An acrylic pigment and nanotechnology, applied in the field of pigments, can solve the problems of cracking on the screen, easy oxidation of oil film, etc., and achieve the effects of small color difference change, improved stability, and high color fastness to light.

Inactive Publication Date: 2016-11-23
苏州冰心文化用品有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The works of acrylic paint have a longer durability, and the oil film in oil painting is easy to oxidize after a long time, and it will turn yellow and harden, which will easily cause cracks in the picture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Step 1: Take calcium aluminate and mechanically mill it in a ball mill, the ball-to-material ratio in the ball mill is 30:1, and the milling time is 2 hours;

[0037] Step 2: Take 28 parts by weight of acrylate emulsion, 3 parts of gum arabic, 6 parts of glycerin, 4 parts of triethanolamine, 6 parts of ethylene glycol butyl ether acetate, 5 parts of aminopropylamine dioleate, polyoxypropylene glyceryl ether 1 part, mix in a stirring tank, the temperature in the stirring tank is 60°C, the stirring speed is 100r / min, and stir for 50min;

[0038] Step 3: Add 6 parts of cetyl palmitate, 1 part of calcium aluminate, 2 parts of nano-calcium oxide, and 5 parts of phthalocyanine green G into the mixing tank in step 2, stir for 40 minutes, and cool to form a composite nano-acrylic pigment.

Embodiment 2

[0040] Step 1: Take calcium aluminate and mechanically mill it in a ball mill, the ball-to-material ratio in the ball mill is 15:1, and the milling time is 5 hours;

[0041] Step 2: Take 19 parts of acrylate emulsion, 8 parts of gum arabic, 2 parts of glycerin, 7 parts of triethanolamine, 2 parts of ethylene glycol butyl ether acetate, 2 parts of aminopropylamine dioleate, and polyoxypropylene glyceryl ether by weight 4 parts, mixed in a stirring tank, the temperature in the stirring tank was 40°C, the stirring speed was 200r / min, and stirred for 30min;

[0042] Step 3: Add 2 parts of hexadecyl palmitate, 4 parts of calcium aluminate, 5 parts of nano-calcium oxide, and 2 parts of phthalocyanine green G into the mixing tank in step 2, stir for 20 minutes, and cool to form a composite nano-acrylic pigment.

Embodiment 3

[0044] Step 1: Take calcium aluminate and mechanically mill it in a ball mill, the ball-to-material ratio in the ball mill is 30:1, and the milling time is 2 hours;

[0045] Step 2: Take 26 parts by weight of acrylate emulsion, 7 parts of gum arabic, 3 parts of glycerin, 5 parts of triethanolamine, 5 parts of ethylene glycol butyl ether acetate, 3 parts of aminopropylamine dioleate, polyoxypropylene glyceryl ether 2 parts, mix in a stirring tank, the temperature in the stirring tank is 60°C, the stirring speed is 100r / min, and stir for 50min;

[0046] Step 3: Add 3 parts of cetyl palmitate, 3 parts of calcium aluminate, 4 parts of nano-calcium oxide, and 4 parts of phthalocyanine green G into the mixing tank of step 2, stir for 40 minutes, and cool to form a composite nano-acrylic pigment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite nano acrylic pigment and a preparation method thereof. The preparation method comprises the following steps: step 1: take calcium aluminate and mechanically ball mill it in a ball mill; step 2: take 19-28 parts of acrylate emulsion by weight , Gum Arabic 3‑8 parts, glycerin 2‑6 parts, triethanolamine 4‑7 parts, ethylene glycol butyl ether acetate 2‑6 parts, aminopropylamine dioleate 2‑5 parts, polyoxypropylene glyceryl ether 1 ‑4 parts, mixed in a mixing tank, the temperature in the mixing tank is 40‑60 °C, the stirring speed is 100‑200r / min, stirring for 30‑50min; Step 3: Add cetyl palmitic acid to the mixing tank in step 2 2-6 parts of ester, 1-4 parts of calcium aluminate, 2-5 parts of nano-calcium oxide, 2-5 parts of phthalocyanine green G, and then stirred for 20-40 minutes, cooled to form a composite nano-acrylic pigment.

Description

technical field [0001] The invention belongs to the field of pigments and relates to a composite nano acrylic pigment and a preparation method thereof. Background technique [0002] Acrylic paint is a synthetic polymer pigment, invented in the 1950s, made of pigment powder mixed with acrylic latex. Acrylic latex is also known as acrylic resin polymerized latex. There are many kinds of acrylic resins, such as methacrylic resins, and therefore, there are many kinds of acrylic paints. Foreign pigment manufacturers have produced acrylic series products, such as matt acrylic paint, semi-matt acrylic paint and glossy acrylic paint, as well as acrylic matte oil, glazing oil, molding ointment and so on. The works of acrylic paint have a longer durability, and the oil film in oil painting is easy to oxidize after a long time, and it will turn yellow and harden, which will easily cause cracks in the picture. The characteristics of acrylic paint superior to other kinds of paint are:...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/06C09D133/04C09D7/12
CPCC09D5/06C08L2205/03C09D7/61C09D7/63C09D7/65C09D133/04
Inventor 李冰心
Owner 苏州冰心文化用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap