Polypropylene porous membrane for lithium-ion battery and preparation method of polypropylene porous membrane
A technology for lithium-ion batteries and porous diaphragms, which is applied to battery components, circuits, electrical components, etc., can solve the problems of weak puncture resistance and high porosity, and achieve uniform strength, strong tensile strength, and moderate size. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0031] Example 1
[0032] The polypropylene porous diaphragm of the lithium ion battery in this embodiment is composed of the following quality components: 2,2'-methylene-bis(4,6-di-tert-butylphenol) sodium phosphate 1.5g, sodium benzoate 0.5g, 2.0kg of polypropylene resin. Among them, polypropylene resin has a viscosity average molecular weight of 1.3×10 4 The isotactic resin has a melt index of 15g / 10min.
[0033] The preparation method of polypropylene porous membrane includes the following steps:
[0034] 1) Accurately take polypropylene resin, 2,2'-methylene-bis(4,6-di-tert-butylphenol) sodium phosphate and sodium benzoate according to the quality, and heat to 180°C to obtain a melt;
[0035] 2) Extruding the melt from the die, cooling it on a cooling roll and casting it into a thick sheet with a cooling temperature of 90°C;
[0036] 3) Take the thick sheet at 135°C and stretch it successively at 2 times in the longitudinal direction and 2 times in the transverse direction to mak...
Example Embodiment
[0038] Example 2
[0039] The polypropylene porous diaphragm of the lithium ion battery in this embodiment is composed of the following quality components: 2,2'-methylene-bis(4,6-di-tert-butylphenol) calcium hydrogen phosphate 15.0g, benzene Calcium formate 5.0g, polypropylene resin 2.0kg. Among them, polypropylene resin has a viscosity average molecular weight of 3.0×10 4 The random resin has a melt index of 10g / 10min.
[0040] The preparation method of polypropylene porous membrane includes the following steps:
[0041] 1) Accurately take polypropylene resin, 2,2'-methylene-bis(4,6-di-tert-butylphenol) calcium hydrogen phosphate and calcium benzoate according to the quality, and heat it to 210°C to obtain a melt;
[0042] 2) Extruding the melt from the die, cooling and casting it into a thick sheet on a cooling roll, the cooling temperature is 100°C;
[0043] 3) Take the thick film at 135°C and stretch it successively at 3 times in the longitudinal direction and 2 times in the trans...
Example Embodiment
[0045] Example 3
[0046] The polypropylene porous diaphragm of the lithium ion battery in this embodiment is composed of the following quality components: methylene bis(2,4-di-tert-butylphenoxy) aluminum phosphate 23.0g, magnesium benzoate 17.0g, Polypropylene resin 2.0kg. Among them, polypropylene resin has a viscosity average molecular weight of 1.1×10 5 Syndiotactic resin, the melt index is 7.8g / 10min.
[0047] The preparation method of polypropylene porous membrane includes the following steps:
[0048] 1) Take polypropylene resin, methylene bis(2,4-di-tert-butylphenoxy) aluminum phosphate and magnesium benzoate accurately according to the quality, and heat to 210°C to obtain a melt;
[0049] 2) Extruding the melt from the die, cooling and casting it into a thick sheet on a cooling roll, the cooling temperature is 110°C;
[0050] 3) Take the thick film at 140℃ and stretch it successively at 3 times in the longitudinal direction and 2.5 times in the transverse direction to make a ...
PUM
Property | Measurement | Unit |
---|---|---|
Melt index | aaaaa | aaaaa |
Melt index | aaaaa | aaaaa |
Melt index | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap