Carbon nanotube-polytetrafluoroethylene valve sealing ring filled with modified mullite powder

A technology of polytetrafluoroethylene and mullite powder, which is applied in the field of valve sealing rings, can solve the problems of poor mechanical properties, large linear expansion coefficient, and low hardness, and achieve stable thermochemical properties, small thermal expansion coefficients, and good sealing performance. Effect

Inactive Publication Date: 2017-02-15
ANHUI RONGDA VALVE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polytetrafluoroethylene (PTFE) is characterized by its high chemical stability, strong high and low temperature resistance, outstanding non-stickiness, good lubricity, excellent electrical insulation, aging resistance, minimal water absorption, etc. , making it widely used in aerospace, petrochemical, mechanical industry, electronic appliances, food industry, textile and other fields. However, due to its poor mechanical properties, large linear expansion coefficient, poor creep resistance, poor wear resistance, low hardness, and difficulties in forming and secondary processing, its application range is limited to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] A carbon nano-polytetrafluoroethylene valve sealing ring filled with modified mullite powder, prepared from the following components by weight: 100 parts of polytetrafluoroethylene, 5 parts of polyphenylene sulfide resin, 5 parts of carbon nanotubes 1 part, 8 parts of phenol, 10 parts of p-toluic acid, 1 part of bentonite, 8 parts of diphenyl ether, 1 part of butyl titanate, 20 parts of 60-70% sodium hypochlorite, 25 parts of EDTA, 50 parts of ammonia water, absolute ethanol 100 parts, 5 parts of mullite, 50 parts of 10-15% hydrogen peroxide, 100 parts of deionized water, 2 parts of 2,4,6-triphenol, 3 parts of ethyl cyanoacrylate, 2 parts of crosslinking agent TAC , 1 part of molybdenum disulfide, 3 parts of silane coupling agent kh550, 10 parts of ammonium chloride, 35 parts of urea, and 35 parts of water.

[0023] A carbon nano-polytetrafluoroethylene valve sealing ring filled with modified mullite powder is prepared by the following steps:

[0024] (1) Activation of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a carbon nanotube-polytetrafluoroethylene valve sealing ring filled with modified mullite powder. The valve sealing ring is prepared from the following components: polytetrafluoroethylene, polyphenylene sulfide, carbon nanotubes, phenol, p-toluylic acid, bentonite, diphenyl ether, butyl titanate, sodium hypochlorite with a concentration of 60 to 70%, EDTA, ammonia water, absolute ethyl alcohol, mullite, hydrogen peroxide with a concentration of 10 to 15%, deionized water, 2,4,6-trisphenol, ethyl alpha-cyanoacrylate, a cross-linking agent TAC, molybdenum disulfide, a silane coupling agent KH550, ammonium chloride, urea and water. The sealing ring provided by the invention has good sealing performance, high hardness, small thermal expansion coefficient, high refractoriness, stable thermo-chemical performance and other excellent performance.

Description

technical field [0001] The invention belongs to the field of valve sealing rings, and in particular relates to a modified mullite powder filled polytetrafluoroethylene valve sealing ring and its preparation method and application. Background technique [0002] Polytetrafluoroethylene (PTFE) is characterized by its high chemical stability, strong high and low temperature resistance, outstanding non-stickiness, good lubricity, excellent electrical insulation, aging resistance, minimal water absorption, etc. , making it widely used in aerospace, petrochemical, mechanical industry, electronic appliances, food industry, textile and other fields. However, due to its poor mechanical properties, large linear expansion coefficient, poor creep resistance, poor wear resistance, low hardness, and difficulties in forming and secondary processing, its application range is limited to a certain extent. In order to improve and overcome the defects of pure PTFE, surface modification, filling...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/18C08L81/02C08K13/06C08K9/02C08K9/04C08K7/24C08K3/34
CPCC08K2201/003C08K2201/011C08L27/18C08L2201/02C08L2201/08C08L81/02C08K13/06C08K9/02C08K9/04C08K9/08C08K7/24C08K3/34
Inventor 胡光荣
Owner ANHUI RONGDA VALVE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products