Aeolian sand reuse interior wall brick and its production method

An aeolian sand and interior wall brick technology, applied in the field of interior wall bricks, can solve the problems of poor appearance and general strength of ceramic bricks, and achieve the effects of low manufacturing cost, high breaking strength and easy storage.

Active Publication Date: 2019-02-22
鄂尔多斯市同圆库布其生态工业治沙股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the ceramic tiles made of the above-mentioned raw materials and components have poor appearance and poor strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0016] The raw materials for making interior wall bricks are: wind-blown sand 55wt%, diatomite 10wt%, clinker 15wt%, white clay 10wt%, coal gangue 9.5wt%, nickel powder 0.5wt%; glaze raw materials are : Aeolian sand 16wt%, white clay 37wt%, ball clay 3wt%, zirconium silicate 13wt%, barium carbonate 15wt%, alumina powder 16wt%.

[0017] Its manufacturing process is:

[0018] Firstly, raw material collection and transportation: raw materials are transported by car to the raw material yard or raw material warehouse, and raw material selection is carried out; then raw material preparation: hard raw materials are unloaded into their respective box feeders by wheel loaders, The feeder is proportioned according to the standard ratio and transported to the belt conveyor to supply the jaw crusher for coarse crushing, then enters the hammer crusher for crushing, and then enters the fine crushing roller machine for fine crushing, and then passes through the rolling sieve for screening, a...

specific Embodiment 2

[0019] The raw materials for making interior wall bricks are 60wt% aeolian sand, 10wt% diatomite, 10wt% clinker, 9.8wt% white clay, 10wt% coal gangue, and 0.2wt% nickel powder; the glaze raw materials are : Aeolian sand 15wt%, white clay 40wt%, ball soil 4wt%, zirconium silicate 15wt%, barium carbonate 16wt%, alumina powder 10wt%.

[0020] Its manufacturing process is:

[0021] Firstly, raw material collection and transportation: raw materials are transported by car to the raw material yard or raw material warehouse, and raw material selection is carried out; then raw material preparation: hard raw materials are unloaded into their respective box feeders by wheel loaders, The feeder is proportioned according to the standard ratio and transported to the belt conveyor to supply the jaw crusher for coarse crushing, then enters the hammer crusher for crushing, and then enters the fine crushing roller machine for fine crushing, and then passes through the rolling sieve for screenin...

specific Embodiment 3

[0022]The raw materials for making interior wall bricks are: blown sand 58.5wt%, diatomite 12.7wt%, clinker 9wt%, white clay 9.5wt%, coal gangue 10wt%, nickel powder 0.3wt%; glaze The raw materials are: aeolian sand 17wt%, white clay 43wt%, ball clay 3wt%, zirconium silicate 13wt%, barium carbonate 15wt%, alumina powder 9wt%.

[0023] Its manufacturing process is:

[0024] Firstly, raw material collection and transportation: raw materials are transported by car to the raw material yard or raw material warehouse, and raw material selection is carried out; then raw material preparation: hard raw materials are unloaded into their respective box feeders by wheel loaders, The feeder is proportioned according to the standard ratio and transported to the belt conveyor to supply the jaw crusher for coarse crushing, then enters the hammer crusher for crushing, and then enters the fine crushing roller machine for fine crushing, and then passes through the rolling sieve for screening, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an interior wall brick made of recyclable aeolian sand and production method thereof. The raw material for the blank of the interior wall brick comprises, by weight, 55%-60% of aeolian sand, 10%-15% of diatomaceous earth, 10%-15% of clinker, 8%-10% of white clay, 5%-10% of coal gangue, 0.2%-0.5% of nickel powder; the raw materials for the glaze includes, by weight, 12%-17% of aeolian sand, 37%-43% of white clay, 3%-6% of ball clay, 13%-17% of zirconium silicate, 15%-16% of barium carbonate and 8%-16% of alumina powder. The interior wall brick produced according to the method has comparatively minor pollution to the environment. Also the raw materials for the production are easy to secure. The production cost is low and the tearing resistance is high.

Description

technical field [0001] The invention belongs to the field of inorganic non-metallic materials (ceramics), and in particular relates to a method for preparing interior wall bricks by using aeolian sand and the prepared interior wall bricks. Background technique [0002] Aeolian sand is sandy soil formed on the surface after natural wind transport, grading, and precipitation. Its particles are uniform, fine, and stable in composition. The main mineral is feldspar mixed with quartz, mica, etc. [0003] The total area of ​​China's deserts is about 700,000 square kilometers. If including the Gobi of more than 500,000 square kilometers, the total area is 1.28 million square kilometers, accounting for 13% of the country's total land area. The arid region in Northwest China is the most concentrated area of ​​deserts in China, accounting for about 80% of the total desert area in the country, and the desertification of the land has made the land unusable for cultivation. Especially i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/14C04B35/622C03C8/00
CPCC03C8/00C04B35/14C04B35/622C04B2235/349C04B2235/405
Inventor 淖门生
Owner 鄂尔多斯市同圆库布其生态工业治沙股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com