Instrument signal line insulation coating and preparation method thereof

An insulating coating and signal line technology, applied in the field of signal line materials, can solve the problems of limited service life of the rubber layer and inability to guarantee insulation, and achieve the effects of improved adhesion, instant curing speed at room temperature, and excellent moisture resistance

Inactive Publication Date: 2016-09-28
马逸晗
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the service life of the rubber layer is limited, and once there is wear and tear, its insulation will not be guaranteed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] (1) Add 15 parts of C9 petroleum resin and 10 parts of chlorosulfonated polyethylene to 40 parts of epoxy resin, first heat to 110-115 ° C and mix for 10 minutes, then add 5 parts of petroleum coke, 5 parts of rubber powder and 4 parts Asbestos powder, continue to heat to 130-135 ° C and mix for 10 minutes to obtain material I;

[0016] (2) Heat 4 parts of carnauba wax until completely melted, then add 4 parts of plasticizer, 3 parts of cetyl alcohol and 2 parts of chlorinated paraffin, heat and mix for 10 minutes to obtain material II;

[0017] (3) Add material II, 8 parts of volcanic ash, 5 parts of molecular sieve powder, 2 parts of lanolin, 2 parts of magnesium aluminum silicate and 0.2 parts of nano-lanthanum oxide to material I, mix well and let stand for 1 hour, then add the mixture In a ball mill, ball mill until the fineness is less than 50 μm.

[0018] Preparation of plasticizers: Add 10 parts of linear low density polyethylene and 8 parts of polyethylene gly...

Embodiment 2

[0020] (1) Add 10 parts of C9 petroleum resin and 10 parts of chlorosulfonated polyethylene to 40 parts of epoxy resin, first heat to 110-115 ° C and mix for 10 minutes, then add 7 parts of petroleum coke, 5 parts of rubber powder and 3 parts Asbestos powder, continue to heat to 130-135 ° C and mix for 10 minutes to obtain material I;

[0021] (2) Heat 5 parts of carnauba wax until completely melted, then add 4 parts of plasticizers, 2 parts of cetyl alcohol and 2 parts of chlorinated paraffin, keep warm and mix for 10 minutes to obtain material II;

[0022] (3) Add material II, 10 parts of volcanic ash, 3 parts of molecular sieve powder, 2 parts of lanolin, 1 part of magnesium aluminum silicate and 0.2 parts of nano-lanthanum oxide to material I, mix thoroughly and let stand for 1 hour, then add the mixture In a ball mill, ball mill until the fineness is less than 50 μm.

[0023] Preparation of plasticizers: Add 10 parts of linear low density polyethylene and 10 parts of pol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an instrument signal line insulation coating and a preparation method thereof, and relates to the technical field of signal line materials. The instrument signal line insulation coating is prepared from, by weight, 35-40 parts of epoxy resin, 10-15 parts of C9 petroleum resin, 10-15 parts of chlorosulfonated polyethylene, 6-10 parts of cinerite, 5-8 parts of petroleum coke, 5-8 parts of rubber powder, 4-6 parts of carnauba wax, 4-6 parts of plastification additive, 3-5 parts of asbestos powder, 3-5 parts of molecular sieve raw powder, 2-3 parts of cetyl alcohol, 2-3 parts of chlorinated paraffin, 1-2 pars of wool fat, 1-2 parts of aluminum-magnesium silicate and 0.1-0.2 part of nano lanthanum oxide. The insulation coating has excellent moisture resistance, fire resistance and insulation performance, the service life of an insulation layer is effectively prolonged, and therefore a signal line is protected better. By means of the added plastification additive, the flexibility of a coating can be enhanced, the adhesive force of the coating on the insulation layer can be fully improved, and the phenomenon that a coating is pulverized and falls off after the signal line is used for a long time is avoided.

Description

Technical field: [0001] The invention relates to the technical field of signal line materials, in particular to an insulating coating for instrument signal lines and a preparation method thereof. Background technique: [0002] The instrument signal line is used to output the signal of the instrument to control the operation of the equipment and the feedback signal of the working state of the input equipment to reduce the workload and achieve precise and high-efficiency processing. Due to the different working environments of instrument signal lines, some instruments require their signal lines to have excellent insulation to ensure production safety. Therefore, the method of wrapping the rubber layer outside the signal core is usually used to improve the insulation. However, the service life of the rubber layer is limited, and its insulation cannot be guaranteed in case of wear. In response to this situation, our company has developed an insulating coating for instrument si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/18C09D5/25C09D7/12
CPCC08K2201/011C08L2201/02C08L2203/202C08L2205/025C08L2205/035C09D5/18C09D163/00C09D7/61C09D7/65C09D7/70C08L57/02C08L23/34C08K13/04C08K7/12C08K3/34C08K2003/221
Inventor 马逸晗
Owner 马逸晗
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap