Polyvinylidene fluoride lyophobic separation membrane and preparation method thereof

A polyvinylidene fluoride, hydrophobic separation membrane technology, applied in semi-permeable membrane separation, chemical instruments and methods, membranes, etc., can solve the problem of polyvinylidene fluoride hydrophilic microporous membrane not resistant to pollution and other problems

Inactive Publication Date: 2017-04-26
廖正康
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims to solve the problem that the polyvinylidene fluoride hydrophilic microporous membrane is not resistant to pollution in the prior art, and provides a polyvinylidene fluoride hydrophobic separation membrane, which is hydrophobic and anti-pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A polyvinylidene fluoride hydrophobic separation membrane, comprising the following raw materials in parts by weight:

[0028] 15 parts polyvinylidene fluoride

[0029] 75 parts of N,N-dimethylformamide

[0030] 3 parts n-butanol

[0031] 3 parts butyl acetate

[0032] 3 parts tributyl phosphate

[0033] Polyethylene glycol PEG-1000 5 parts

[0034] Anhydrous Lithium Chloride 3 parts

[0035] Sodium chloride 3 parts

[0036] 300 parts of deionized water

[0037] Alcohol 5 parts

[0038] 5 parts isopropyl alcohol

[0039] 2 parts of hydrophobic coating solution.

Embodiment 2

[0041] A polyvinylidene fluoride hydrophobic separation membrane, comprising the following raw materials in parts by weight:

[0042] 20 parts polyvinylidene fluoride

[0043] 85 parts of N,N-dimethylformamide

[0044] 5 parts n-butanol

[0045] Butyl acetate 5 parts

[0046] Tributyl Phosphate 5 parts

[0047] Polyethylene glycol PEG-1000 10 parts

[0048] Anhydrous Lithium Chloride 5 parts

[0049] Sodium chloride 5 parts

[0050] 500 parts of deionized water

[0051] Alcohol 10 parts

[0052] 10 parts isopropyl alcohol

[0053] 5 parts of hydrophobic coating solution.

Embodiment 3

[0055] A polyvinylidene fluoride hydrophobic separation membrane, comprising the following raw materials in parts by weight:

[0056] 17 parts polyvinylidene fluoride

[0057] 80 parts of N,N-dimethylformamide

[0058] 4 parts n-butanol

[0059] 4 parts butyl acetate

[0060] 4 parts tributyl phosphate

[0061] Polyethylene glycol PEG-1000 7 parts

[0062] Anhydrous Lithium Chloride 4 parts

[0063] Sodium chloride 4 parts

[0064] 400 parts of deionized water

[0065] Alcohol 7 parts

[0066] 7 parts isopropyl alcohol

[0067] 3 parts of hydrophobic coating solution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a polyvinylidene fluoride lyophobic separation membrane and a preparation method thereof, and belongs to the technical field of lyophobic separation membranes. The polyvinylidene fluoride lyophobic separation membrane comprises the following raw materials in parts by weight: 15-20 parts of polyvinylidene fluoride, 75-85 parts of N,N-dimethyl formamide, 3-5 parts of n-butyl alcohol, 3-5 parts of butyl acetate, 3-5 parts of tributyl phosphate, 5-10 parts of polyethylene glycol PEG-1000, 3-5 parts of anhydrous lithium chloride, 3-5 parts of sodium chloride, 300-500 parts of deionized water, 5-10 parts of alcohol, 5-10 parts of isopropyl alcohol and 2-5 parts of a lyophobic coating. The polyvinylidene fluoride lyophobic separation membrane provided by the invention has hydrophobicity and is capable of preventing contamination.

Description

technical field [0001] The invention relates to a separation membrane and a preparation method thereof. More specifically, the invention relates to a polyvinylidene fluoride hydrophobic separation membrane and a preparation method thereof, belonging to the technical field of hydrophobic separation membranes. Background technique [0002] In recent decades, polymer membranes have been widely used in various gas and liquid separation fields, such as microfiltration, ultrafiltration, reverse osmosis and nanofiltration, and polyvinylidene fluoride (PVDF) membranes have become the most widely used membranes due to their excellent comprehensive performance. One of the wide range of polymer membranes. Polyvinylidene fluoride (PVDF) has good thermal stability, chemical stability and mechanical strength. The main preparation method of polyvinylidene fluoride (PVDF) membrane is the phase inversion method. During the preparation process of phase inversion, the structure and propertie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D67/00B01D69/02B01D71/34
CPCB01D71/34B01D67/0011B01D69/02B01D2325/38
Inventor 廖正康
Owner 廖正康
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com