Solvent-free single-component polyurethane adhesive for gravel water permeable pavement and preparation method of solvent-free single-component polyurethane adhesive
A technology of polyurethane adhesive and permeable pavement, applied in non-polymer adhesive additives, adhesive additives and other directions, can solve the problems of complex preparation process, poor impact resistance, high brittleness, etc., and achieve simple operation and convenient construction. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0024] Prepare 1000g of one-component polyurethane adhesive, 350g of polyether polyol (ring-opening of propylene oxide, end-capping of ethylene oxide, functionality of 2, molecular weight of 2000-3000) polyether polyol of formula quantity, polyether Add 80g of polyol (polyol with a functionality of 3 and a number average molecular weight of 300-500), 70g of castor oil and 100g of plasticizer (octyl epoxy soyate) into the reaction kettle at room temperature, heat up to 100°C, and dehydrate 1.5 hours (-0.1MPa vacuum), the moisture is lower than 0.1%, lower the temperature to 40°C, add polyphenyl polymethylene polyisocyanate 300g, antioxidant 1,3,5-trimethyl-2,4, 6-tris(3,5-di-tert-butyl-4-hydroxybenzene) 10g, UV absorber 2,4-tert-butyl-6-(5-chlorobenzotriazolyl-2) phenol 10g, Raise the temperature to 80°C for 2 hours, cool down to 65°C, add 5g of catalyst rare earth naphthenate, 50g of isocyanatopropyl triethoxysilane, 2-isopropyl-N-hydroxyethyl-oxazolidinate 15g of quasi-compo...
Embodiment 2
[0026] Prepare 1000g of one-component polyurethane adhesive, 280g of polyether polyol (ring-opening of propylene oxide, end-capping of ethylene oxide, functionality of 2, molecular weight of 2000-3000) polyether polyol of formula quantity, polyether Add 70g of polyol (polyol with a functionality of 3 and a number average molecular weight of 300-500), 80g of castor oil and 80g of plasticizer (octyl epoxy soyate) into the reaction kettle at room temperature, heat up to 100°C, and dehydrate 1.5 hours (-0.1MPa vacuum), the moisture is lower than 0.1%, lower the temperature to 40°C, add MDI and polyphenyl polymethylene polyisocyanate 140 and 300g, antioxidant 1,3,5-trimethyl -2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzene)benzene 5g, UV absorber 2,4-tert-butyl-6-(5-chlorobenzotriazolyl- 2) 5 g of phenol, react for 2 hours at 80 °C, cool down to 65 °C, add 8 g of catalyst rare earth naphthenate, 20 g of isocyanatopropyl triethoxysilane, 2-isopropyl-N-hydroxyethyl Base-oxazolidine es...
Embodiment 3
[0028] Prepare 1000g of one-component polyurethane adhesive, 300g of polyether polyol (opening of propylene oxide ring, end-blocking of ethylene oxide, functionality is 2, molecular weight is 2000-3000 polyol) of formula quantity, polyether Add 100 g of polyol (polyol with a functionality of 3 and a number average molecular weight of 300-500) and 80 g of plasticizer (epoxy soybean oleate) into the reactor at room temperature, raise the temperature to 100 ° C, and dehydrate for 1.5 hours (- 0.1MPa vacuum), the moisture is lower than 0.1%, lower the temperature to 40°C, add MDI and polyphenyl polymethylene polyisocyanate 70 and 300g, antioxidant 1,3,5-trimethyl-2,4 , 5g of 6-tris(3,5-di-tert-butyl-4-hydroxybenzene)benzene, 5g of ultraviolet absorber 2,4-tert-butyl-6-(5-chlorobenzotriazolyl-2)phenol , reacted at 80°C for 2 hours, lowered the temperature to 65°C, and added 5g of catalyst rare earth naphthenate, 30g of isocyanatopropyl triethoxysilane, 2-isopropyl-N-hydroxyethyl-ox...
PUM
![No PUM](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap