Fire-retardant hydrolysis-resistance solvent-free polyurethane synthetic leather resin and preparation method and application thereof

A solvent-free polyurethane, hydrolysis-resistant technology, used in textiles and papermaking, etc., can solve the problems of different molding and processing methods, lack of systematic research on fire and flame retardant, and achieve better physical properties, good film strength and solvent resistance. The effect of hydrolysis resistance

Inactive Publication Date: 2016-10-12
HEFEI ANLI POLYURETHANE NEW MATERIAL
View PDF2 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, due to the different molding and processing methods from traditional solvent-based polyurethane synthetic leather, com

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] A flame-retardant hydrolysis-resistant solvent-free polyurethane resin for synthetic leather, consisting of a hydroxyl component A and an isocyanate component B:

[0058] Described A component is made up of the raw material of following weight part:

[0059] Polyether diol (Poly THF 2000) 40 parts

[0060] Polyether diol (polyoxypropylene diol DP-3000) 8 parts

[0061] Polyether triol (polyoxypropylene triol GY-6000E) 32 parts

[0062] Chain extender (ethylene glycol EG) 1 part

[0063] Chain extender (1,4-butanediol BDO) 3 parts

[0064] Cross-linking agent (glycerol) 1 part

[0065] Phosphate ester additive flame retardant 8 parts

[0066] Reactive flame retardant ( N,N -Diethyl di(2-hydroxyethyl)aminomethylene phosphonate) 4 parts

[0067] Reactive flame retardant (tri(dipropylene glycol) phosphite) 1 part

[0068] Foaming agent (H 2 0) 0.4 parts

[0069] Foam stabilizer (DC-3042 / DC-3043) 0.3 parts

[0070] Catalyst (BiCAT 8124) 0.1 parts

[0071] Light / ...

Embodiment 2

[0090] A flame-retardant hydrolysis-resistant solvent-free polyurethane resin for synthetic leather, consisting of a hydroxyl component A and an isocyanate component B:

[0091] Described A component is made up of the raw material of following weight part:

[0092] Polyether diol (Poly THF 2000) 45 parts

[0093] Polyether diol (polyoxypropylene diol DP-3000) 15 parts

[0094] Polyether triol (polyoxypropylene triol GY-6000E) 20 parts

[0095] Chain extender (ethylene glycol EG) 2 parts

[0096] Chain extender (1,4-butanediol BDO) 2 parts

[0097] Cross-linking agent (glycerol) 1.5 parts

[0098] 10 parts of melamine additive flame retardant

[0099] Reactive flame retardant (dimethyl N,N-di(2-hydroxyethyl)aminomethylphosphonate) 3.5 parts

[0100] Reactive flame retardant (tri(dipropylene glycol) phosphite) 1.5 parts

[0101] Foaming agent (H 2 0) 0.6 parts

[0102] Foam stabilizer (B 8715 LF2) 0.4 parts

[0103] Catalyst (Borchi Kat 22) 0.15 parts

[0104] Light / hea...

Embodiment 3

[0123] A flame-retardant hydrolysis-resistant solvent-free polyurethane resin for synthetic leather, consisting of a hydroxyl component A and an isocyanate component B:

[0124] Described A component is made up of the raw material of following weight part:

[0125] Polyether diol (Poly THF 2000) 20 parts

[0126] Polyether diol (polyoxypropylene diol DP-3000) 10 parts

[0127] Polyether triol (polyoxypropylene triol GY-6000E) 50 parts

[0128] Chain extender (ethylene glycol EG) 2 parts

[0129] Chain extender (1,4-butanediol BDO) 2 parts

[0130] Cross-linking agent (glycerol) 2 parts

[0131] Inorganic salt additive flame retardant 10 parts

[0132] Reactive flame retardant (organophosphate diol Exolit OP 550) 4 parts

[0133] Reactive flame retardant (tri(dipropylene glycol) phosphite) 1 part

[0134] Foaming agent (H 2 0) 0.8 parts

[0135] Foam stabilizer (L-3002) 0.35 parts

[0136] Catalyst (MB20) 0.15 parts

[0137] Light / heat stabilizer (UV-1164) 0.25 parts...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses fire-retardant hydrolysis-resistance solvent-free polyurethane synthetic leather resin. The resin is prepared by mixing a component A and a component B according to the mass ratio of 2:1-1:2. The component A comprises 30-60 parts of polyether diols, 20-50 parts of polyether triols, 0-5 parts of chain extender, 0-2 parts of cross linking agent, 0-10 parts of additive-type flame retardant, 0-5 parts of reactive-type flame retardant, 0-1 part of foaming agent, 0-0.5 part of catalyst, 0-0.5 part of foam stabilizer, and 0-1 part of light/heat stabilizer. The component B comprises 50-70 parts of polyether triols, 30-50 parts of isocyanate, and 0-0.1 part of catalyst. The invention further provides a preparation method and application of the resin. The solvent-free polyurethane synthetic leather made from the resin meets BS (British standard) 5852 NO. 0&1 flame standards and FMVOSS (Federal Motor Vehicle Safety Standard) NO. 302 flame standards.

Description

technical field [0001] The invention belongs to the technical field of chemical products and preparation methods thereof, and relates to a flame-retardant hydrolysis-resistant solvent-free polyurethane resin for synthetic leather, and also relates to a preparation method and application of the resin. Background technique [0002] As the global polyurethane synthetic leather industry and consumers have higher and higher environmental protection requirements for the VOC content of synthetic leather products, and with the continuous development and upgrading of industry technology, environmentally friendly polyurethane synthetic leather products have gradually developed and been consumed in recent years. recognized by those. Among them, solvent-free polyurethane synthetic leather is particularly favored as a category of environmentally friendly polyurethane synthetic leather products due to its outstanding physical properties and advantages in energy saving and emission reducti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/66C08G18/48C08G18/32C08J9/08D06N3/14C08G101/00
CPCC08G18/3887C08G18/3889C08G18/4812C08G18/6677C08G2110/0083D06N3/146D06N2211/28
Inventor 孔为青武春余李晓飞王海峰高兵王燕武笪丽红姚克俭黄万里
Owner HEFEI ANLI POLYURETHANE NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap