High-performance nitrile rubber sealing material and preparation method thereof

A high-performance nitrile and rubber sealing technology, applied in the field of rubber materials, can solve the problems of poor wear resistance, single temperature resistance, low tensile strength and tear strength of nitrile rubber, and achieve the effect of excellent high temperature oil resistance

Active Publication Date: 2017-03-29
南阳天一密封股份有限公司
View PDF6 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the purpose of the present invention is to provide a kind of high-performance nitrile rubber sealing material for the deficiencies in the prior art, which solves the poor wear resistance of common nitrile rubber, and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance nitrile rubber sealing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A high-performance nitrile rubber sealing material, comprising the following raw materials in parts by weight: 25 parts by weight of nitrile rubber, 7 parts of compound vulcanizing agent, 4 parts of antioxidant, 15 parts of activator, 25 parts of reinforcing agent and heat-resistant additives 5 servings.

[0036] Among them, the nitrile rubber is a mixture of nitrile rubber-40, nitrile rubber-26 and nitrile rubber-18 at a weight ratio of 5:2:1.

[0037] The compound vulcanizing agent includes a vulcanizing agent and a crosslinking aid;

[0038] The vulcanizing agent is a mixture of sulfur and dicumyl peroxide in a weight ratio of 1.5:1,

[0039] The cross-linking assistant is a mixture of tetramethylthiuram disulfide, dibenzothiazole disulfide and N-tert-butyl-2-benzothiazole sulfenamide in a weight ratio of 1:1:1.

[0040] The anti-aging agent is made by mixing anti-aging agent RD, anti-aging agent 4010NA and anti-aging agent 445 in a weight ratio of 1:1:1.

[0041] Among them, ...

Embodiment 2

[0050] A high-performance nitrile rubber sealing material, comprising the following raw materials in parts by weight: 26 parts by weight of nitrile rubber, 6 parts of compound vulcanizing agent, 4.2 parts of antioxidant, 14 parts of activator, 26 parts of reinforcing agent and heat-resistant additives 4 parts.

[0051] Among them, the nitrile rubber is a mixture of nitrile rubber-40, nitrile rubber-26 and nitrile rubber-18 at a weight ratio of 7:2:1.

[0052] The compound vulcanizing agent includes a vulcanizing agent and a crosslinking aid;

[0053] The vulcanizing agent is a mixture of sulfur and dicumyl peroxide in a weight ratio of 2:1,

[0054] The cross-linking assistant is a mixture of tetramethylthiuram disulfide, dibenzothiazole disulfide and N-tert-butyl-2-benzothiazole sulfenamide in a weight ratio of 2:1:2.

[0055] The anti-aging agent is made by mixing anti-aging agent RD, anti-aging agent 4010NA and anti-aging agent 445 at a weight ratio of 1.5:1.

[0056] Among them, the...

Embodiment 3

[0065] A high-performance nitrile rubber sealing material, including the following parts by weight of raw materials: 28 parts by weight of nitrile rubber, 5 parts of compound vulcanizing agent, 4.4 parts of antioxidant, 13 parts of activator, 27 parts of reinforcing agent and heat-resistant additives 3 copies.

[0066] Among them, the nitrile rubber is a mixture of nitrile rubber-40, nitrile rubber-26 and nitrile rubber-18 at a weight ratio of 5:4:1.

[0067] The compound vulcanizing agent includes a vulcanizing agent and a crosslinking aid;

[0068] The vulcanizing agent is a mixture of sulfur and dicumyl peroxide in a weight ratio of 1:1,

[0069] The crosslinking aid is a mixture of tetramethylthiuram disulfide, dibenzothiazole disulfide and N-tert-butyl-2-benzothiazole sulfenamide in a weight ratio of 3:3:1.

[0070] The anti-aging agent is made by mixing anti-aging agent RD, anti-aging agent 4010NA and anti-aging agent 445 in a weight ratio of 1.5:0.5:1.

[0071] Among them, the ac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tear strengthaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-performance nitrile rubber sealing material and a preparation method thereof. The high-performance nitrile rubber sealing material is prepared from the following raw materials in parts by weight: 25 to 35 parts of nitrile rubber, 4 to 7 parts of composite sulfurizing reagent, 4 to 5 parts of anti-aging agent, 8 to 15 parts of activating agent, 25 to 30 parts of reinforcing agent and 2 to 5 parts of heat-resistant additive. By adopting the high-performance nitrile rubber sealing material, the problems of poor wear resistance, low tensile strength and low tearing strength in ordinary nitrile rubber are solved, and the prepared product has high mechanical performance and superior high-temperature performance.

Description

Technical field [0001] The invention relates to the technical field of rubber materials, in particular to a high-performance nitrile rubber sealing material and a preparation method thereof. Background technique [0002] Due to its excellent oil resistance, abrasion resistance, low compression set and good processing performance, nitrile rubber has a good cost performance compared with other special rubbers such as fluorine rubber, acrylic rubber, hydrogenated nitrile rubber, etc. Therefore, it has been widely used in the production of oil-resistant products, accounting for about 50% of the glue used in the production of oil-resistant seals. However, with the development of modern technology, the operating speed of various mechanical equipment and vehicles is getting higher and higher, and the working environment temperature and working conditions of the seals are becoming more and more demanding. In order to reduce the use of expensive high-temperature and oil-resistant special ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/02C08K13/06C08K3/06C08K5/14C08K3/04C08K3/36C08K3/34C08K3/22B29B7/00B29C35/02
CPCB29B7/002B29C35/02C08K2201/014C08L9/02C08L2201/08C08L2205/025C08L2205/035C08K13/06C08K3/06C08K5/14C08K3/04C08K3/36C08K3/346C08K2003/222
Inventor 樊红星赵红祥刘元英杨松涛陈宇翔朱建周张冰潭
Owner 南阳天一密封股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap