A kind of interface agent and two-component technology, which is applied in the engineering field, can solve the problems of the interface agent's toxicity to humans and the environment, low bonding strength of new and old concrete, and poor corrosion resistance, so as to achieve good durability and stable and reliable quality , good construction performance

Inactive Publication Date: 2017-03-29
GANSU CHANGLONG HIGHWAY MAINTENANCE TECH RES INST CO LTD
View PDF8 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the interface agents used in my country's engineering mainly include cement paste, expanded cement paste, epoxy glue, fly ash modified cement mortar, etc., but the bonding strength of new and old concrete repaired or reinforced by using this type of interface agent is low, Poor corrosion resistance, poor durability, some interface agents are toxic to humans and the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Emulsion type two-component interface agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1 Emulsion type two-component interface agent, this interface agent is made up of A component and B component; Wherein

[0024] Component A is calculated by weight percentage (kg / kg), consisting of 46.8% rapid hardening cement, 5.9% ordinary cement, 41.0% quartz sand, 5.8% active mineral admixture, 0.3% water reducer, 0.1 % boric acid, 0.01% hydroxypropyl methylcellulose, 0.09% analytically pure lithium carbonate;

[0025] Component B is composed of 40.5% latex, 1.1% BASF water-based defoamer, and 58.4% water by weight percentage (kg / kg).

[0026] The method of using the emulsion type two-component interface agent refers to:

[0027] Firstly, the construction base is treated. According to the different construction area and environmental conditions of the concrete base surface, the concrete base surface can be roughened by sand blasting, high-pressure water flushing, angle grinder grinding and chiseling; Foreign matter such as milk skin, loose particles, a...

Embodiment 2

[0029] Embodiment 2 Emulsion type two-component interface agent, this interface agent is made up of A component and B component; Wherein

[0030] Component A is calculated by weight percentage (kg / kg), consisting of 49.7% rapid hardening cement, 6.3% ordinary cement, 37.3% quartz sand, 6.2% active mineral admixture, 0.2% water reducer, 0.2 % boric acid, 0.01% hydroxypropyl methylcellulose, 0.09% analytically pure lithium carbonate;

[0031] Component B is composed of 36.1% latex, 1.1% BASF water-based defoamer, and 62.8% water in terms of weight percentage (kg / kg).

[0032] The method of using the emulsion type two-component interface agent refers to:

[0033] Firstly, the construction base is treated. According to the different construction area and environmental conditions of the concrete base surface, the concrete base surface can be roughened by sand blasting, high-pressure water flushing, angle grinder grinding and chiseling; Foreign matter such as milk skin, loose par...

Embodiment 3

[0035] Embodiment 3 Emulsion type two-component interface agent, this interface agent is made up of A component and B component; Wherein

[0036] Component A is calculated by weight percentage (kg / kg), consisting of 55.8% rapid hardening cement, 37.3% quartz sand, 6.2% active mineral admixture, 0.4% water reducer, 0.2% boric acid, 0.01% Hydroxypropyl methylcellulose and 0.09% analytically pure lithium carbonate are mixed;

[0037] Component B is composed of 33.3% latex, 1.2% BASF water-based defoamer, and 65.5% water by weight percentage (kg / kg).

[0038] The method of using the emulsion type two-component interface agent refers to:

[0039] Firstly, the construction base is treated. According to the different construction area and environmental conditions of the concrete base surface, the concrete base surface can be roughened by sand blasting, high-pressure water flushing, angle grinder grinding and chiseling; Foreign matter such as milk skin, loose particles, and exposed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to an emulsion type two-component interface agent, which is formed by a component A and a component B. The component A is prepared from mixing the following components in percentage by weight: 46.0 to 55.9 percent of rapid hardening cement, 0 to 6.3 percent of ordinary cement, 37.2 to 47.0 percent of quartz sand, 5.8 to 6.2 percent of active mineral admixture, 0.2 to 0.4 percent of water reducing agent, 0.1 to 0.2 percent of boric acid, 0.01 percent of hydroxypropyl methyl cellulose, and 0.09 percent of analytically pure lithium carbonate; and the component B is prepared from mixing the following components in percentage by weight: 33.3 to 40.5 percent of latex, 1.1 to 1.2 percent of Basf water-based defoaming agent, and 58.4 to 65.5 percent of water. The emulsion type two-component interface agent provided by the invention has higher early strength, high bonding strength, good durability, and capability of enhancing concrete surface performances or endowing a concrete surface with required functions.

Description

technical field [0001] The invention relates to the technical field of engineering, in particular to an emulsion type two-component interface agent. Background technique [0002] Due to the development of the economy, large-scale construction of traffic infrastructure such as roads and bridges is bound to be carried out; after the completion of the roads and bridges, in the later period of continuous use, due to natural or man-made factors, various road structures will inevitably appear. problem, which requires repairs to the road surface. In the process of repairing, the bonding strength of old and new concrete is the key to the quality of the repaired and reconstructed concrete. [0003] At present, the interface agents used in my country's engineering mainly include cement paste, expanded cement paste, epoxy glue, fly ash modified cement mortar, etc., but the bonding strength of new and old concrete repaired or reinforced by using this type of interface agent is low, Poo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2111/00482C04B7/00C04B14/06C04B18/08C04B18/146C04B22/0013C04B24/383C04B22/10C04B24/24C04B2103/302C04B2103/50
Inventor 李刊丁民张国宏魏定邦赵静卓王晖曹青霞
Owner GANSU CHANGLONG HIGHWAY MAINTENANCE TECH RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap