Metal antirust agent

A technology of metal antirust agent and citric acid, which is applied in the field of metal antirust agent, can solve the problems of foam generation, affecting degreasing and decontamination effects, etc., and achieves the effects of strong antirust ability, strong degreasing and decontamination ability, and scientific and reasonable formula

Inactive Publication Date: 2016-10-26
梁红
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, many antirust agents will produce foam during use, which will affect the effect of degreasing and decontamination.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] Metal antirust agent, comprising the following components by weight: 6 parts of citric acid, 1 part of ethylenediaminetetraacetic acid, 4 parts of dibasic acid, 10 parts of monoethanolamine benzoate, 10 parts of triethanolamine, 10 parts of diethanolamine, synthesized 20 parts of boric acid ester, 25 parts of polyethylene glycol ester, 35 parts of epoxy acrylate resin, 30 parts of N-oleoyl acid octadecylamine salt, 0.4 part of silicone defoamer, 600 parts of water.

[0010] Add citric acid, ethylenediaminetetraacetic acid, and dibasic acid into the reaction kettle, then add monoethanolamine benzoate, triethanolamine, and diethanolamine to react, and keep the temperature at 40°C for 4 hours, then add silicone defoamer , Stir for 1h, then add water. Add N-oleoyl acid octadecylamine salt into the reaction kettle, and stir and react at 80°C for 40min. Add the synthetic boric acid ester, polyethylene glycol ester, and epoxy acrylate resin into the reaction kettle, stir and ...

Embodiment 2

[0012] A metal antirust agent, comprising the following components by weight: 8 parts of citric acid, 3 parts of ethylenediaminetetraacetic acid, 6 parts of dibasic acid, 15 parts of monoethanolamine benzoate, 15 parts of triethanolamine, 15 parts of diethanolamine, synthesized 25 parts of boric acid ester, 30 parts of polyethylene glycol ester, 40 parts of epoxy acrylate resin, 35 parts of N-oleoyl acid octadecylamine salt, 0.7 part of silicone defoamer, 700 parts of water.

[0013] Add citric acid, ethylenediaminetetraacetic acid, and dibasic acid into the reaction kettle, then add monoethanolamine benzoate, triethanolamine, and diethanolamine to react, and keep the temperature at 40°C for 4 hours, then add silicone defoamer , Stir for 1h, then add water. Add N-oleoyl acid octadecylamine salt into the reaction kettle, and stir and react at 80°C for 40min. Add the synthetic boric acid ester, polyethylene glycol ester, and epoxy acrylate resin into the reaction kettle, stir a...

Embodiment 3

[0015] A metal antirust agent, comprising the following components by weight: 10 parts of citric acid, 5 parts of ethylenediaminetetraacetic acid, 8 parts of dibasic acid, 20 parts of monoethanolamine benzoate, 20 parts of triethanolamine, 20 parts of diethanolamine, synthesized 30 parts of boric acid ester, 35 parts of polyethylene glycol ester, 45 parts of epoxy acrylate resin, 40 parts of N-oleoyl acid octadecylamine salt, 1.0 part of silicone defoamer, 800 parts of water.

[0016] Add citric acid, ethylenediaminetetraacetic acid, and dibasic acid into the reaction kettle, then add monoethanolamine benzoate, triethanolamine, and diethanolamine to react, and keep the temperature at 40°C for 4 hours, then add silicone defoamer , Stir for 1h, then add water. Add N-oleoyl acid octadecylamine salt into the reaction kettle, and stir and react at 80°C for 40min. Add the synthetic boric acid ester, polyethylene glycol ester, and epoxy acrylate resin into the reaction kettle, stir ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a metal antirust agent. The metal antirust agent comprises, by weight, 6-10 parts of citric acid, 1-5 parts of edetic acid, 4-8 parts of binary acid, 10-20 parts of monoethaneamine benzoate, 10-20 parts of triethanolamine, 10-20 parts of diethanol amine, 20-30 parts of synthetic boric acid ester, 25-35 parts of macrogol ester, 35-45 parts of epoxy acrylate resin, 30-40 parts of N-octadecane oeoyl sarcosine acid, 0.4-1.0 part of a silicon antifoaming agent and 600-800 parts of water. The metal antirust agent is scientific and reasonable in formula and free of hazardous substances such as trichloroethane and tetrachloroethane and environment pollution, and the ozone sphere at a high altitude cannot be damaged. The degreasing and decontamination capacity is high, and no harmful effect to non-ferrous metal exists. The antirust capability is high, foam is not produced, and the overflowing phenomenon cannot occur at a high pressure.

Description

technical field [0001] The invention relates to the field of chemical products, in particular to a metal antirust agent. Background technique [0002] Metal corrosion is a problem often encountered in production and life. Metal rust not only damages the shape, color and mechanical properties of the metal workpiece itself, but also reduces the quality of its products. In our country, the steel due to metal corrosion accounts for 20% of the total steel output every year, and about 30% of the equipment is scrapped due to corrosion, which not only pollutes the environment, but also wastes a lot of resources and energy consumption. The metal scrapped due to corrosion accounts for about 20%-40% of the world's annual metal output every year, and the corrosion of steel accounts for half of the metal corrosion, which is a serious waste of resources. [0003] Metal is widely used in various industries such as machinery, automobiles, home appliances, construction, etc. In order to imp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F11/173
CPCC23F11/173
Inventor 梁红
Owner 梁红
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com