A kind of antibacterial building concrete production process

A production process and concrete technology, which is applied in the field of building materials, can solve the problems of moldy concrete body, affecting concrete performance, green appearance, etc., and achieve the effects of good water absorption, avoiding discoloration, and excellent air permeability

Active Publication Date: 2019-03-08
湖州鸿鼎混凝土制品有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The concrete in the prior art has been quite mature for the technology of resisting sulphate, acid and alkali substances, etc. However, there is no resistance measure for some bacterial erosion such as anaerobic bacteria, which often causes the concrete body to become moldy, etc., which is not only easy to cause The appearance is green and produces peculiar smell, which will also affect the performance of concrete and may cause corrosion to internal steel bars, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antibacterial building concrete production process
  • A kind of antibacterial building concrete production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Step 1. Preparation of antibacterial solution

[0030] The first step, the preparation mass percentage concentration is respectively the methyl cellulose aqueous solution of 5% and the copper sulfate solution that mass percentage concentration is 8%, for subsequent use;

[0031] In the second step, under microwave vibration or high-speed stirring, slowly add chitosan to the above-mentioned copper salt solution, and keep microwave vibration or high-speed stirring for 30-120min to obtain mixed solution A; wherein, chitosan is mixed in mixed solution A The mass fraction in is 10%;

[0032] In the third step, under ultrasonic vibration or high-speed stirring, the above-mentioned mixed solution A is slowly added to the above-mentioned methyl cellulose aqueous solution in a volume ratio of 7:4;

[0033] Then, at 40°C, ascorbic acid was added to react for 45 minutes according to the molar ratio of copper ions to 1:1.2, and then 2-3% pectin and 5-8% sodium alginate were added ...

Embodiment 2

[0041] Step 1. Preparation of antibacterial solution

[0042] The first step, prepare the methyl cellulose aqueous solution that mass percentage concentration is 10% and the copper sulfate solution that mass percentage concentration is 11% respectively, for subsequent use;

[0043] In the second step, under microwave vibration or high-speed stirring, chitosan is slowly added to the above-mentioned copper salt solution, and microwave vibration or high-speed stirring is maintained for 120 minutes to obtain mixed solution A; wherein, the amount of chitosan in mixed solution A The quality score is 10%;

[0044] In the third step, under ultrasonic vibration or high-speed stirring, the above-mentioned mixed solution A is slowly added to the above-mentioned methyl cellulose aqueous solution in a volume ratio of 7:4;

[0045] Then, at 40°C, ascorbic acid was added to react for 45 minutes according to the molar ratio of copper ions to 1:1.2, and then 2-3% pectin and 5-8% sodium algina...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

An antibacterial building concrete production process characterized by comprising the following steps: mixing by weight 6-10 parts of cement, 0.2-0.5 part of silica fume, 10-15 parts of sand, 15-20 parts of gravel, 1-2 parts of water and 0.02-0.05 part of antibacterial liquid, stirring 0.01-0.02 part of copper plated steel fiber, adding 0.01-0.05 part of a water reducing agent, and stirring again.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a process for making antibacterial building concrete. Background technique [0002] Concrete is one of the most commonly used building basic components in infrastructure construction at this stage. It has the characteristics of high bearing capacity, fast and convenient construction, low environmental pollution, reliable molding quality, and good comprehensive technical and economic benefits. It has been widely used in various provinces and cities across the country. scope of promotion. In the production process, it is usually made by mixing cement, mineral admixtures and sand. [0003] The concrete in the prior art has been quite mature for the technology of resisting sulphate, acid and alkali substances, etc. However, there is no resistance measure for some bacterial erosion such as anaerobic bacteria, which often causes the concrete body to become moldy, etc., whic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B14/02C04B14/06C04B14/36C04B18/14C04B103/30C04B103/67
CPCC04B20/1014C04B20/1048C04B28/00C04B28/02C04B28/04C04B40/0039C04B2103/67C04B2111/2092C04B18/146C04B14/06C04B14/02C04B14/368C04B16/0683C04B2103/302C04B14/48C04B16/0675C04B24/383C04B24/38C04B2103/0016Y02W30/91
Inventor 耿云花
Owner 湖州鸿鼎混凝土制品有限公司