Novel anti-slipping floor tiles and preparation method of novel anti-slipping floor tiles

An anti-skid and floor tile technology, applied in the field of building materials, can solve the problems of unsatisfactory anti-skid performance, reduced anti-skid performance, etc., to achieve good uniform dispersion and hydrophilicity, improve hardness, and improve the effect of adhesion

Inactive Publication Date: 2017-05-31
GUIZHOU XINGGUI HENGYUAN NOVEL BUILDING MATERIAL CO LTD
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In North America, there are about 27,000 personal accidental injuries caused by slippery roads and falls every day, and more than 50% of the cases occur in public places. At present, the research and development of the anti-skid performance of floor tiles is a hot research topic of various manufacturers. For example, the application The patent No. 201310400173.8 discloses "A Non-slip Floor Tile", which discloses that its raw material components are: fly ash, coal gangue, broken glass fiber, white mud, mung bean rock; and further discloses its mass percentage: fly ash 1-10 parts, 25-40 parts of coal gangue, 1-5 parts of broken glass fiber, 2-8 parts of white mud, 50-60 parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel anti-slipping floor tiles and preparation method of novel anti-slipping floor tiles

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1

[0021] A novel anti-skid floor tile and a preparation method thereof, comprising the following raw materials by weight: 20kg of granite, 12kg of marble, 25kg of clay, 20kg of cement, 10kg of coal gangue, 8kg of expanded perlite, 12kg of modified bentonite, 6kg of agent, 8kg of thickener, 18kg of anti-slip agent, and some water.

[0022] The cement used is fly ash Portland cement.

[0023] For the bentonite, first wash the bentonite sample with water until the washed water becomes clear, then soak the bentonite with 1.2 mol / L hydrochloric acid for 2 hours, remove the bentonite, add water to soak the bentonite, and the water can exceed the surface of the bentonite by 3cm. 15% sodium fluorosilicate by mass of bentonite, stirred for 1.5h in a constant temperature water bath at 65°C, filtered, and calcined the filter cake at 300°C for 35min under nitrogen protection, and then cooled.

[0024] The thickener, hydroxyethyl cellulose, polyvinyl alcohol and sodium a...

Example Embodiment

[0031] Example 2

[0032] A novel anti-skid floor tile and a preparation method thereof, comprising the following raw materials by weight: 30kg of granite, 18kg of marble, 35kg of clay, 40kg of cement, 20kg of coal gangue, 12kg of expanded perlite, 18kg of modified bentonite, 9kg of agent, 14kg of thickener, 22kg of anti-slip agent, and some water.

[0033] The cement used is fly ash Portland cement.

[0034] For the bentonite, first wash the bentonite sample with water until the washed water becomes clear, then soak the bentonite with 1.2-1.6mol / L hydrochloric acid for 3 hours, remove the bentonite, add water to soak the bentonite, and the water can exceed the surface of the bentonite by 5cm. , add 20% sodium fluorosilicate by mass of bentonite, stir in a constant temperature water bath at 65°C for 1.8h, filter, under nitrogen protection, calcine the filter cake at 310°C for 45min, and then cool.

[0035] For the thickener, hydroxyethyl cellulose, polyvinyl alcohol and sodi...

Example Embodiment

[0042] Example 3

[0043]A novel anti-skid floor tile and a preparation method thereof, comprising the following raw materials by weight: 25kg of granite, 15kg of marble, 30kg of clay, 30kg of cement, 15kg of coal gangue, 10kg of expanded perlite, 15kg of modified bentonite, 8kg of agent, 12kg of thickener, 20kg of anti-slip agent, and some water.

[0044] The cement used is fly ash Portland cement.

[0045] For the bentonite, first wash the bentonite sample with water until the washed water becomes clear, then soak the bentonite with 1.5mol / L hydrochloric acid for 2.5h, remove the bentonite, add water to soak the bentonite, and the water can exceed the surface of the bentonite by 4m. Add 18% sodium fluorosilicate by mass of bentonite, stir in a constant temperature water bath at 65°C for 1.7h, filter, and under nitrogen protection, the filter cake is calcined at 305°C for 40min, and then cooled.

[0046] The thickener, hydroxyethyl cellulose, polyvinyl alcohol and sodium al...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of building materials and in particular relates to novel anti-slipping floor tiles and a preparation method of the novel anti-slipping floor tiles. The novel anti-slipping floor tiles are prepared from the following raw materials in parts by weight: 20 to 30 parts of granite, 12 to 18 parts of marble, 25 to 35 parts of clay, 20 to 40 parts of cement, 10 to 20 parts of coal gangue, 8 to 12 parts of expanded perlite, 12 to 18 parts of expanded bentonite, 6 to 9 parts of a water reducing agent, 8 to 14 parts of a thickener, 18 to 22 parts of an anti-slipping agent and a number of water. The floor tiles provided by the invention are firm and durable, have no toxin or harms, are natural and environmentally friendly, and also have an anti-cracking effect; the floor tiles are not easy to damage, the product quality is stable and the production cost is greatly reduced; under the condition of guaranteeing great demanding on the floor tiles by a building industry, the prepared floor tiles have a relatively high anti-slipping property and the anti-slipping property is greatly improved; the safety of working places and public places is guaranteed and the occurrence rate of slipping accidents is reduced.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a novel anti-skid floor tile and a preparation method thereof. Background technique [0002] Floor tiles are a kind of ground decoration material, also called floor tiles, which are made of clay and have various specifications. They are firm in quality, pressure-resistant and wear-resistant, and moisture-proof. Some are glazed and have decorative effects. They are mostly used in public buildings. And the ground and floor of civil buildings. [0003] Slip resistance is simply defined as the ability of a material to overcome the problem of slipping and falling in a special environment. It is characterized by many influencing factors, large injuries, and high probability of occurrence. It has become the number one problem of safety hazards in workplaces and public places. In my country in 2005, there were 5.065 million cases of wet slipping and falling injuries, and the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/13C04B33/132C04B35/16
CPCC04B33/13C04B33/132C04B35/16C04B2235/3463C04B2235/349Y02P40/60
Inventor 邓兴贵林波蔡安谷
Owner GUIZHOU XINGGUI HENGYUAN NOVEL BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products