Water-soluble epoxy silicone acrylic resin and preparation method thereof

A technology of epoxy silicone acrylic resin and silicone acrylic resin, applied in the direction of coating, etc., can solve the problems of unsatisfactory performance indicators, poor water solubility, etc., and achieve the effect of high social value and economic benefits

Inactive Publication Date: 2016-06-15
广东顺德大地缘新材料有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems of poor water solubility and other unsatisfactory performance indicators existing in the existing silicone acrylic resin, the present invention proposes a water-soluble epoxy silicone acrylic resin, which can be directly formulated with tap water when preparing various coatings without using Any solvent formulation and is environmentally friendly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A water-soluble epoxy silicone acrylic resin, calculated in parts by weight, comprises the following components:

[0025] 20 parts methyl methacrylate, 45 parts butyl acrylate, 5 parts octyl acrylate and 3 parts hydroxypropyl acrylate, 10 parts methacrylic acid and 2 parts acrylic acid, 8 parts epoxy resin, 4 parts silane coupling agent , 5 parts of benzoyl peroxide and 5 parts of azobisisobutyronitrile, 7 parts of isopropanol, 25 parts of propylene glycol methyl ether and 10 parts of propylene glycol butyl ether, 9 parts of dimethylethanolamine and tap water, the addition of the tap water The amount is subject to the solid content reaching 40%.

[0026] The preparation method comprises the following steps:

[0027] 1) Calculated in parts by weight, weigh 20 parts of methyl methacrylate, 45 parts of butyl acrylate, 5 parts of octyl acrylate and 3 parts of hydroxypropyl acrylate, 10 parts of methacrylic acid, 2 parts of acrylic acid and 5 parts Benzoyl peroxide is stir...

Embodiment 2

[0032] A water-soluble epoxy silicone acrylic resin, calculated in parts by weight, comprises the following components:

[0033] 30 parts of methyl methacrylate, 35 parts of butyl acrylate, 10 parts of octyl acrylate and 7 parts of hydroxypropyl acrylate, 6 parts of methacrylic acid and 5 parts of acrylic acid, 12 parts of epoxy resin, 2 parts of silane coupling agent , 7 parts of benzoyl peroxide and 3 parts of azobisisobutyronitrile, 4 parts of isopropanol, 35 parts of propylene glycol methyl ether and 20 parts of propylene glycol butyl ether, 7 parts of triethylamine and tap water, the addition of the tap water Subject to the solid content reaching 70%.

[0034] The preparation method comprises the following steps:

[0035] 1) Calculated in parts by weight, weigh 30 parts of methyl methacrylate, 35 parts of butyl acrylate, 10 parts of octyl acrylate and 7 parts of hydroxypropyl acrylate, 6 parts of methacrylic acid, 5 parts of acrylic acid and 7 parts Benzoyl peroxide is ...

Embodiment 3

[0040] A water-soluble epoxy silicone acrylic resin, calculated in parts by weight, comprises the following components:

[0041] 20 parts of butyl acrylate, 35 parts of octyl acrylate and 15 parts, 10 parts of acrylic acid, 10 parts of epoxy resin, 3 parts of silane coupling agent, 4 parts of benzoyl oxide, 6 parts of azobisisoheptanonitrile, isopropyl 32 parts of alcohol, 22 parts of propylene glycol methyl ether, 8 parts of organic amine neutralizer AMP-95 and tap water, the addition of the tap water is based on the fact that the solid content reaches 60%.

[0042] The preparation method comprises the following steps:

[0043] 1) Calculated in parts by weight, weigh 20 parts of butyl acrylate, 35 parts of octyl acrylate, 15 parts of acrylic acid, 4 parts of benzoyl peroxide and stir evenly to obtain a mixed solution a;

[0044] 2) Weigh 10 parts of epoxy resin, 6 parts of azobisisoheptanonitrile, 32 parts of isopropanol, and 22 parts of propylene glycol methyl ether, mix th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention provides water-soluble epoxy silicone acrylic resin and a preparation method thereof. The preparation method includes following steps: 1), weighing, by weight, 63-92 parts of acrylate, 8-15 parts of acrylic acid and 5-7 parts of initiator, and well stirring to obtain mixed liquid a; 2), weighing 8-12 parts of epoxy resin, 3-5 parts of initiator and 39-62 parts of organic solvent for mixing, and well stirring and dissolving at 100-130 DEG C to obtain mixed liquid b; 3), at 100-110 DEG C, dropwise adding the mixed liquid a obtained in the step 1) at a constant speed into the mixed liquid b, holding temperature for 0.8-1.2 h after dropwise adding is finished, adding 2-4 parts of silane coupling agent, and holding temperature for 0.8-1.2 h; 4), sampling, adding a neutralizing agent water solution to detect water solubility until the sample is completely dissolved in water, and stopping reaction for cooling. When water-soluble resin is used to prepare various coatings, tap water is directly used for blending, no solvent is needed for blending, and environment protection is realized.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a water-soluble epoxy silicone acrylic resin and a preparation method thereof. Background technique [0002] Acrylic resin is widely used in the field of coatings because of its excellent film-forming properties, good transparency, excellent mechanical properties and environmental protection; but its molecules are mostly linear structures and lack crosslinking points, so water resistance, weather resistance and resistance The heat is poor, which affects its application range. The emergence of silicone materials provides a good solution to overcome these defects. Polyorganosiloxane has many excellent properties, such as low glass transition temperature and surface tension, special temperature resistance, weather resistance, etc. Silicone-modified acrylate is to use the excellent high and low temperature resistance and water resistance of polysiloxane to improve the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/10C08F220/06C08F220/18C08F220/14C08F220/28C09D151/08
CPCC08F283/10C09D151/08C08F220/1804
Inventor 张孟强
Owner 广东顺德大地缘新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com