Heat-insulation paint used for automobile containing box and preparation method thereof

A technology of thermal insulation and storage boxes, applied in the field of coatings, to achieve the effects of short production cycle, simple preparation method and convenient transportation

Inactive Publication Date: 2016-10-12
安徽班合拍卖服务有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, people are paying more and more attention to the interior materials of automobiles and the articles in the automobile, and have higher and higher requirements for the coating performance and environmental protection of automotive supplies. The market demand and growing application prospects require the development of coatings with strong competitive advantages in terms of technology, cost, and performance, so that they have good protection and decoration for automotive products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A heat-insulating and heat-preserving coating for a car storage box, characterized in that it is made of the following raw materials in parts by weight: 15 parts of hydroxyl acrylic resin, 5 parts of pure acrylic emulsion, 5 parts of cellulose resin, 2 parts of vinyl resin, oxidized 1 part of aluminum, 0.2 part of leveling agent, 1 part of catalyst, 0.2 part of thickener, 1 part of talc, 1 part of silicon dioxide, 0.2 part of methyl isobutyl ketone, 0.3 part of dimethyl carbonate, 20 parts of deionized water part, 2 parts of pentaerythritol;

[0020] Its preparation method comprises the following steps in turn:

[0021] (1) Put hydroxyl acrylic resin, pure acrylic emulsion, cellulose resin, vinyl resin, aluminum oxide and deionized water into a reaction vessel, control the temperature at 50-60°C, and stir for 15 minutes to disperse the mixture evenly;

[0022] (2) Add talcum powder, silicon dioxide, methyl isobutyl ketone and dimethyl carbonate into the reaction vessel...

Embodiment 2

[0029] A heat-insulating and heat-preserving coating for a car storage box, characterized in that it is made of the following raw materials in parts by weight: 35 parts of hydroxyl acrylic resin, 20 parts of pure acrylic emulsion, 20 parts of cellulose resin, 10 parts of vinyl resin, oxidized 5 parts of aluminum, 1 part of leveling agent, 5 parts of catalyst, 1.5 parts of thickener, 5 parts of talc, 5 parts of silicon dioxide, 1 part of methyl isobutyl ketone, 2 parts of dimethyl carbonate, 50 parts of deionized water part, 10 parts of pentaerythritol;

[0030] Its preparation method comprises the following steps in turn:

[0031] (1) Put hydroxyacrylic resin, pure acrylic emulsion, cellulose resin, vinyl resin, aluminum oxide and deionized water into a reaction vessel, control the temperature at 50-60°C, and stir for 30 minutes to disperse the mixture evenly;

[0032] (2) Then add talcum powder, silicon dioxide, methyl isobutyl ketone and dimethyl carbonate into the reaction...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a heat-insulation paint used for an automobile containing box. The heat-insulation paint comprises the following raw materials: hydroxy acrylic resin, a pure acrylic emulsion, cellulose resin, ethene resin, alumina, a leveling agent, a catalyst, a thickening agent, powdered steatile, silica, methyl isobutyl ketone, dimethyl carbonate, deionized water and pentaerythritol. The preparation method comprises the following steps: 1) uniformly stirring the corresponding raw materials; 2) preparing a mixing solution; 3) preparing paint mixed liquor; and 4) grinding the paint mixed liquor, filtering the paint mixed liquor to obtain the finished product. The product has excellent performance, and has advantages of good high temperature resistance, flat and fine coating surface, and good light retention, tensile strength and breaking elongation are better than that of the common paint, the usage requirements of anticorrosion and weatherability of the automobile containing box on coating can be satisfied; and the preparation method has the advantages of simple process and low cost, and is adapted to industrial batch production.

Description

technical field [0001] The invention relates to the field of paint industry, in particular to a heat-insulating paint used for a car storage box and a preparation method thereof. Background technique [0002] With the development of social living standards, more and more people now own their own private cars. Auto supplies or car maintenance supplies have become an indispensable part of vehicle maintenance. As the three major sectors of the automotive aftermarket One, the auto supplies market is also one of the fastest growing and most promising industries. Along with the blowout development of my country's automobile industry, the development speed of the automobile supplies industry is increasing rapidly. According to statistics, in 2011, the total output value of my country's automobile supplies products has reached 430 billion yuan. At present, there are more than 100,000 dealers in my country's automobile supplies industry. Family. As the Chinese government pays more a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/14C09D133/04C09D101/02C09D7/12
CPCC09D133/14C08L2205/035C09D7/61C09D7/63C08L33/04C08L1/02C08K13/02C08K2003/2227C08K3/34C08K3/36C08K5/109
Inventor 韩梅
Owner 安徽班合拍卖服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products