A kind of phosphating treatment process of steel

A phosphating treatment and steel technology, which is applied in the field of steel processing, can solve the problems of coarse and not dense phosphating film, unreachable treatment effect, and long treatment time, so as to improve compactness and adhesion, improve processing efficiency, and process The effect of shortening the duration

Active Publication Date: 2019-02-26
CHANGZHOU RAISED FLOOR SHANGHAI HUILI GROUP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Phosphating method is one of the existing methods for treating the surface of steel, but it has the problems that the phosphating film itself is relatively rough and not dense, has low adhesion, and the treatment time is long, and the treatment effect cannot reach people's ideal goals.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A phosphating treatment process for steel, comprising the steps of:

[0022] (1) Degreasing treatment:

[0023] Put the steel to be processed into the degreasing solution for degreasing treatment, and take it out for later use;

[0024] (2) Grinding treatment:

[0025] First use 80-mesh sandpaper to polish the steel after step (1), and then use 320-mesh sandpaper for secondary grinding;

[0026] (3) Washing treatment:

[0027] After washing away the debris and impurities on the surface of the steel material treated in step (2) with deionized water, dry it at a temperature of 80°C for later use;

[0028] (4) Phosphating treatment:

[0029] a. Take the material according to the corresponding weight portion and prepare it as a phosphating treatment solution for subsequent use; the mass fraction of each substance in the phosphating treatment solution is: 2% sodium dihydrogen phosphate, 0.3% phosphoric acid, 0.2% sodium nitrate, 0.1% nitric acid Zinc, 0.05% citric acid,...

Embodiment 2

[0035] A phosphating treatment process for steel, comprising the steps of:

[0036] (1) Degreasing treatment:

[0037] Put the steel to be processed into the degreasing solution for degreasing treatment, and take it out for later use;

[0038] (2) Grinding treatment:

[0039] First use 80-mesh sandpaper to polish the steel after step (1), and then use 320-mesh sandpaper for secondary grinding;

[0040] (3) Washing treatment:

[0041] After washing away the debris and impurities on the surface of the steel material treated in step (2) with deionized water, dry it at a temperature of 85°C for later use;

[0042] (4) Phosphating treatment:

[0043] a. Take the material according to the corresponding weight portion and prepare it as a phosphating treatment solution for subsequent use; the mass fraction of each substance in the phosphating treatment solution is: 3% sodium dihydrogen phosphate, 0.5% phosphoric acid, 0.4% sodium nitrate, 0.3% nitric acid Zinc, 0.15% citric acid,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a phosphorization treatment technology of steel, and belongs to the technical field of steel processing. The phosphorization treatment technology comprises the specific steps of (1) degreasing treatment; (2) polishing treatment; (3) water washing treatment; (4) phosphorization treatment; and (5) drying treatment. According to the phosphorization treatment technology, bonding strength of steel interferes can be effectively strengthened and can be improved by 20% or above, implementation of the surface bonding technology is better facilitated, the entire treatment time of the technology is shortened by 60% or above, the processing efficiency is remarkably improved, and quite good economic benefits are achieved.

Description

technical field [0001] The invention belongs to the technical field of steel processing, and in particular relates to a phosphating process for steel. Background technique [0002] Surface adhesive coating technology is a new technology that a composite material adhesive composed of high molecular polymer and special filler is coated on the surface of parts to achieve a certain purpose. The method of improving the interface bonding strength is mainly divided into two aspects. The first is to change the composition of the binder used in the composite material, and to improve the bonding force by modifying the binder. The second is the surface pretreatment of the metal substrate, which is also an important factor affecting the bonding strength of the adhesive / metal interface. Before bonding, a series of treatments are carried out on the metal surface to remove the oxide layer and dust on the metal surface to form a new surface, which can improve the strength of the metal inte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/42C23C22/78
CPCC23C22/42C23C22/78
Inventor 洪功正潘永刚蔡永波
Owner CHANGZHOU RAISED FLOOR SHANGHAI HUILI GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com