High Gloss Sublimation Transfer Paper

A high-gloss, sublimation technology, applied in printing, temperature recording method, copy/marking method, etc., can solve the problems of dull pattern, not vivid and vivid, affecting the overall product visual effect, etc., and achieve the gloss of the coating. Good results

Active Publication Date: 2018-10-16
苏州万敦新材料有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Dye-sublimation transfer paper is widely used in the dye-sublimation product industry, and its gloss will affect the vision of the pattern, thereby affecting the visual effect of the overall product. Without gloss, the pattern is dull and not vivid enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A high-gloss thermal sublimation transfer paper, including a paper base layer and a coating on it, is composed of the following components by weight: 23.5 parts of carboxymethyl cellulose, 1.5 parts of sucrose, 0.23 parts of ethylene glycol ether, poly 6.5 parts of citric acid, 2.5 parts of hyaluronic acid, 4.2 parts of dibutyl phthalate, 5.5 parts of morpholine, 1.15 parts of microcrystalline wax Jonwax26 emulsion, 2.3 parts of phthalocyanine blue, 2.5 parts of benzidine yellow, aminated resin liquid 3.6 parts, 4.25 parts of propylene glycol methyl ether, 3.3 parts of titanium dioxide, 4.5 parts of trisodium phosphate, and 2.5 parts of sodium alginate.

[0015] The present invention also discloses a method for preparing the above-mentioned high-gloss thermal sublimation transfer paper, which includes the following steps:

[0016] 1) Put carboxymethyl cellulose, sucrose, and ethylene glycol ether into a dissolution kettle, heat to 50-60 degrees Celsius and reflux for 2 ...

Embodiment 2

[0023] A high-gloss thermal sublimation transfer paper, comprising a paper base layer and a coating thereon, wherein the coating consists of the following components by weight: 30 parts of carboxymethyl cellulose, 2 parts of sucrose, ethylene glycol 0.5 parts of ether, 7 parts of polycitric acid, 3 parts of hyaluronic acid, 5 parts of dibutyl phthalate, 6 parts of morpholine, 4 parts of microcrystalline wax Jonwax26 emulsion, 3 parts of phthalocyanine blue, 4 parts of benzidine yellow , 5 parts of aminated resin liquid, 5 parts of propylene glycol methyl ether, 6 parts of titanium dioxide, 5 parts of trisodium phosphate, and 3.3 parts of sodium alginate.

[0024] The present invention also discloses a method for preparing the above-mentioned high-gloss thermal sublimation transfer paper, which includes the following steps:

[0025] 1) Put carboxymethyl cellulose, sucrose, and ethylene glycol ether into a dissolution kettle, heat to 50-60 degrees Celsius and reflux for 2 hours,...

Embodiment 3

[0032] A high-gloss thermal sublimation transfer paper, including a paper base layer and a coating thereon, consists of the following components by weight: 34.5 parts of carboxymethyl cellulose, 2.5 parts of sucrose, 0.6 parts of ethylene glycol ether, poly 6.5-7.8 parts of citric acid, 3.6 parts of hyaluronic acid, 5.5 parts of dibutyl phthalate, 7.8 parts of morpholine, 4.6 parts of microcrystalline wax Jonwax26 emulsion, 3.5 parts of phthalocyanine blue, 4.5 parts of benzidine yellow, amination 6.5 parts of resin liquid, 6.6 parts of propylene glycol methyl ether, 6.5 parts of titanium dioxide, 6.5 parts of trisodium phosphate, and 3.6 parts of sodium alginate.

[0033] The invention also discloses a method for preparing high-gloss thermal sublimation transfer paper, which includes the following steps:

[0034] 1) Put carboxymethyl cellulose, sucrose, and ethylene glycol ether into a dissolution kettle, heat to 50-60 degrees Celsius and reflux for 2 hours, stir evenly, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-glossiness heat sublimation transfer paper. The high-glossiness heat sublimation transfer paper comprises a paper base layer and a coating on the paper base layer, wherein the coating comprises the following components by weight: 23.5-34.5 parts of carboxymethyl cellulose, 1.5-2.5 parts of saccharose, 0.23-0.6 part of glycol ether, 6.5-7.8 parts of poly citric acid, 2.5-3.6 parts of hyaluronic acid, 4.2-5.5 parts of dibutyl phthalate, 5.5-7.8 parts of morpholine, 1.15-4.6 parts of a microcrystalline wax Jonwax26 emulsion, 2.3-3.5 parts of phthalocyanine blue, 2.5-4.5 parts of benzidine yellow, 3.6-6.5 parts of aminated resin liquid, 4.25-6.6 parts of propylene glycol monomethyl ether, 3.3-6.5 parts of titanium dioxide, 4.5-6.5 parts of trisodium phosphate anhydrous and 2.5-3.6 parts of sodium alginate. According to the high-glossiness heat sublimation transfer paper, owing to the preparation method and all components of the surface coating, the formed coating is good in glossiness, and the prepared end product is bright in pattern and longer in retention time.

Description

technical field [0001] The invention relates to the technical field of thermal transfer printing, in particular to a high-gloss thermal sublimation transfer paper. Background technique [0002] Dye-sublimation transfer paper is widely used in the dye-sublimation product industry, and its gloss will affect the vision of the pattern, thereby affecting the visual effect of the overall product. Without gloss, the pattern is dull and not vivid enough. Contents of the invention [0003] Purpose of the invention: The purpose of the invention is to provide a high-gloss sublimation transfer paper in order to make up for the deficiencies in the existing research technology. [0004] Technical solution: A high-gloss thermal sublimation transfer paper, including a paper base layer and a coating on it, the coating is composed of the following components by weight: 23.5-34.5 parts of carboxymethyl cellulose, 1.5 parts of sucrose -2.5 parts, 0.23-0.6 parts of ethylene glycol ether, 6.5-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B41M5/44B41M5/42
CPCB41M5/423B41M5/426B41M5/44
Inventor 戚裕
Owner 苏州万敦新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com