Putty powder and preparation method thereof
A putty powder and talcum powder technology, which is applied in the production of bulk chemicals, filling slurry, etc., can solve the problems of insufficient environmental protection performance, poor leveling effect, rough putty powder, etc., and achieves fluffy internal structure, good user experience, and improved The effect of breathability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0032] A kind of putty powder, comprises the raw material of following weight parts:
[0033] 80 parts of talcum powder, 20 parts of heavy calcium, 10 parts of gypsum, 20 parts of bentonite, 20 parts of cellulose, 20 parts of starch glue, 8 parts of lubricant, 5 parts of ash calcium, 3 parts of spices, 3 parts of high-gluten flour, 40 parts Straw, 20 parts of bamboo residue, 35 parts of millennium wood, 30 parts of bamboo charcoal granules, 6 parts of fatty alcohol polyoxyethylene ether, 100 parts of pure water, 50 parts of magnetized water, 5 parts of starter and 2 parts of pigment.
[0034] The preparation method of described putty powder, comprises the following steps:
[0035] 1) Take rice straw, bamboo dregs, and millennium wood according to the above weight parts, mix them, crush them, add the above weight parts of magnetized water, stir evenly, place them at 0°C for cooling treatment for 30 minutes, then place them in a sealed place and heat them at 40°C for 2 hours, th...
Embodiment 2
[0049] A kind of putty powder, comprises the raw material of following weight parts:
[0050] 85 parts of talcum powder, 24 parts of heavy calcium, 13 parts of gypsum, 25 parts of bentonite, 25 parts of cellulose, 25 parts of starch glue, 9 parts of lubricant, 6 parts of ash calcium, 4 parts of spices, 4 parts of high-gluten flour, 45 parts Straw, 25 parts of bamboo residue, 37 parts of millennium wood, 35 parts of bamboo charcoal particles, 7 parts of fatty alcohol polyoxyethylene ether, 111 parts of pure water, 55 parts of magnetized water, 6 parts of starter and 3 parts of pigment.
[0051] The preparation method of described putty powder, comprises the following steps:
[0052] 1) Take rice straw, bamboo dregs, and millennium wood according to the above weight parts, mix them, crush them, add the above weight parts of magnetized water, stir evenly, place them at 0°C for cooling treatment for 30 minutes, then place them in a sealed place and heat them at 40°C for 2 hours, t...
Embodiment 3
[0066] A kind of putty powder, comprises the raw material of following weight parts:
[0067] 90 parts of talcum powder, 30 parts of heavy calcium, 15 parts of gypsum, 30 parts of bentonite, 30 parts of cellulose, 30 parts of starch glue, 10 parts of lubricant, 8 parts of ash calcium, 5 parts of spices, 5 parts of high-gluten flour, 50 parts Straw, 30 parts of bamboo residue, 40 parts of millennium wood, 40 parts of bamboo charcoal particles, 8 parts of fatty alcohol polyoxyethylene ether, 120 parts of pure water, 60 parts of magnetized water, 8 parts of starter and 4 parts of pigment.
[0068] The preparation method of described putty powder, comprises the following steps:
[0069] 1) Take rice straw, bamboo dregs, and millennium wood according to the above weight parts, mix them, crush them, add the above weight parts of magnetized water, stir evenly, place them at 0°C for cooling treatment for 30 minutes, then place them in a sealed place and heat them at 40°C for 2 hours, ...
PUM
| Property | Measurement | Unit |
|---|---|---|
| Particle size | aaaaa | aaaaa |
| Height | aaaaa | aaaaa |
| Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More