Fiberglass reinforced plastic raw material for manufacturing oil separation tank

A glass fiber reinforced plastic and oil separator technology, which is applied in the field of composite materials, can solve the problems of destroying molecular structure, reducing material strength, cutting glass fibers, etc., and achieves the effects of good stain resistance, improved corrosion resistance, and reduced stress concentration.

Active Publication Date: 2017-05-31
安徽星元环保科技有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the grease trap made of glass fiber reinforced plastics shows good performance characteristics, because the matrix resin is a polymer material, it is easy to age after long-term use, especially under the action of active media, the resin macromol

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example 1

[0024] A glass fiber reinforced plastic material used to make grease traps, made of the following parts by weight:

[0025] 45 parts of unsaturated polyester resin, 8 parts of epoxy resin, 6 parts of phenolic resin, 38 parts of composite fiber filler, 2 parts of antioxidant, 1 part of polymerization inhibitor, 4 parts of toughening agent, 2 parts of curing agent, 1 part of accelerator The mixed modified fiber filler is made of the following parts by weight: 63 parts of glass fiber, 4 parts of kaolin, 5 parts of zeolite powder, 5 parts of graphene, 6 parts of kapok fiber.

[0026] Further, the antioxidant is composed of antioxidant 1010 and antioxidant 1076.

[0027] Further, the polymerization inhibitor is composed of hydroquinone and p-hydroxyanisole.

[0028] Further, the toughening agent is composed of dibutyl phthalate and polyvinyl butyral.

[0029] Further, the curing agent is composed of ethylenediamine, diaminodiphenylmethane, and vinyltriamine.

[0030] Furthe...

Example Embodiment

[0037] Example 2

[0038] A glass fiber reinforced plastic material used to make grease traps, made of the following parts by weight:

[0039] 48 parts unsaturated polyester resin, 9 parts epoxy resin, 8 parts phenolic resin, 40 parts composite fiber filler, 2.5 parts antioxidant, 2 parts polymerization inhibitor, 6 parts toughening agent, 3 parts curing agent, 2 parts accelerator The mixed modified fiber filler is made of the following parts by weight: 65 parts of glass fiber, 5 parts of kaolin, 7 parts of zeolite powder, 6 parts of graphene, 7 parts of kapok fiber. The rest of the method steps are the same as in Example 1.

Example Embodiment

[0040] Example 3

[0041] A glass fiber reinforced plastic material used to make grease traps, made of the following parts by weight:

[0042] 50 parts of unsaturated polyester resin, 11 parts of epoxy resin, 10 parts of phenolic resin, 42 parts of composite fiber filler, 3 parts of antioxidant, 3 parts of polymerization inhibitor, 7 parts of toughener, 4 parts of curing agent, 3 parts of accelerator The mixed modified fiber filler is made of the following parts by weight: 67 parts of glass fiber, 6 parts of kaolin, 8 parts of zeolite powder, 7 parts of graphene, 8 parts of kapok fiber. The rest of the method steps are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fiberglass reinforced plastic raw material for manufacturing an oil separation tank and belongs to the technical field of composites. The fiberglass reinforced plastic raw material is particularly prepared from the following substances: unsaturated polyester resin, epoxy resin, phenolic resin, complex fiber filling, an antioxidant, a polymerization inhibitor, a flexibilizer, a curing agent and an accelerator. Fiberglass reinforced plastic prepared from the raw material has good characteristics of corrosive resistance, impact resistance, bending resistance and pressure resistance; oily soil is not easily deposited on a surface; an antifouling characteristic is good; a service life can be prolonged to above 5 years; and the fiberglass reinforced plastic has a good popularization value.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and in particular relates to a glass fiber reinforced plastic raw material used for manufacturing grease traps. Background technique [0002] The wastewater discharged from restaurants, guesthouses, schools, corporate offices and other large catering establishments contains a large amount of oil. If it is directly discharged into urban sewage pipes, it will not only cause greater pollution, but also increase the difficulty of sewage treatment. At the same time, the oily water contains a lot of organic components, which are directly discharged into the sewage pipes, and the oily liquid adheres to the sewer pipes to form a thick greasy layer, which causes pipeline blockages, is difficult to dredge, and produces odors and breeds germs, polluting the surrounding environment. Therefore, before the catering sewage containing a large amount of oil is discharged into the urban sewage pipe, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/06C08L63/00C08L61/06C08L1/02C08L29/14C08K13/06C08K9/06C08K9/04C08K7/14C08K3/34C08K3/04C08K5/134C08K5/526C08K5/12C08K5/17C08K5/18B01D17/02
CPCB01D17/02C08L67/06C08L2205/035C08L2205/16C08L63/00C08L61/06C08L1/02C08L29/14C08K13/06C08K9/06C08K9/08C08K7/14C08K3/346C08K3/34C08K3/04C08K5/1345C08K5/526C08K5/12C08K5/17C08K5/18
Inventor 黄奋芝
Owner 安徽星元环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap