High-white-degree bagasse paper pulp and environment-friendly pulp preparation process thereof

A high-brightness, bagasse-based technology, applied in pulp bleaching, cellulose pulp post-treatment, washing/replacing pulp treatment liquid, etc., can solve problems such as high viscosity of black liquor, difficulty in evaporation and alkali recovery, and impact on the environment

Inactive Publication Date: 2017-06-20
芜湖市哈贝纸业有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, sugarcane pulping is mainly based on alkaline cooking. The traditional alkaline cooking has a low yield of pulp, and most of the silicon dissolves in the black liquor, resulting in high viscosity of the black liquor, difficulty in evaporation and alkali recovery, which seriously affects the environment, and the whiteness of the pulp is not good. High, unable to meet the production requirements of high whiteness paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of bagasse pulp with high brightness is produced by the following pulping process:

[0029] S1. Dedust and remove the pith from the air-dried bagasse, add distilled water 6 times the weight of the absolute dry bagasse, heat up to 120° C., keep warm for 30 minutes, filter, and take the filter bagasse to obtain pre-extracted bagasse;

[0030] S2, pre-extracting bagasse is packed into the digester, adding hydrogen peroxide, alkali and modified zeolite as cooking agent, the amount of hydrogen peroxide is 105% of the weight of pre-extracting bagasse, and the amount of alkali is the weight of pre-extracting bagasse The amount of zeolite is 1% of the pre-extracted bagasse weight, then add distilled water according to 4 times the pre-extracted bagasse weight, heat to 150 ° C, keep warm for 1.5h, and obtain the cooking material;

[0031] S3, cooling the cooking material, adding alkali, the amount of alkali is 1% of the weight of pre-extracted bagasse, and keeping the temp...

Embodiment 2

[0034] A kind of bagasse pulp with high brightness is produced by the following pulping process:

[0035] S1. Dedust and remove the pith from the air-dried bagasse, add distilled water 10 times the weight of the dry bagasse, heat up to 150° C., keep warm for 50 minutes, filter, and take the filter bagasse to obtain pre-extracted bagasse;

[0036] S2, pre-extracting bagasse is loaded into the digester, adding hydrogen peroxide, alkali and modified zeolite as cooking agent, the amount of hydrogen peroxide is 15% of the weight of pre-extracting bagasse, and the amount of alkali is the weight of pre-extracting bagasse The amount of zeolite is 5% of the pre-extracted bagasse weight, then add distilled water according to 8 times the pre-extracted bagasse weight, heat to 170 ° C, keep warm for 0.5h, and obtain the cooking material;

[0037] S3, cooling the cooking material, adding alkali, the amount of alkali is 1-5% of the weight of pre-extracted bagasse, and keeping the temperature...

Embodiment 3

[0040] A kind of bagasse pulp with high brightness is produced by the following pulping process:

[0041] S1. Dedust and remove the pith from the air-dried bagasse, add distilled water 8 times the weight of the absolute dry bagasse, heat up to 130° C., keep warm for 40 minutes, filter, and take the filter bagasse to obtain pre-extracted bagasse;

[0042] S2, pre-extracting bagasse is packed into a digester, adding hydrogen peroxide, sodium hydroxide and modified zeolite as a cooking agent, the amount of hydrogen peroxide is 13% of the weight of pre-extracting bagasse, and the amount of alkali is pre-extracting 15% of the weight of the bagasse, the amount of zeolite is 3% of the weight of the pre-extracted bagasse, and then add distilled water according to 6 times the weight of the pre-extracted bagasse, heat to 160 ° C, keep warm for 1 hour, and obtain the cooking material;

[0043] S3. Cool the cooking material, add sodium hydroxide, the amount of sodium hydroxide is 3% of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly pulp preparation process of high-white-degree bagasse paper pulp. The process comprises the following steps of S1, performing dust removal and devitalization on air dried bagasse; adding distilled water accounting for 6 to 10 times of the weight of the absolutely dried bagasse; raising the temperature to 120 to 150 DEG C; performing heat insulation for 30 to 50min; performing filtering; taking filter slag to obtain pre-extraction bagasse; S2, charging the pre-extraction bagasse into a steaming and boiling device; adding hydrogen sulfide, alkali and modified zeolite as the steaming and boiling agents; heating the materials to 150 to 170 DEG C; performing heat insulation to obtain steaming and boiling materials; S3, cooling the steaming and boiling materials; adding alkali; performing heat insulation at the temperature being 60 to 80 DEG C to obtain coarse pulp; S4, diluting the coarse pulp; repeatedly performing washing and purification; then, raising the pulp concentration to be higher than 20 percent to obtain the high-white-degree bagasse paper pulp. The invention also discloses the high-white-degree bagasse paper pulp. The bagasse is used as the raw material; the hot water extraction process is used; the zeolite is added, so that the bleaching efficiency is improved; the production cost is reduced; the paper pulp white degree is improved; the preparation process is reasonable; the efficiency is high.

Description

technical field [0001] The invention relates to the technical field of bagasse pulp, in particular to a high-whiteness bagasse pulp and an environmentally friendly pulping process thereof. Background technique [0002] Bagasse is a by-product of sugarcane sugar production. It can be used to make chemical pulp by conventional alkaline or kraft method. It is easy to boil and bleach, and has good pulp performance. The amount of chemicals used for cooking and bleaching is much less than that of wood. Bagasse pulp has a very mature black liquor alkali recovery technology. Since the fiber length of bagasse is 1.01-2.34 mm, which is equivalent to the fiber length of hardwood, the bagasse bleached chemical pulp is blended with certain long fibers to produce base paper that meets the quality indicators. At present, sugarcane pulping is mainly based on alkaline cooking. The traditional alkaline cooking has a low yield of pulp, and most of the silicon dissolves in the black liquor, re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21C1/02D21C7/00D21C9/02D21C9/16
CPCD21C1/02D21C7/00D21C9/02D21C9/163
Inventor 李先明
Owner 芜湖市哈贝纸业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com