Super-transparent acrylate pressure-sensitive adhesive emulsion capable of being coated at high speed as well as preparation method and application thereof

A technology of ultra-transparent acrylate and pressure-sensitive adhesive emulsion, which is applied in the field of pressure-sensitive adhesives, can solve the problems of affecting the health of operators, polluting the environment, and high costs, and achieves the goals of ensuring mechanical stability, improving light transmittance, and saving costs. Effect

Active Publication Date: 2017-03-22
余姚市维特胶粘制品有限公司
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Solvent-type acrylate has excellent comprehensive properties, but it contains 50-70% of organic solvents such as toluene and ethyl acetate, which not only affects the health of operators, pollutes the environment, but also has high costs. This situation prompts people to urgently search for and Development of a new type of ultra-transparent pressure-sensitive adhesive that can be coated at high speed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] In terms of parts by weight, the formula of the super transparent acrylate pressure-sensitive adhesive emulsion that can be coated at high speed is:

[0060] 80 parts of isooctyl acrylate

[0061] Styrene 15 parts

[0062] Acrylic 4 parts

[0063] 3 parts cyclohexyl acrylate

[0064] n-dodecanethiol 0.01 parts

[0065] Allyloxy nonylphenol polyoxyethylene sulfonate 0.52 parts

[0066] Allyloxy nonylphenol polyoxyethylene 0.28 parts

[0067] Sodium bicarbonate 0.02 part

[0068] Silicone defoamer 0.02 parts

[0069] 0.05 part of diisooctyl sulfonate

[0070] Potassium persulfate 0.25 parts

[0071] Ammonia 0.05 part

[0072] Appropriate amount of deionized water

[0073] The preparation method of the super transparent acrylate pressure-sensitive adhesive emulsion that can be coated at a high speed comprises the following steps:

[0074] (1) Mix and stir allyloxynonylphenol polyoxyethylene sulfonate, allyloxynonylphenol polyoxyethylene, sodium bicarbonate and 3...

Embodiment 2

[0081] In terms of parts by weight, the formula of the super transparent acrylate pressure-sensitive adhesive emulsion that can be coated at high speed is:

[0082] 72 parts of isooctyl acrylate

[0083] 18 parts ethyl acrylate

[0084] Styrene 12 parts

[0085] 6 parts of hydroxyethyl acrylate

[0086] 2.5 parts of isobornyl methacrylate

[0087] n-dodecanethiol 0.01 parts

[0088] Allyloxyoctylphenol polyoxyethylene sulfonate 0.52 parts

[0089] Allyloxy nonylphenol polyoxyethylene 0.28 parts

[0090] Mineral oil defoamer 0.02 parts

[0091] 0.05 part of diisooctyl sulfonate

[0092] Ammonium persulfate 0.3 parts

[0093] Ammonia 0.05 part

[0094] Appropriate amount of deionized water

[0095] The preparation method of the super transparent acrylate pressure-sensitive adhesive emulsion that can be coated at a high speed comprises the following steps:

[0096] (1) First mix and stir allyloxyoctylphenol polyoxyethylene sulfonate, allyloxynonylphenol polyoxyethylene...

Embodiment 3

[0103] In terms of parts by weight, the formula of the super transparent acrylate pressure-sensitive adhesive emulsion that can be coated at high speed is:

[0104] Butyl acrylate 75 parts

[0105] Vinyl acetate 15 parts

[0106] 4 parts hydroxypropyl acrylate

[0107] 3 parts cyclohexyl acrylate

[0108] n-dodecanethiol 0.02 parts

[0109] Allyloxy nonylphenol polyoxyethylene sulfonate 0.6 parts

[0110] Allyloxyoctylphenol polyoxyethylene 0.35 parts

[0111] Sodium bicarbonate 0.01 parts

[0112] Mineral oil defoamer 0.03 parts

[0113] Diisooctyl sulfonate 0.04 parts

[0114] Potassium persulfate 0.25 parts

[0115] Ammonia 0.04 parts

[0116] Appropriate amount of deionized water

[0117] The preparation method of the super transparent acrylate pressure-sensitive adhesive emulsion that can be coated at a high speed comprises the following steps:

[0118] (1) Mix and stir allyloxy nonylphenol polyoxyethylene sulfonate, allyloxyoctylphenol polyoxyethylene, sodium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses super-transparent acrylate pressure-sensitive adhesive emulsion capable of being coated at a high speed. The super-transparent acrylate pressure-sensitive adhesive emulsion is prepared from the following raw materials in parts by weight: 60 to 90 parts of an acrylate soft monomer, 3 to 25 parts of an acrylate hard monomer, 0 to 10 parts of a functional monomer, 2 to 10 parts of a high-refractive-index monomer, 0 to 0.05 part of a molecular weight regulator, 0.1 to 0.8 part of a reactive anionic emulsifier, 0.1 to 0.5 part of a reactive non-ionic emulsifier, 0.02 to 0.1 part of a defoaming agent, 0 to 0.08 part of a base material wetting agent, 0.2 to 1.0 part of an initiator and water; the pH (Potential of Hydrogen) value of the pressure-sensitive adhesive emulsion is 7.5 to 8, and the solid content is 40 percent to 55 percent. The pressure-sensitive adhesive emulsion disclosed by the invention can be coated at the high speed (150m / min to 300m / min), and an adhesive surface has no defects including bubbles and the like; the stripping force is not lower than 2.0N / 10mm, and the light transmittance can reach 90 percent or more; the super-transparent acrylate pressure-sensitive adhesive emulsion can be widely applied to protective adhesive films in the fields of manufacturing decoration, electronics, electrical appliances, automobile industries and the like.

Description

technical field [0001] The invention belongs to the field of pressure-sensitive adhesives, and in particular relates to a super-transparent acrylic pressure-sensitive adhesive emulsion that can be coated at a high speed and a preparation method and application thereof. Background technique [0002] The ultra-transparent acrylate pressure-sensitive adhesive that can be coated at high speed means that within the coating speed range of 150-300m / min, there is no residual adhesive on the surface of the adherend when it is peeled off from the adherend, and it maintains a certain mechanical strength. At the same time, it has high Light transmittance and low haze value. [0003] At present, the ultra-transparent acrylate pressure-sensitive adhesives that can be coated at high speed are mainly solvent-based acrylates. Solvent-type acrylate has excellent comprehensive properties, but it contains 50-70% of organic solvents such as toluene and ethyl acetate, which not only affects the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/18C08F212/08C08F220/06C08F220/28C08F218/08C08F2/26C08F2/30C09J133/08C09J7/02
CPCC09J7/22C09J7/38C09J133/08C08F2/26C08F2/30C08F220/18C08F220/1808C08F220/1804C09J2301/122C09J2301/302C08F218/08C08F220/281C08F212/08C08F220/06
Inventor 李卫东曹英杰白永平李晶波李小静卫晓波岳利培殷晓芬席丹
Owner 余姚市维特胶粘制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products