PVA (polyvinyl alcohol)-base medical antibacterial composite film

A composite film and film layer technology, applied in the field of PVA-based medical antibacterial composite film, can solve problems such as poor barrier properties, swelling of liquid pollutants, holes, etc., and achieve the effects of avoiding processes, high production efficiency, and good antibacterial properties.

Active Publication Date: 2017-06-13
常州绿之源高分子材料有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The problem to be solved by the present invention is: in order to solve the problem that when the existing PVA film material is directly used as medical protective clothing, it is easy to be swollen by liquid pollutants, and holes appear, and its barrier property is poor. A PVA-based medical antibact

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVA (polyvinyl alcohol)-base medical antibacterial composite film
  • PVA (polyvinyl alcohol)-base medical antibacterial composite film
  • PVA (polyvinyl alcohol)-base medical antibacterial composite film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A PVA-based medical antibacterial composite film, comprising: a composite PVA film layer and a PVA needle-punched non-woven fabric layer, the PVA film layer is a blown film, the PVA film layer is a PVA double-layer composite film, and the PVA film layer includes the following components: Points and parts by weight are:

[0031]

[0032] Wherein, magnesium hydroxide and chitosan sorbate mass ratio are 1:10

[0033] Wherein, the preparation method of PVA film layer comprises the steps:

[0034] (1) PVA raw material is mixed uniformly by weight percentage, carries out melting extruding granulation with twin-screw extruder, obtains polyvinyl alcohol masterbatch;

[0035] (2) Extrusion: the polyvinyl alcohol masterbatch is sent to the extruder of the blown film machine, and the extruder is a single-screw extruder, and the diameter of the single screw is 35mm, and the rotating speed is 35r / min; The extrusion process is as follows: the temperature of the first stage is 15...

Embodiment 2

[0041] A PVA-based medical antibacterial composite film, comprising: a composite PVA film layer and a PVA needle-punched non-woven fabric layer, the PVA film layer is a blown film, the PVA film layer is a PVA double-layer composite film, and the PVA film layer includes the following components: Points and parts by weight are:

[0042]

[0043] Wherein, magnesium hydroxide and chitosan sorbate mass ratio are 1:10

[0044] Wherein, the preparation method of PVA film layer comprises the steps:

[0045] (1) PVA raw material is mixed uniformly by weight percentage, carries out melting extruding granulation with twin-screw extruder, obtains polyvinyl alcohol masterbatch;

[0046] (2) Extrusion: the polyvinyl alcohol masterbatch is sent to the extruder of the blown film machine, and the extruder is a single-screw extruder, and the diameter of the single screw is 20mm, and the rotating speed is 30r / min; The extrusion process is as follows: the temperature of the first stage is 15...

Embodiment 3

[0052] A PVA-based medical antibacterial composite film, comprising: a composite PVA film layer and a PVA needle-punched non-woven fabric layer, the PVA film layer is a blown film, the PVA film layer is a PVA double-layer composite film, and the PVA film layer includes the following components: Points and parts by weight are:

[0053]

[0054] Wherein, magnesium hydroxide and chitosan sorbate mass ratio are 1:10

[0055] Wherein, the preparation method of PVA film layer comprises the steps:

[0056] (1) PVA raw material is mixed uniformly by weight percentage, carries out melting extruding granulation with twin-screw extruder, obtains polyvinyl alcohol masterbatch;

[0057] (2) Extrusion: the polyvinyl alcohol masterbatch is sent to the extruder of the blown film machine, and the extruder is a single-screw extruder, and the diameter of the single screw is 65mm, and the rotating speed is 40r / min; The extrusion process is as follows: the temperature of the first stage is 15...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of PVA (polyvinyl alcohol) composite films, particularly a PVA-base medical antibacterial composite film. The PVA-base medical antibacterial composite film comprises a PVA film layer and a PVA nonwoven fabric layer which are mutually compounded, wherein the PVA film layer is a blown film. According to the PVA-base medical antibacterial composite film, the PVA nonwoven fabric layer is compounded outside the PVA film layer; and the PVA nonwoven fabric is utilized to effectively fix the liquid pollutants by utilizing the characteristic of high porosity, thereby effectively protecting the PVA film layer from being dissolved by the liquid pollutants.

Description

technical field [0001] The invention relates to the technical field of PVA composite membranes, in particular to a PVA-based medical antibacterial composite membrane. Background technique [0002] Water-soluble environmentally friendly medical materials are new environmental protection products developed in developed countries such as Europe and the United States in recent years. The purpose is to avoid pollution and cross-infection of medical staff and patients. Through the extensive use in developed countries such as Europe and the United States in recent years, it is found that the water-soluble PVA environmental protection medical material produced by water-soluble PVA environmental protection material has ideal wear resistance and environmental protection. [0003] The emergence of PVA film can be used as work clothes or protective clothing for medical staff. When there is infection or infection on the work clothes or protective clothing, it can be treated together with...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/02B32B27/12B32B27/20B32B27/30B32B33/00B29D7/01B29C47/92B29C55/28B29C48/92
CPCB29C48/92B29C55/28B29C2948/9258B29C2948/92619B29C2948/92704B29D7/01B32B5/022B32B27/12B32B27/20B32B27/306B32B33/00B32B2307/7145
Inventor 彭呈褚鹏飞
Owner 常州绿之源高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap