Environmental-friendly heat-isolating high-performance aqueous damping coating and preparation method thereof

An environmentally friendly, damping coating technology, applied in the coating and other directions, to achieve the effect of strong decoration, good hiding power and wide damping temperature range

Inactive Publication Date: 2017-06-13
SOUTH CHINA UNIV OF TECH
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The addition of rigid polyurethane foam can not only solve the recycling problem of waste polyurethane rigid foam, but also reduce the cost of water-based damping coatings, and also enhance the function of water-based damping coatings, killing three birds with one stone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] An environmentally friendly heat-insulating high-performance water-based damping coating prepared from the following components by weight: DOW PRIMAL with a Tg of -20°C TM 20 parts of AC-8556 pure acrylic elastic emulsion; 15 parts of KLS-9345 pure silicone acrylic emulsion with Tg=0℃ and core-shell structure; KLS-9345 pure silicone acrylic emulsion with Tg=40℃ 10 parts of silicone acrylic emulsion; inorganic filler (10 parts of 800 mesh mica powder, 5 parts of 800 mesh heavy calcium, 5 parts of 1250 mesh talc powder); 15 parts of 400 mesh polyurethane rigid foam powder; 5 parts of damping pigment filler 400 mesh silicone rubber powder (produced by Tianjin Mingjintai Rubber & Plastic Technology Co., Ltd., 400 mesh); 5 parts of flame retardant melamine cyanurate (HT-211 of Taixing Chemical); 1.5 parts of antifreeze (propylene glycol); substrate wetting agent (Digao's Wet260) 0.5 parts; water-based wetting and dispersing agent (Hemings NUOSPERSE FX 365) 1.0 parts; water-...

Embodiment 2

[0044] An environmentally friendly heat-insulating high-performance water-based damping coating, prepared from the following components by weight: water-based emulsion (Dow PRIMAL with a Tg of -20°C TM AC-8556 pure acrylic elastic emulsion 15 parts, Tg = 0 ℃, Kelisen KLS-9345 pure silicon acrylic emulsion with core-shell structure 15 parts, Tg = 40 ℃ Kelisen XL-788 pure 15 parts of silicon-acrylic emulsion); inorganic filler (10 parts of 800 mesh heavy calcium, 5 parts of 800 mesh mica powder, 5 parts of 1250 mesh talc powder); 10 parts of 400 mesh polyurethane hard foam powder; 10 parts of damping pigment filler 400 mesh silicone rubber powder 5 parts (produced by Tianjin Mingjintai Rubber & Plastic Technology Co., Ltd., 400 mesh); 5 parts of flame retardant zinc borate (HT-207); 1.5 parts of antifreeze (propylene glycol), substrate wetting agent (Wet260 of Tego) 0.5 parts; water-based wetting and dispersing agent (Hemings NUOSPERSE FX 365) 1.0 parts; water-based defoamer (H...

Embodiment 3

[0053] An environmentally friendly heat-insulating high-performance water-based damping coating, prepared from the following components by weight: water-based emulsion (Dow PRIMAL with a Tg of -20°C TM 20 parts of AC-8556 pure acrylic elastic emulsion, Tg=0℃, 10 parts of KLS-9345 pure silicone acrylic emulsion with core-shell structure, Tg=40℃ of pure Kelisen XL-788 with core-shell structure 5 parts of silicon acrylic emulsion); inorganic filler (5 parts of 800 mesh heavy calcium, 10 parts of 800 mesh mica powder, 5 parts of 1250 mesh talc powder); 15 parts of 400 mesh polyurethane hard foam powder; 15 parts of damping pigment filler 400 mesh silicone rubber powder Parts (produced by Tianjin Mingjintai Rubber & Plastic Technology Co., Ltd., 400 mesh); flame retardant zinc borate (HT-207) 5 parts; antifreeze agent (propylene glycol) 1.5 parts; substrate wetting agent (Wet260 of Tego) 0.5 parts; water-based wetting and dispersing agent (Hemings NUOSPERSE FX 365) 1.0 parts; wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of coatings and discloses an environmental-friendly heat-isolating high-performance aqueous damping coating and a preparation method thereof. The coating is prepared from the following components in parts by weight: 30-45 parts of an aqueous emulsion, 5-20 parts of a damping pigment and filler, 10-20 parts of rigid polyurethane foam, 15-25 parts of inorganic filler, 5-10 parts of a flame retardant, 1-5 parts of an antifreezing agent, 0.5-1.0 part of a base material wetting agent, 1.0-5.0 parts of an aqueous wetting dispersing agent, 0.5-2.0 part of an aqueous defoamer, 0.5-3.0 parts of a coupling agent, 0.5-2.0 parts of a coalescing agent, 0.5-1.5 parts of a thickener and 5-10 parts of water. The aqueous emulsion is a self-crosslinked acrylate emulsion. The coating provided by the invention has the advantages of being high in damping value, wide in damping temperature domain, good in heat-isolating property and the like and is good in covering force to a base material and strong in decorativeness. The method provided by the invention is simple and easy to operate, and green and environmental-friendly.

Description

technical field [0001] The invention belongs to the technical field of coatings, and relates to an environmentally friendly heat-insulating high-performance water-based damping coating and a preparation method thereof. Background technique [0002] Damping coatings use the viscoelastic properties of organic polymer materials to convert the vibration mechanical energy of sound waves into thermal energy and dissipate them (ie, mechanical loss), thereby achieving the purpose of reducing amplitude, reducing vibration, and suppressing noise. [0003] As the society pays more and more attention to environmental protection, water-based damping coatings are currently being used in the fields of automobiles, trains, ships, aircraft, construction machinery and other household appliances to play the role of sound insulation, sound absorption, vibration reduction and heat preservation. The damping coating can play a damping and vibration reduction effect, which mainly depends on the int...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/12
CPCC09D143/04C08L2205/025C08L2205/035C09D7/61C09D7/65C09D133/04C08L43/04C08L75/04C08K13/02C08K3/34C08K2003/265C08K5/34928C08L33/04C08K2003/387
Inventor 涂伟萍阳红军凡宇卢明张明徽崔航唐成成
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com