Preparation method of nano Ru/C supported catalyst

A catalyst and carbon supported technology, applied in the field of catalysis, can solve the problems of low catalytic activity, low stability, easy loss of active components, etc., and achieve the effects of uniform particle size distribution, high dispersion, and avoiding desorption and migration.

Active Publication Date: 2016-04-20
LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF7 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the disadvantages of low catalytic activity, low stability and easy loss of active components in existing catalysts used for hydrogenation of cinnamic acid to generate 3-cyclohexylpropionic acid, and provides a high-efficiency catalyst for hydrogenation of cinnamic acid. Preparation method of nano-ruthenium carbon-supported catalyst with catalytic activity and stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of nano Ru/C supported catalyst
  • Preparation method of nano Ru/C supported catalyst
  • Preparation method of nano Ru/C supported catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Accurately weigh 50.00 g of pretreated activated carbon, add it to 300 mL aqueous solution containing 5.56 g of ruthenium trichloride hydrate, stir and impregnate for 3 h, and then use 1.0 mol L -1 Sodium carbonate aqueous solution adjusted the pH of the mixed slurry to 9, continued to stir for 4 hours, stood still for 2 hours, filtered, washed the filter cake with water until it was neutral and free of chloride ions, then transferred to an oven for 4 hours at 100°C, and then dried under N 2 The atmosphere was roasted at 150°C for 4h, then at 400°C for 4h, and finally in H 2 :N 2 =1:9 (v / v) atmosphere at 300 ° C for 3 h, that is, a highly dispersed nano-ruthenium carbon-supported catalyst with a ruthenium loading of 4.0% was obtained.

Embodiment 2

[0024] Accurately weigh 50.00 g of pretreated activated carbon, add it to 300 mL aqueous solution containing 4.13 g of ruthenium trichloride hydrate, stir and impregnate for 3 h, and then use 1.0 mol L -1 Sodium carbonate aqueous solution adjusted the pH of the mixed slurry to 9, continued to stir for 4 hours, let it stand for 1 hour, filtered, washed the filter cake with water until it was neutral and free of chloride ions, then transferred to an oven for 4 hours at 100°C, and dried under N 2 The atmosphere was roasted at 150°C for 4h, then at 400°C for 4h, and finally in H 2 :N 2 =1:9 (v / v) reduction at 300°C for 3 h, and a highly dispersed nano-ruthenium carbon-supported catalyst with a ruthenium loading of 3.0% was obtained.

Embodiment 3

[0026] Accurately weigh 50.00 g of pretreated activated carbon, add it to 300 mL aqueous solution containing 7.02 g of ruthenium trichloride hydrate, stir and impregnate for 3 h, and then use 1.0 mol L -1 Adjust the pH of the mixed slurry to 9 with aqueous sodium carbonate solution, continue to stir for 4 hours, let it stand for 1 hour, filter, wash the filter cake with water until it is neutral and free of chloride ions, and then transfer it to an oven for drying at 100°C for 6 hours. 2 The atmosphere was first fired at 150°C for 4h, then fired at 400°C for 2h, and finally in H 2 :N 2 =3:7 (v / v) atmosphere at 120 ° C for 10 h, that is, a highly dispersed nano-ruthenium carbon-supported catalyst with a ruthenium loading of 5.0% was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a nano Ru / C supported catalyst. The method comprises steps as follows: treated activated carbon is added to a ruthenium slat aqueous solution, stirring and dipping are performed for 0.5-4 h, then an alkaline compound aqueous solution is used for adjusting the pH of mixed slurry of activated carbon and ruthenium salt to 7-12, the mixed slurry is stirred continuously for 1-6 h, left to stand for 2-4 h and filtered, a filter cake is washed with water to be neutral and free of chloride ions and dried at the temperature of 80-120 DEG C for 4-12 h, and a treated Ru / C precursor is obtained; the treated Ru / C precursor is subjected to sectioned calcination in the inert atmosphere; a product after calcination is reduced, and then the nano Ru / C supported catalyst with high dispersion is obtained. The particle size of ruthenium particles of the catalyst is 1-4 nm. The method is low in production cost, has mild preparation conditions and causes few three industrial wastes, and the catalyst has advantages of long service life and the like.

Description

technical field [0001] The invention relates to a preparation method of a high-activity and high-stability nano-ruthenium carbon-supported catalyst used for hydrogenation of cinnamic acid to prepare 3-cyclohexylpropionic acid, belonging to the technical field of catalysis. Background technique [0002] 3-Cyclohexylpropionic acid, also known as pineapple acid, is an important intermediate in organic synthesis and pharmaceutical synthesis, and is widely used in the synthesis of spices, farnesyltransferase inhibitors and ferroelectric liquid crystal materials. It is mainly used in the industry to synthesize allyl cyclohexyl propionate (commonly known as pineapple ester). Pineapple ester is an additive with strong sweet pineapple fruit aroma, which is widely used in food, cosmetics and tobacco fields. The preparation methods of pineapple acid mainly contain benzaldehyde method and cyclohexanol method at present. The cyclohexanol method uses methyl acrylate and cyclohexanol as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/46B01J35/00C07C51/36C07C53/134
CPCC07C51/36B01J23/462B01J35/393C07C53/134
Inventor 丑凌军赵华华宋焕玲赵军杨建闫亮
Owner LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com