Thermoplastic elastomer door seal easy to weld and preparation method thereof

A thermoplastic elastic, easy-to-weld technology, applied in the field of door sealing materials, can solve the problems of not exerting TPE door seals, affecting the transportation and use of door seals, and poor welding tension, achieving good clearance, good elasticity, and reducing electrical energy consumption. Effect

Active Publication Date: 2017-04-26
QINGDAO NEW MATERIAL TECH IND PARK DEV
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The patent clearly stated that the welding tension of general TPE materials is poor, which affects the transportation and use of door seals, and the raw materials used to improve welding performance are mainly POE plastics and PP elastomers
Since the SEBS elastomer used in this patent is less, but mainly a large amount of POE plastic and PP elastomer, the door seal has poor elasticity and strong plasticity, and the door seal is not easy to recover after deformation, and the advantages of TPE door seal are not fully utilized

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The easy-to-weld thermoplastic elastomer door seal of the present embodiment comprises the following components in parts by weight: 40 parts of SEBS elastomer (YH-507), 15 parts of tackifying resin (carbon five hydrogenated resin), filler (calcium carbonate ) 15 parts, processing oil (kinematic viscosity at 40°C is 100mm 2 ·s -1 paraffin oil) 15 parts, polypropylene 15 parts, lubricant (erucamide) 1 part, pigment 1 part, antibacterial and antifungal agent (zirconium phosphate silver loaded) 0.5 part, antioxidant (antioxidant 1010) 0.3 part , 0.3 parts of ultraviolet absorber (UV-326).

[0031] The preparation method of the easy-to-weld thermoplastic elastomer door seal of the present embodiment comprises the following steps:

[0032] Add 40 parts of SEBS elastomer (YH-507) and 15 parts of paraffin oil into the low-speed mixer, stir and mix for 30 minutes, let the paraffin oil be fully absorbed by YH-507, and park for more than 6 hours for later use.

[0033] Weigh th...

Embodiment 2

[0038] The easy-to-weld thermoplastic elastomer door seal of the present embodiment comprises the following components in parts by weight: 55 parts of SEBS elastomer (YH-507), 10 parts of tackifying resin (pentaerythritol modified rosin resin), filler (talcum powder ) 15 parts, processing oil (kinematic viscosity at 40°C is 200mm 2 ·s -1 5 parts of paraffin oil), 15 parts of polypropylene, 1 part of lubricant (silicone masterbatch), 1 part of pigment, 0.5 part of antibacterial and antifungal agent (chitin), 0.1 part of antioxidant (antioxidant 1098), Ultraviolet absorber (UV-329) 0.1 part.

[0039] The easy-to-weld thermoplastic elastomer door seal of this embodiment comprises the following steps:

[0040] Add 55 parts of S EBS elastomer (YH-507) and 5 parts of paraffin oil into the low-speed mixer, stir and mix for 20 minutes, let the paraffin oil be fully absorbed by YH-507, and park for more than 6 hours for later use.

[0041] Weigh fully oil-absorbed YH-507 and pentaer...

Embodiment 3

[0046] The easy-to-weld thermoplastic elastomer door seal of the present embodiment comprises the following components in parts by weight: 50 parts of SEBS elastomer (YH-507), 15 parts of tackifying resin (pentaerythritol modified rosin resin), filler (talcum powder ) 15 parts, processing oil (kinematic viscosity at 40°C is 100mm 2 ·s -1 10 parts of paraffin oil), 10 parts of polypropylene, 2 parts of lubricant (silicone masterbatch), 1 part of pigment, 0.5 part of antibacterial and antifungal agent (silver zirconium phosphate), antioxidant (antioxidant 1010 and anti-oxidant Oxygen agent 168) 0.5 part, ultraviolet absorber (UV-329 and UV-770) 0.5 part.

[0047] The easy-to-weld thermoplastic elastomer door seal of this embodiment comprises the following steps:

[0048] Add 50 parts of SEBS elastomer (YH-507) and 10 parts of paraffin oil into the low-speed mixer, stir and mix for 20 minutes, let the paraffin oil be fully absorbed by YH-507, and park for more than 6 hours for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
brittleness temperatureaaaaaaaaaa
service temperatureaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a thermoplastic elastomer door seal easy to weld. The door seal is prepared from, by weight, 40-55 parts of SEBS elastomers, 5-15 parts of tackifying resin, 10-15 parts of filler, 5-15 parts of processing oil, 10-15 parts of polypropylene, 1-2 parts of lubricating agent, 0.1-1 part of pigment, 0.1-0.5 part of antibacterial and antifungal agent, 0.1-0.5 part of antioxidant and 0.1-0.5 part of ultraviolet light absorber. The invention further provides a preparation method of the thermoplastic elastomer door seal. The thermoplastic elastomer door seal easy to weld is high in welding strength and good in rebound elasticity, still keeps the good elasticity in the low-temperature application environment such as refrigerators and other refrigeration appliances, prevents a flash seam from being produced, can better close the gap between a door body and a box body, reduces electric appliance energy consumption and makes a contribution to further energy conservation of the refrigeration appliances.

Description

technical field [0001] The invention belongs to the technical field of door seal materials, and in particular relates to an easily weldable thermoplastic elastomer (TPE) door seal for refrigerators, freezers, wine cabinets and other refrigeration appliances and a preparation method thereof. Background technique [0002] At the end of September 2015, the National Standardization Management Committee issued a new version of the refrigerator energy efficiency standard GB 12021.2-2015 "Limited Values ​​of Electricity Consumption and Energy Efficiency Levels of Household Refrigerators" (hereinafter referred to as the new standard), which is used to replace GB 12021.2-2008 and was released in 2016. It was officially implemented on October 1, 2019. The new standard stipulates that the power consumption of energy efficiency level 1 products is about 40% lower than that of the original energy efficiency level 1 products. However, the proportion of refrigerators with energy efficienc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02C08L57/02C08L91/06C08L93/04
CPCC08L53/025C08L2205/035C08L2207/04C08L57/02C08L91/06C08L93/04
Inventor 杨有财梁坤栗磊高雷岳超纲李荣勋
Owner QINGDAO NEW MATERIAL TECH IND PARK DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com