Preparation method of graphene and capsaicin synthetic ship bottom paint
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of encapsaicin and graphene, applied in the field of coatings, can solve the problems of increased ship navigation resistance, accelerated metal corrosion, high toxicity, etc., and achieves good adhesion and compatibility, excellent self-lubrication, and excellent conductivity Effect
Inactive Publication Date: 2016-11-16
刘方旭
View PDF0 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Marine biofouling will increase the navigation resistance of ships, lead to accelerated metal corrosion, block seawater pipelines, and reduce the service life of marine equipment
For this reason, people have studied a variety of antifouling technologies. In the early days, compounds such as mercury and arsenic were used to prepare antifouling coatings, but they were eliminated due to the high toxicity of these substances; Antifouling paints formulated with vinyl resin and chlorinated rubber as the main base materials; since the 1960s, people have applied organotin compounds to antifouling paints to prolong the antifouling time, but these antifouling paints contain chemical toxicity Substances have the defect of polluting the marine environment, and the traditional antifouling paint is poor in seawater impact resistance, and the wear resistance is generally about 1 year; it needs frequent paint repairs and maintenance, which leads to increased maintenance costs for the hull, which affects the antifouling and antifouling properties of the hull. Rust has brought many disadvantages
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0011] The components are: 10 parts, 10 parts of capsaicin, 23 parts of acrylic resin, 5 parts of chlorinated paraffin, 6 parts of xylene, 28 parts of talcum powder, 15 parts of zinc yellow, and 3 parts of additives.
[0012] The preparation steps are as follows:
[0013] (1) solvent preparation: acrylic resin and xylene are mixed and stirred evenly to obtain a mixed solvent;
[0014] (2) Mixing: Put the mixed solvent into the mixing tank, then put graphene, capsaicin, chlorinated rubber, chlorinated paraffin and solvent into the container and stir evenly, then add talcum powder, zinc yellow and additives and stir evenly , to get a mixture;
[0015] (3) Grinding: use a colloid mill to grind the mixture until the fineness reaches 20um, and then the graphene capsaicin synthetic bottom paint is obtained.
Embodiment 2
[0017] 12 parts of graphene, 16 parts of capsaicin, 20 parts of acrylic resin, 6 parts of chlorinated paraffin, 8 parts of xylene, 20 parts of talcum powder, 13 parts of zinc yellow, and 5 parts of additives.
[0018] The preparation steps are as follows:
[0019] (1) solvent preparation: acrylic resin and xylene are mixed and stirred evenly to obtain a mixed solvent;
[0020] (2) Mixing: Put the mixed solvent into the mixing tank, then put graphene, capsaicin, chlorinated rubber, chlorinated paraffin and solvent into the container and stir evenly, then add talcum powder, zinc yellow and additives and stir evenly , to get a mixture;
[0021] (3) Grinding: use a colloid mill to grind the mixture until the fineness reaches 20um, and then the graphene capsaicin synthetic bottom paint is obtained.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a method for preparing a graphene capsaicin synthetic boat bottom paint. The components include: 10-12 parts of graphene, 10-16 parts of capsaicin, 20-23 parts of acrylic resin, and 5-6 parts of chlorinated paraffin 6-8 parts of xylene, 20-28 parts of talcum powder, 13-15 parts of zinc yellow, 3-5 parts of additives; among them, graphene has high strength, wear resistance, self-lubrication and excellent conductivity characteristics, can greatly increase the wear resistance of ship bottom paint; capsaicin is a stable alkaloid; it is not affected by temperature, and has the function of antibacterial and repelling marine attached organisms; compared with chemical coating additives, spicy It will not poison attached organisms, cause biological variation, and will not destroy the marine food chain or cause sea water pollution; and it has good matching properties when mixed with acrylic resin, chlorinated paraffin, xylene, talcum powder, and zinc yellow. Good adhesion and compatibility.
Description
technical field [0001] The invention relates to the technical field of coatings, in particular to a method for preparing a graphene capsaicin-synthesized boat bottom paint. Background technique [0002] Marine biofouling is the biofouling formed by the adsorption and growth of marine microorganisms, animals and plants on the surface of the hull or marine facilities, which brings many adverse effects to marine shipping and development. Marine biofouling will increase the navigation resistance of ships, lead to accelerated metal corrosion, block seawater pipelines, and reduce the service life of marine equipment. For this reason, people have studied a variety of antifouling technologies. In the early days, compounds such as mercury and arsenic were used to prepare antifouling coatings, but they were eliminated due to the high toxicity of these substances; Antifouling paints formulated with vinyl resin and chlorinated rubber as the main base materials; since the 1960s, people ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more