many kinds of crystal handicrafts with different shapes. Crystal table is a common one, and the value can be enhanced after the surface of the crystal is plated with gold or silver. Simple gold / silver plating on the crystal surface is too monotonous and has no three-dimensional effect. People hope that the crystal surface can have fine patterns and rich colors. The demand is getting stronger and stronger. Contents of the invention [0003] Purpose of the invention: In order to overcome the deficiencies in the prior art, the purpose of the invention is to provide a method for making a gold and silver two-color pattern crystal table. [0004] Techni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B44C5/00B44C1/20B44C1/22C23C14/35C23C14/18C25D5/02C25D3/48C25D3/46
CPCB44C1/20B44C1/227B44C5/00C23C14/185C23C14/35C25D3/46C25D3/48C25D5/022
Inventor 冯正元冯育华
Owner 南通好汉邦新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap