A kind of uv offset printing freezing point ink and preparation method thereof

A technology of ink and freezing point, which is applied in the field of UV offset printing freezing point ink and its preparation, can solve the problems of slow drying speed, weak adhesion and poor water resistance, and achieve the effects of fast drying speed, strong adhesion and strong water resistance

Active Publication Date: 2017-06-30
东莞智源彩印有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] At present, there are not many UV offset printing freezing point ink products on the market, and there are generally problems such as slow drying speed, weak adhesion, and poor water resistance. Therefore, it is necessary to develop a UV offset printing with excellent properties such as strong adhesion and good water resistance. Freezing Ink

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of uv offset printing freezing point ink and preparation method thereof
  • A kind of uv offset printing freezing point ink and preparation method thereof
  • A kind of uv offset printing freezing point ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1, UV offset printing freezing point ink of the present invention and its preparation

[0033] Formula: polymer resin binder 300kg, reactive diluent 300kg, photoinitiator ITX 50kg, PTFE wax powder 80kg and Lubrizol hyperdispersant 325001kg.

[0034] The polymer resin binder is obtained by mixing polyketone resin, polyurethane acrylate resin and polyester acrylic resin in a weight ratio of 1:1.8:1.6.

[0035] The reactive diluent is obtained by mixing trimethylolpropane triacrylate and acryloyl morpholine in a weight ratio of 1:2.

[0036] Preparation method: S1. Mix and boil the photoinitiator of the formulated amount and 1 / 3 of the reactive diluent of the formulated amount to obtain the photoinitiator mixed solution, which is set aside;

[0037] S2. Add the formula amount of polymer resin binder and 2 / 3 formula amount of reactive diluent into the stirring tank, disperse and stir at 600r / min for 20min to obtain the pre-prepared resin liquid, and then add the...

Embodiment 2

[0039] Embodiment 2, UV offset printing freezing point ink of the present invention and its preparation

[0040] Formula: polymer resin binder 500kg, reactive diluent 500kg, photoinitiator 379100kg, nano calcium carbonate 150kg and Lubrizol hyperdispersant 3250020kg.

[0041] The polymer resin binder is obtained by mixing polyketone resin, polyurethane acrylate resin and polyester acrylic resin in a weight ratio of 1:2.4:2.2.

[0042] The reactive diluent is obtained by mixing trimethylolpropane triacrylate and acryloyl morpholine in a weight ratio of 1:4.

[0043] Preparation method: S1. Mix and boil the photoinitiator of the formulated amount and 1 / 3 of the reactive diluent of the formulated amount to obtain the photoinitiator mixed solution, which is set aside;

[0044] S2. Add the formula amount of polymer resin binder and 2 / 3 formula amount of reactive diluent into the stirring tank, disperse and stir at 800r / min for 30min to obtain the pre-prepared resin liquid, and the...

Embodiment 3

[0046] Embodiment 3, UV offset printing freezing point ink of the present invention and its preparation

[0047] Formula: polymer resin binder 460kg, reactive diluent 380kg, photoinitiator TPO 80kg, polytetrafluoroethylene wax powder 100kg and Lubrizol hyperdispersant 3250010kg.

[0048] The polymer resin binder is obtained by mixing polyketone resin, polyurethane acrylate resin and polyester acrylic resin in a weight ratio of 1:2.0:1.8.

[0049] The reactive diluent is obtained by mixing trimethylolpropane triacrylate and acryloyl morpholine in a weight ratio of 1:3.

[0050] Preparation method: S1. Mix and boil the photoinitiator of the formulated amount and 1 / 3 of the reactive diluent of the formulated amount to obtain the photoinitiator mixed solution, which is set aside;

[0051] S2. Add the formula amount of polymer resin binder and 2 / 3 formula amount of reactive diluent into the mixing tank, disperse and stir at 700r / min for 25min to obtain the pre-prepared resin liqui...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of printing ink and particularly relates to a UV offset print freezing-point printing ink and a preparation method thereof. The UV offset print freezing-point printing ink is prepared from the following raw materials in parts by weight: 30-50 parts of macromolecular resin junction material, 30-50 parts of a reactive diluent, 5-10 parts of a photoinitiator, 8-15 parts of a filler and 0.1-2 parts of an accessory ingredient. The UV offset print freezing-point printing ink is applied to product package printing, and has the advantages of rapid curing speed, short curing time, long storage time, good stability, strong adhesive force, rub resistance, water resistance, ageing resistance, high glossiness, bright color, distinctive line and the like.

Description

technical field [0001] The invention belongs to the technical field of ink, and in particular relates to a UV offset printing freezing point ink and a preparation method thereof. Background technique [0002] Freezing point ink, also known as snowflake ink, in the industry, the pattern of "snowflake" is larger, generally larger than 2mm, and the pattern of "freezing point" is smaller, generally less than 2mm. Freezing point ink is a kind of UV ink that can produce fine and uniform texture on the surface of the ink after twice curing, which can protect and decorate the surface of the product, so it is widely used in the packaging and printing industry, especially in the domestic cigarette pack printing industry . [0003] Resin is one of the important components of ink. It is divided into two types: UV resin and ordinary resin. The former needs to be cured by UV light of a specific wavelength, and the latter can be cured under specific temperature (or heat) conditions. In t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/101C09D11/102C09D11/104C09D11/03
CPCC09D11/03C09D11/101C09D11/102C09D11/104
Inventor 徐国民刘卫管韶坤李朝刚陈明
Owner 东莞智源彩印有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com