Loadable solvent-free epoxy resin floor coating

A technology for epoxy resin and floor coatings, applied in the direction of epoxy resin coatings, anti-corrosion coatings, coatings, etc., can solve the problems of reduced coating performance, high coating viscosity, and reduced cross-linking density, achieving short drying time, The effect of high bond strength, high tensile strength and high hardness

Active Publication Date: 2017-01-18
胜利油田德利实业有限责任公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Reactive diluents are generally added to solvent-free epoxy coatings to reduce the viscosity and facilitate construction, but it will lead to a decrease in cross-linking density and reduce the performance of the coating.
Without adding active diluent, the viscosity of the paint is very high, so it can only be applied by double-tube feeding heating and airless spraying

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Loadable solvent-free epoxy resin floor coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A load-bearing solvent-free epoxy resin floor coating, consisting of A and B components;

[0023] Component A is composed of the following raw materials in parts by weight: 90 parts of bisphenol A epoxy resin, 5 parts of allyl glycidyl ether, 2 parts of butyl glycidyl ether, 0.6 part of BYK-A530, cobalt naphthenate 1 part, 5 parts of precipitated barium sulfate, 2 parts of quartz powder, 15 parts of color paste, 0.6 part of organomodified polysiloxane, 0.9 part of KH-560, 0.1 part of BYK-110, 0.5 part of BYK-P104S, 40 parts of quartz sand 15 parts of tea stalk powder;

[0024] Component B consists of the following raw materials in parts by weight: 10 parts of modified polyamide, 2.0 parts of trimethylhexamethylenediamine;

[0025] The weight ratio of A component to B component is 5:1.

Embodiment 2

[0027] A load-bearing solvent-free epoxy resin floor coating, consisting of A and B components;

[0028] Component A consists of the following raw materials in parts by weight: 95 parts of bisphenol A epoxy resin, 4 parts of allyl glycidyl ether, 3 parts of butyl glycidyl ether, 0.4 parts of BYK-A530, cobalt naphthenate 1.2 parts, 4 parts of precipitated barium sulfate, 3 parts of quartz powder, 12 parts of color paste, 1.0 parts of organomodified polysiloxane, 0.5 parts of KH-560, 0.4 parts of BYK-110, 0.3 parts of BYK-P104S, 42 parts of quartz sand 12 parts of tea stalk powder;

[0029] Component B consists of the following raw materials in parts by weight: 12 parts of modified polyamide, 1.0 part of trimethylhexamethylenediamine;

[0030] The weight ratio of A component to B component is 5:1.

Embodiment 3

[0032] A load-bearing solvent-free epoxy resin floor coating, consisting of A and B components;

[0033] Component A consists of the following raw materials in parts by weight: 100 parts of bisphenol A epoxy resin, 3 parts of allyl glycidyl ether, 4 parts of butyl glycidyl ether, 0.2 parts of BYK-A530, cobalt naphthenate 1.4 parts, 2 parts of precipitated barium sulfate, 4 parts of quartz powder, 10 parts of color paste, 1.3 parts of organic modified polysiloxane, 0.3 parts of KH-560, 0.6 parts of BYK-110, 0.1 parts of BYK-P104S, 45 parts of quartz sand 10 parts of tea stalk powder;

[0034] Component B consists of the following raw materials in parts by weight: 15 parts of modified polyamide, 0.2 part of trimethylhexamethylenediamine;

[0035] The weight ratio of A component to B component is 5:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of epoxy coating, and particularly relates to a loadable solvent-free epoxy resin floor coating. The coating is prepared from a component A and a component B; the component A is prepared from, by weight, 90-100 parts of bisphenol A epoxy resin, 40-45 parts of quartz sand and 10-15 parts of tea stem powder; the component B is prepared from, by weight, 10-15 parts of modified polyamide and 0.2-2.0 parts of trimethyl hexamethylene diamine; the mass ratio of the component A to the component B is 5:1. The coating is environmentally friendly, high in hardness, good in wear resistance, applicable heavy-load places, good in chemical resistance, high in adhesive force, excellent in durability and corrosion resistance, resistant to scratches, short in drying time and easy and convenient to construct.

Description

technical field [0001] The invention belongs to the field of preparation of epoxy coatings, and in particular relates to a load-carrying solvent-free epoxy resin floor coating. Background technique [0002] Epoxy resin coatings have the advantages of strong anti-corrosion ability, strong adhesion, high hardness, wear resistance, salt spray resistance, acid and alkali resistance, high gloss, high solid content, and high fullness. Therefore, it is widely used as industrial heavy-duty anti-corrosion paint, anti-rust primer, floor paint, oil tank paint, drinking water tank paint, etc. However, traditional solvent-based coatings contain more than 30% organic solvents. During the process of manufacturing, construction, drying, and curing of coatings, a large amount of VOC is released into the atmosphere, which constitutes extremely serious pollution and harm to the human ecological environment. threaten. The solvent-free epoxy coating has no volatile organic solvents, is non-tox...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/12C09D5/08
CPCC08L2205/035C09D5/08C09D163/00C08L83/04C08L97/02C08K13/02C08K3/36C08K2003/3045C08K5/098
Inventor 谢桂秀郑鸿芳陈宙飞杨喜丽
Owner 胜利油田德利实业有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More