High-temperature-resistant anti-corrosion paint and preparation method thereof

An anti-corrosion coating and high temperature resistant technology, applied in anti-corrosion coatings, fire-retardant coatings, coatings, etc., can solve the problems of affecting the appearance of the paint film, poor corrosion resistance, long surface drying time of the paint film, etc., to achieve excellent anti-corrosion, easy operation, easy to achieve effect

Inactive Publication Date: 2016-06-22
HUANGHE S & T COLLEGE
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there are many reports on heat-resistant coatings, and the temperature resistance of existing high-temperature-resistant coatings can basically meet the requirements for use, but there are some shortcomings.
For example, the surface drying time of the paint film is long, which will affect the appearance of the paint film due to dust and other reasons during use; the disadvantages such as poor corrosion resistance at high temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant anti-corrosion paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1 of the present invention provides a high temperature resistant anti-corrosion coating, which includes the following raw materials in parts by weight: 8 parts of aluminum sol, 15 parts of aluminum dihydrogen phosphate, 8 parts of glass powder, 5 parts of talcum powder, 20 parts of mica powder, acrylic bicyclic 1 part of pentenyloxyethyl ester and 20 parts of water, wherein, each raw material in this embodiment is technical grade.

[0020] Preparation method: Under the condition of 40°C, uniformly mix aluminum sol, aluminum dihydrogen phosphate and water to form the first mixed solution; add glass powder, talc powder and mica powder to the first mixed solution, and ultrasonically Disperse for 30 minutes to obtain a second mixed solution; add dicyclopentenyloxyethyl acrylate to the second mixed solution, and stir at a speed of 1200 r / min for 6 hours at 40°C to obtain this The high temperature resistant anticorrosion coating described in embodiment.

Embodiment 2

[0022] Embodiment 2 of the present invention provides a high temperature resistant anti-corrosion coating, which includes the following raw materials in parts by weight: 9 parts of aluminum sol, 16 parts of aluminum dihydrogen phosphate, 10 parts of glass powder, 7 parts of talcum powder, 22 parts of mica powder, acrylic bicyclic 2 parts of pentenyloxyethyl ester and 23 parts of water, wherein, each raw material in this embodiment is technical grade.

[0023] Preparation method: Under the condition of 50°C, uniformly mix aluminum sol, aluminum dihydrogen phosphate and water to form the first mixed solution; add glass powder, talc powder and mica powder to the first mixed solution, and ultrasonically Disperse for 30 minutes to obtain a second mixed solution; add dicyclopentenyloxyethyl acrylate to the second mixed solution, and stir at a speed of 1100 r / min for 6 hours at 50°C to obtain this The high temperature resistant anticorrosion coating described in embodiment.

Embodiment 3

[0025] Embodiment 3 of the present invention provides a high temperature resistant anti-corrosion coating, which includes the following raw materials in parts by weight: 10 parts of aluminum sol, 17 parts of aluminum dihydrogen phosphate, 11 parts of glass powder, 8 parts of talcum powder, 23 parts of mica powder, acrylic bicyclic 2 parts of pentenyloxyethyl ester and 25 parts of water, wherein, each raw material in this embodiment is technical grade.

[0026] Preparation method: Under the condition of 60°C, uniformly mix aluminum sol, aluminum dihydrogen phosphate and water to form the first mixed solution; add glass powder, mica powder and talc powder to the first mixed solution, and ultrasonically Disperse for 35 minutes to obtain a second mixed solution; add dicyclopentenyloxyethyl acrylate to the second mixed solution, and stir at a speed of 1000 r / min at 60°C for 5 hours to obtain this The high temperature resistant anticorrosion coating described in embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high temperature resistant anticorrosion coating, which comprises the following raw materials in parts by weight: 8-12 parts of aluminum sol, 15-20 parts of aluminum dihydrogen phosphate, 8-14 parts of glass powder, 5-10 parts of talc powder, mica 20-25 parts of powder, 1-5 parts of dicyclopentenyloxyethyl acrylate and 20-30 parts of water. The present invention also provides a preparation method of the above-mentioned high temperature resistant anticorrosion coating. The components in the above-mentioned high-temperature-resistant anti-corrosion coating provided by the present invention cooperate with each other and complement each other, so that the coating has excellent anti-corrosion, high temperature resistance, crack resistance, storage stability, etc. under the premise of maintaining good adhesion. characteristic.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to a high-temperature-resistant anti-corrosion coating and a preparation method thereof. Background technique [0002] With the rapid development of modern industry and national defense construction (such as aerospace, aviation, weapons, etc.), the requirements for high-temperature resistant coatings for equipment are getting higher and higher. Physical and mechanical properties and anti-corrosion properties. [0003] High temperature resistant coatings, also known as heat resistant coatings, generally refer to coatings that can maintain proper physical and mechanical properties without discoloration or falling off of the paint film above 200°C, so that the protected objects can function normally in high temperature environments Special functional coatings. Therefore, high-temperature-resistant coatings are widely used in high-temperature places such as steel chimneys, high-tempe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/00C09D5/08C09D7/12
CPCC09D1/00C09D5/08C09D5/18C09D7/61
Inventor 高德峰张发厅李慧康红伟付志豪刘建秀赵庆革
Owner HUANGHE S & T COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com