Anti-aging foaming material and preparation method thereof

A foaming material and anti-aging technology, which is applied in the field of aging-resistant foaming materials and its preparation, can solve the problems of aging resistance and poor compression resistance, and achieve the effects of improving water resistance, aging resistance and strength

Inactive Publication Date: 2017-05-17
ANHUI SOYA DECORATIVE MATERIALS
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For most thermoplastic or thermosetting plastics, they can be processed into foamed materials, but there are disadvantages such as poor compression resistance and aging resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] An aging-resistant foaming material, made of the following components by weight: 90 parts of high-melt strength polypropylene, 8 parts of dry paint, 12 parts of chrysanthemum stone, 6 parts of mastic gum, 1 part of manganese borate, trichloride 5 parts of ethylsilane, 2 parts of diallyl phthalate, 3 parts of azodicarbonamide, 1 part of N-phenyl-α-aniline, and 0.5 parts of ethylenethiourea.

[0017] Preferably, the above-mentioned high melt strength polypropylene has a melting point of 170°C and a melt index of 3.18g×10min -1 .

[0018] Preferably, the above dry paint contains 75% urushiol and a density of 1.15g / m 3 , with an average particle size of 100 μm.

[0019] Preferably, the density of above-mentioned chrysoprase is 2.3g / m 3 , with an average particle size of 80 μm.

[0020] Specifically, a method for preparing an aging-resistant foaming material comprises the following steps:

[0021] (1) Put high-melt-strength polypropylene, dry paint, chrysoprase, mastic ...

Embodiment 2

[0024] An aging-resistant foaming material, made of the following components by weight: 95 parts of high-melt strength polypropylene, 9 parts of dry paint, 16 parts of chrysanthemum stone, 7 parts of mastic gum, 2 parts of manganese borate, trichloride 6 parts of ethylsilane, 3 parts of diallyl phthalate, 5 parts of azodicarbonamide, 2 parts of N-phenyl-α-aniline, and 0.6 parts of ethylenethiourea.

[0025] Preferably, the above-mentioned high melt strength polypropylene has a melting point of 170°C and a melt index of 3.18g×10min -1 .

[0026] Preferably, the above dry paint contains 75% urushiol and a density of 1.15g / m 3 , with an average particle size of 110 μm.

[0027] Preferably, the density of above-mentioned chrysoprase is 2.4g / m 3 , with an average particle size of 90 μm.

[0028] Specifically, a method for preparing an aging-resistant foaming material comprises the following steps:

[0029] (1) Put high-melt-strength polypropylene, dry paint, chrysoprase, masti...

Embodiment 3

[0032] An aging-resistant foaming material, made of the following components in parts by weight: 100 parts of high-melt strength polypropylene, 10 parts of dry paint, 18 parts of golden stone, 8 parts of mastic gum, 3 parts of manganese borate, trichloride 7 parts of ethylsilane, 4 parts of diallyl phthalate, 8 parts of azodicarbonamide, 3 parts of N-phenyl-α-aniline, and 0.7 parts of ethylenethiourea.

[0033] Preferably, the above-mentioned high melt strength polypropylene has a melting point of 170°C and a melt index of 3.18g×10min -1 .

[0034] Preferably, the above dry paint contains 75% urushiol and a density of 1.15g / m 3 , with an average particle size of 120 μm.

[0035] Preferably, the density of above-mentioned chrysoprase is 2.5g / m 3 , with an average particle size of 100 μm.

[0036] Specifically, a method for preparing an aging-resistant foaming material comprises the following steps:

[0037] (1) Put high-melt-strength polypropylene, dry paint, chrysoprase, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-aging foaming material and a preparation method thereof. The anti-aging foaming material is prepared from the following components in parts by weight: 90-100 parts of high-melt-strength polypropylene, 8-10 parts of dried lacquer, 12-18 parts of vermiculite schist seu, 6-8 parts of manganese borate, 5-7 parts of ethyltrichlorosilane, 2-4 parts of diallyl phthalate, 3-8 parts of azodicarbonamide, 1-3 parts of N-phenyl-alpha-aniline and 0.5-0.7 part of ethylene thiourea. The foaming material has excellent mechanical performance, excellent aging resistance, excellent thermal and sound insulation performance, relatively good cell shape and uniform cell distribution, and the material quality is greatly improved.

Description

technical field [0001] The invention belongs to the field of foam material production, and in particular relates to an aging-resistant foam material and a preparation method thereof. Background technique [0002] Polymer foaming material refers to a type of material that uses polymer as the matrix but is filled with tiny pores inside. Its preparation method is generally by adding a foaming agent (physical foaming agent, chemical foaming agent or compound foaming agent) to the plastic. Foaming agent), while adding some processing aids, through intermittent foaming, extrusion foaming, injection foaming and other processes to process and shape. Because there are a large number of gas micropores distributed in the plastic matrix, the polymer foam material has excellent properties such as low density, sound absorption, shock absorption, and heat preservation, and can save costs and resources. Since the advent of polymer foaming materials in the early 20th century, its types have...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L93/00C08K13/02C08K3/34C08K3/38C08K5/12C08K5/18C08K5/5419C08J9/10
CPCC08L23/12C08J9/103C08J2203/04C08J2323/12C08J2493/00C08K2201/003C08L2201/08C08L2203/14C08L93/00C08K13/02C08K3/34C08K2003/387C08K5/12C08K5/18C08K5/5419
Inventor 李华令刘华平
Owner ANHUI SOYA DECORATIVE MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap