Long-acting water-based metal antirust agent and preparation method thereof

A water-based anti-rust agent technology, applied in the coating process of metal materials, etc., can solve problems such as failure of aircraft parts and auto parts, and achieve good lubricity, long acting time, and good environmental protection effects

Active Publication Date: 2016-09-28
NANXIONG JIASHENG IND
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Corrosion, while causing huge economic losses, may also lead to the failure of certain equipment, such as aircraft parts and auto parts, and cause irreparable and catastrophic consequences

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Long-acting water-based metal antirust agent and preparation method thereof
  • Long-acting water-based metal antirust agent and preparation method thereof
  • Long-acting water-based metal antirust agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The long-acting water-based antirust agent provided in this embodiment is prepared from the following raw materials in parts by weight:

[0028]

[0029] Wherein, the preparation method of the long-chain complex amine borate ester is: 12 mass parts of boric acid, 12 mass parts of triethanolamine, 5 mass parts of tetraethylenepentamine, 3 mass parts of dodecylethyleneamine, 6 mass parts Add 80 parts by mass of polyvinyl alcohol to 80 parts by mass of anhydrous DMSO to obtain a mixed solution, raise the temperature of the mixed solution to 130°C, reflux for 4 hours, distill off DMSO and a small amount of water under reduced pressure, and then add 60 parts by mass of tetrahydrofuran Separating unreacted triethanolamine, tetraethylenepentamine, and dodecylethyleneamine, removing residual tetrahydrofuran, and vacuum drying to obtain a colorless viscous long-chain complex borate ester.

[0030] The preparation method of the above-mentioned long-acting water-based antirust ...

Embodiment 2

[0035] The long-acting water-based antirust agent provided in this embodiment is prepared from the following raw materials in parts by weight:

[0036]

[0037] Wherein, the preparation method of the long-chain compound amine borate ester is: 10 mass parts of boric acid, 12 mass parts of triethanolamine, 7 mass parts of tetraethylenepentamine, 4 mass parts of dodecylethyleneamine, 4 mass parts Add 100 parts by mass of polyvinyl alcohol to 100 parts by mass of anhydrous DMSO to obtain a mixed solution, raise the temperature of the mixed solution to 120°C, reflux for 6 hours, distill off DMSO and a small amount of water under reduced pressure, and then add 50 parts by mass of tetrahydrofuran Separating unreacted triethanolamine, tetraethylenepentamine, and dodecylethyleneamine, removing residual tetrahydrofuran, and vacuum drying to obtain a colorless viscous long-chain complex borate ester.

[0038] The preparation method of the above-mentioned long-acting water-based antiru...

Embodiment 3

[0043]The long-acting water-based antirust agent provided in this embodiment is prepared from the following raw materials in parts by weight:

[0044]

[0045] Wherein, the preparation method of the long-chain complex amine borate ester is: 15 parts by mass of boric acid, 15 parts by mass of triethanolamine, 8 parts by mass of tetraethylenepentamine, 4 parts by mass of dodecylethyleneamine, 8 parts by mass of Add 50 parts by mass of polyvinyl alcohol to 50 parts by mass of anhydrous DMSO to obtain a mixed solution, raise the temperature of the mixed solution to 110°C, reflux for 5 hours, distill off DMSO and a small amount of water under reduced pressure, and then add 80 parts by mass of tetrahydrofuran Separating unreacted triethanolamine, tetraethylenepentamine, and dodecylethyleneamine, removing residual tetrahydrofuran, and vacuum drying to obtain a colorless viscous long-chain complex borate ester.

[0046] The preparation method of the above-mentioned long-acting wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a long-acting water-based metal antirust agent and a preparation method thereof. Dodecyl dicarboxylic acid, carboxymethyl cellulose, inositol hexaphosphate, sodium metasilicate, perfluorocaprylic acid, sodium molybdate, barium titanate, long-chain compound amine boric acid ester, polyethyleneglycol, isopropanol, hydroxyethyl ethylenediamine triacetic acid, 2-ethyl-4-methylimidazole and deionized water are used as raw materials. The preparation method of the long-chain compound amine boric acid ester is improved. All the raw materials are subjected to phased mixed treatment to obtain the water-based metal antirust agent. The long-acting environment-friendly water-based metal antirust agent with the excellent rust-resisting effect is obtained through the preparation method which is simple and easy to operate.

Description

technical field [0001] The invention belongs to the technical field of chemical products and relates to an antirust agent, in particular to a long-acting water-based metal antirust agent and a preparation method thereof. Background technique [0002] Metal is an indispensable material in modern industry and life because of its excellent characteristics, but metal is easily corroded during use, which brings huge social harm and economic loss. According to reports, the economic loss caused by metal corrosion in my country accounts for 4% of GDP (gross domestic product) every year. my country's GDP in 2013 was 56 trillion yuan. Based on this, the economic loss caused by metal corrosion is estimated to be about 2.24 trillion. This is an astonishing figure; the losses caused by various natural disasters in my country in 2013 were about 580.84 billion yuan, which shows that the losses caused by metal corrosion are far greater than various natural disasters. While causing huge econ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/44
CPCC23C22/44
Inventor 张佳斌
Owner NANXIONG JIASHENG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap