A nano-inorganic and antibacterial fiber technology, which is applied in the direction of fiber chemical characteristics, rayon manufacturing, single-component polyolefin rayon, etc., can solve the problems of easy aggregation and poor compatibility of nano-inorganic antibacterial agents, and achieve low cost, Overcoming the effects of easy reunion and simple process

Active Publication Date: 2016-06-22
HUIZHOU HUANMEISHENG NEW MATERIAL CO LTD
View PDF7 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to overcome the defects of the above-mentioned prior art and provide a nano-inorganic antibacterial fiber masterbatch to solve the problems of easy agglomeration of nano-inorganic antibacterial agents and poor compatibility with fiber resins, and improve the antibacterial effect of antibacterial fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] S1. Add 2.5kg of nano-titanium dioxide powder (20nm) and 2.5kg of nano-zinc oxide powder (50nm) to the ceramic sand mill, then add silane coupling agent KH5601kg and 0.5kg of silicone oil, and grind at high speed until thick paste;

[0033] S2. Add 0.5kg of HDI to make the isocyanate react with the silane coupling agent to form a coating on the surface of the inorganic powder;

[0034] S3. Grinding at high speed until the particle size is 1000nm;

[0035] S4. Add 3kg of nylon chip resin and 50g of antioxidant, and extrude at a temperature of 180-250°C through a devolatilized twin-screw to prepare a masterbatch, so as to obtain a nylon anti-UV, antibacterial and anti-mildew function masterbatch.

Embodiment 2

[0037] S1. Add 2.0kg of nano-cuprous oxide powder (20nm) and 3kg of nano-silver powder (50nm) to a ceramic sand mill, then add silane coupling agent KH5501kg and 0.5kg of silicone oil, and grind at high speed to a thick paste;

[0038] S2. Add 0.5kg of HDI to make the isocyanate react with the silane coupling agent to form a coating on the surface of the inorganic powder;

[0039] S3. Grinding at high speed until the particle size is 1000nm;

[0040] S4. Add 3kg of polyester chip resin and 50g of antioxidant, and extrude at a temperature of 180-250° C. to prepare a masterbatch through a devolatilized twin-screw to obtain a polyester antibacterial and mildew-proof functional masterbatch.

Embodiment 3

[0042] S1. Add 1kg of nano-zinc powder (10nm) and 4kg of silver ion antibacterial agent powder (100nm) to the ceramic sand mill, then add silane coupling agent KH5701kg and silicone oil 0.5kg, and grind at high speed until it is thick paste;

[0043] S2. Add 0.5kg of HDI to make the isocyanate react with the silane coupling agent to form a coating on the surface of the inorganic powder;

[0044] S3. Grinding at high speed until the particle size is 1000nm;

[0045] S4. Add 3kg of polypropylene resin and 50g of antioxidant, and extrude at a temperature of 180-250° C. to prepare masterbatches through devolatilization twin-screws to obtain polypropylene antibacterial and mildew-proof functional masterbatches.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a nano inorganic antibacterial fiber masterbatch and a preparation method thereof. The nano inorganic antibacterial fiber masterbatch is composed of, by weight, 1-30 parts of fiber resin, 1-50 parts of nano inorganic antibacterial powder, 1-5 parts of silicon oil, 1-10 parts of a silane coupling agent, 1-5 parts of isocyanate and 0.1-0.5 part of an antioxidant. The preparation method includes: adding the nano inorganic antibacterial powder into a sand mill, then adding the silane coupling agent, and grinding at a high speed until a paste state is achieved; adding the isocyanate, and grinding at a high speed to obtain organic-inorganic hybrid nanopowder; jointly subjecting the nanopowder and the fiber resin to twin-screw extrusion for preparing the masterbatch. The prepared nano inorganic antibacterial fiber masterbatch is widely applicable to various fibers.

Description

technical field [0001] The invention relates to the field of polymer synthesis modification and processing, in particular, the invention relates to an inorganic antibacterial fiber masterbatch and a preparation method thereof. Background technique [0002] At present, with the improvement of people's living standards, the requirements for functional fibers and their textile products are getting higher and higher, and fibers with antibacterial functions and their textile products are one of the major categories. The preparation methods of antibacterial fibers are generally divided into two types, one is wet impregnation, the fibers or their textile products are immersed in a surface treatment agent containing antibacterial agents, and then dried and cured to obtain antibacterial fibers or textiles, but their washing resistance is poor. , the antibacterial agent is easy to peel off after washing, which leads to the decline of antibacterial performance; another preparation me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/00C08L67/00C08L23/12C08L83/04C08L75/04C08K9/10C08K9/06C08K9/04C08K3/22C08K3/08C08J3/22D01F1/10D01F6/90D01F6/92D01F6/46
CPCC08J3/226C08J2323/12C08J2367/00C08J2377/00C08J2423/12C08J2467/00C08J2477/00C08L23/12C08L67/00C08L77/00C08L2201/08C08L2203/12C08L2205/03D01F1/103D01F1/106D01F6/46D01F6/90D01F6/92C08L83/04C08L75/04C08K9/10C08K9/06C08K9/04C08K2003/2241C08K2003/2296C08K2003/2248C08K2003/0806C08K2003/0893
Inventor 廖道权谢太和赵良知
Owner HUIZHOU HUANMEISHENG NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap