Graphene-based enhanced high-solid epoxy anticorrosive coating and method for preparing same

A technology of anti-corrosion coatings and graphene, which is applied in anti-corrosion coatings, epoxy resin coatings, conductive coatings, etc., can solve problems such as poor anti-corrosion performance, non-environmentally friendly graphene, and difficulty in stabilizing dispersants, and achieve excellent anti-corrosion performance and energy saving Energy consumption, good adhesion effect

Inactive Publication Date: 2016-07-06
XINHE NEW MATERIALS CO LTD
View PDF4 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Therefore, aiming at the above content, the present invention provides a kind of based on graphene-enhanced high solid content epoxy anticorrosion coating and preparation method thereof, solves the poor anticorrosion property of anticorrosion coating of the prior art, not environmental protection and the stability of dispersant of graphene in coating difficult question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A graphene-enhanced high-solid epoxy anti-corrosion coating, consisting of a main paint and a curing agent mixed uniformly, the main paint is composed of the following raw materials in parts by weight: 8 parts by weight of bisphenol A epoxy resin, 10 parts by weight of ethanol -15 parts by weight, 0.2-3 parts by weight of defoamer, 0.1-2 parts by weight of graphene, 10-15 parts by weight of pigment, 35-45 parts by weight of talcum powder, 0.5-5 parts by weight of organic bentonite; the curing agent consists of The raw materials are composed of the following parts by weight: 75-85 parts by weight of Mannich base curing agent, 5-15 parts by weight of ethanol, and 3-8 parts by weight of defoamer. The diameter of the graphene sheet is 15 microns, the number of layers is ≤ 10, and the oxygen content is 15%.

[0037] Its preparation method comprises the following steps:

[0038] (1) Preparation of main paint: Add 18 parts by weight of bisphenol A epoxy resin, 10 parts by wei...

Embodiment 2

[0042]A graphene-enhanced high-solid epoxy anti-corrosion coating is composed of a main paint and a curing agent mixed uniformly, and the main paint is composed of the following raw materials in parts by weight: 20 parts by weight of brominated epoxy resin, ethyl acetate 12 parts by weight, 1.5 parts by weight of wetting agent, 1.1 parts by weight of graphene, 12 parts by weight of pigment, 40 parts by weight of silicon micropowder, 2.7 parts by weight of fumed silica; the curing agent is composed of the following raw materials in parts by weight: cashew nuts 80 parts by weight of phenol-modified amine curing agent, 10 parts by weight of ethyl acetate, and 5 parts by weight of wetting agent. The diameter of the graphene sheet is 20 microns, the number of layers is ≤ 10, and the oxygen content is 25%.

[0043] Its preparation method comprises the following steps:

[0044] (1) Preparation of the main paint: 20 parts by weight of brominated epoxy resin, 12 parts by weight of eth...

Embodiment 3

[0048] A graphene-enhanced high-solid epoxy anti-corrosion coating is composed of a main paint and a curing agent mixed uniformly, and the main paint is composed of the following raw materials in parts by weight: 25 parts by weight of novolak epoxy resin, methyl ethyl 15 parts by weight of ketone, 3 parts by weight of adhesion promoter, 2 parts by weight of graphene, 15 parts by weight of pigment, 45 parts by weight of nano-calcium carbonate, 5 parts by weight of hydrogenated castor oil; Composition: 85 parts by weight of amidoamine curing agent, 15 parts by weight of methyl ethyl ketone, and 8 parts by weight of adhesion promoter. The diameter of the graphene sheet is 30 microns, the number of layers is ≤ 10, and the oxygen content is 33%.

[0049] A preparation method based on graphene-enhanced high-solid epoxy anticorrosion coating, comprising the steps of:

[0050] (1) Preparation of main paint: add 25 parts by weight of novolac epoxy resin, 15 parts by weight of methyl e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The present invention involves the field of anticorrosive coatings, which provides a graphene -based high -solid high -solid -based epoxy anticorrosive coating and its production method to solve the poor anticorrosive coating performance of existing technologies, not environmental protection, and graphene difficult to stabilize the stability in the coatings.The problem is composed of the main paint and curing agent mixed. The main paint consists of the following weights of the following weights: epoxy resin 18‑25 weight, dilute agent 10‑15 weight, auxiliary 0.2‑3 weight portion, Graphene 0.1量2 weight, pigment 10‑15 weight, filler 35‑45 weight, tactile 0.5‑5 weight; the curing agent consists of the following weights of each raw material: amine resin 75‑‑‑85 weights, dilute agents 5‑15 weights, and additives 3‑8 weights.

Description

technical field [0001] The invention relates to the field of anti-corrosion coatings, in particular to a graphene-enhanced high-solid epoxy anti-corrosion coating and a preparation method thereof. Background technique [0002] According to relevant data, the economic loss caused by corrosion of metal materials in my country is relatively large every year, accounting for about 5% of the gross national product. From the perspective of the economics of anti-corrosion treatment, the use of anti-corrosion coatings is the most economical and effective method. With the continuous improvement of infrastructure design requirements, new requirements for coating performance requirements are constantly emerging, especially new requirements are put forward for the anti-corrosion protection life of coatings, the versatility of materials, and environmental friendliness. [0003] Traditional anti-corrosion coatings are generally classified by resin into epoxy, epoxy bitumen, chlorinated rub...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D163/04C09D5/08C09D5/24C09D7/12
CPCC09D163/00C08K3/04C08K3/34C08K3/346C08K3/36C08K2201/011C08K2201/014C09D5/08C09D5/24C09D7/61C09D7/62C09D163/04
Inventor 王书传王立李旺平
Owner XINHE NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap