Peelable fluorescent nail polish and its preparation process

A nail polish and fluorescent technology, applied in the field of peelable fluorescent nail polish and its preparation process, 365nm UV-LED light source irradiation and curing, can solve the problems of slow drying, inconvenient production and use of nail polish, and less durability than oily nail polish Glue and other problems, to achieve the effect of uniform color, easy control, high film hardness

Inactive Publication Date: 2019-03-19
SHANGHAI INST OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current peelable nail polish is generally water-based and needs to be used with transparent water or sealant water; the durability is not as good as that of oil-based nail polish, and it dries slowly, and peelable nail polish is generally included in the formula of nail polish The addition of strippable components brings inconvenience to the production and use of nail polish

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Peelable fluorescent nail polish and its preparation process
  • Peelable fluorescent nail polish and its preparation process
  • Peelable fluorescent nail polish and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A peelable fluorescent nail polish, calculated in parts by weight, its raw material composition and content are as follows:

[0037]

[0038] Wherein: described UV curable resin A is calculated in parts by weight, and its composition and content are as follows:

[0039]

[0040] Described UV curing resin A is prepared according to the following steps:

[0041] Add 10 parts of methylphenyl hydrogen-containing silicone oil and 10 parts of trimethylolpropane triacrylate into a 500ml three-necked flask, then add 0.01 part of polymerization inhibitor, pass in protective gas, stir and heat, and raise the temperature to 60 ℃, add 0.03 parts of catalyst, keep stirring for 3 hours, stop heating, wait until the temperature of the flask drops to room temperature, and obtain UV curable resin A.

[0042] UV curing resin B is a mixture of dipentaerythritol hexaacrylate, diethylene glycol diacrylate and isobornyl acrylate in a mass ratio of 1:1:1;

[0043] The leveling agent i...

Embodiment 2

[0055] A peelable fluorescent nail polish, calculated in parts by weight, its raw material composition and content are as follows:

[0056]

[0057] Wherein: described UV curable resin A is calculated in parts by weight, and its composition and content are as follows:

[0058]

[0059]

[0060] The UV curable resin A is prepared according to the following steps: 20 parts of methylphenyl hydrogen-containing silicone oil and 40 parts of trimethylolpropane triacrylate are added to a 500ml three-necked flask, and then 0.02 parts of a polymerization inhibitor are added , pass in protective gas, stir and heat, raise the temperature to 80°C, add 0.05 part of catalyst, keep stirring for 5 hours, stop heating, wait until the temperature of the flask drops to room temperature, and obtain UV curable resin A.

[0061] The UV curable resin B is a mixture of dipentaerythritol hexaacrylate, diethylene glycol diacrylate and isobornyl acrylate in a mass ratio of 1:2:2;

[0062] The l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses strippable fluorescent nail lacquer gel and a preparation process thereof. The strippable nail lacquer gel comprises 50-80 parts of UV curing resin A, 50-80 parts of UV curing resin B, 0.05-0.1 part of levelling agents, 1-10 parts of wetting agent, 0.2-1 part of defoaming agents, 0.1-10 parts of fluorescent UV color paste, 3-5 parts of photoinitiators A and 3-5 parts of photoinitiators B by weight. After being coated with a film, the strippable nail lacquer gel can be fast cured for 1-10 seconds through 365nm UV irradiation and can be widely used in the technical field of manicure of all kinds of crowds.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a strippable fluorescent nail polish and a preparation process thereof. The strippable fluorescent nail polish is particularly suitable for curing by irradiation with a 365nm UV-LED light source. Background technique [0002] Women's love for nail art stems from a kind of love. Nail polish is applied to the nails with tools, and cross-linking polymerization occurs after being irradiated by ordinary UV light sources. The resulting cured nail polish is bright in color, crystal clear and full, and endlessly changing. It is the favorite of ladies. Compared with ordinary UV light source curing methods, UV-LED light source has many advantages such as high luminous efficiency, long life, fast response speed, less heat release, energy saving, environmental protection, etc., and has gradually replaced ordinary UV light source. With the enrichment of urban life and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K8/891A61Q3/02C08G77/38
CPCA61K8/891A61K2800/434A61Q3/02C08G77/38
Inventor 张英强余乐平杨伊婷常文秀李烨
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com