Preparation technology of nano ATO heat-insulating coating
A thermal insulation coating and preparation technology, which is applied in coatings, devices for coating liquid on the surface, radiation-absorbing coatings, etc., can solve the problems of affecting the thermal insulation effect and uneven particle size distribution of ATO, and achieve hydrophobic performance Strong, good heat insulation performance, improve the effect of dispersion effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0025] The preparation technology of nano-ATO thermal insulation coating of the present invention, it adopts the following steps:
[0026] First, add ethanol to the nano-ATO powder and stir evenly to prepare a slurry, and then spray the uniformly stirred slurry vertically through the nozzle to the surface of the high-speed rotating roller; during the implementation process, the mass flow rate of the slurry injection should be ensured. 6- 8g / s, the vertical distance between the nozzle and the roller is 0.01-0.1mm, the diameter of the roller used at the same time is 40-50mm, and the rotation speed of the roller is 300-350r / min; during the implementation process, the effect of the nozzle and the roller makes the slurry The first dispersion, and the slurry thrown to the atomization chamber is hit by high-speed gas to achieve the second dispersion; this makes the particle size of ATO smaller, laying a good foundation for the preparation of stable coatings; in the atomization chamber...
Embodiment 1
[0031] Take ATO powder with a particle size of about 30nm, add ethanol to prepare a 20wt% slurry, and then spray the slurry vertically through the nozzle onto the surface of the rotating roller; keep the mass flow rate of the slurry injection at 6g / s, the nozzle and the roller The vertical distance between them is 0.01mm, the diameter of the roller is 40mm, and the rotation speed of the roller is 300r / min; at the same time, in the atomization chamber, maintain an angle of 45° with the horizontal direction, and pass argon gas at a flow rate of 30m / s to impact Slurry; then under the pressure of the gas, the slurry is sprayed into the collection chamber through the injector, and then the gas is recovered from the upper side of the collection chamber, and the ATO slurry is collected from the bottom of the collection chamber; then, slowly add ethanol to the collected ATO slurry And silane coupling agent, wherein the volume ratio of ATO slurry, ethanol, silane coupling agent is 1:3:0...
Embodiment 2
[0033] Take ATO powder with a particle size of about 35nm, add ethanol to prepare a 25wt% slurry, then spray the slurry vertically through the nozzle to the surface of the rotating roller; keep the mass flow rate of the slurry injection at 7g / s, the nozzle and The vertical distance between the rollers is 0.05mm, the diameter of the rollers is 45mm, and the rotation speed of the rollers is 320r / min; at the same time, in the atomization chamber, an angle of 60° with the horizontal direction is maintained, and argon gas is introduced at a flow rate of 30m / s Hit the slurry; then under the pressure of the gas, the slurry is injected into the collection chamber through the injector, and then the gas is recovered from the upper side of the collection chamber, and the ATO slurry is collected from the bottom of the collection chamber; then, slowly add to the collected ATO slurry Ethanol and silane coupling agent, wherein the volume ratio of ATO slurry, ethanol, silane coupling agent is ...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com