Emulsion explosive and granulation method and physical sensitization mixing and granulation machine
An emulsified explosive and integrated machine technology, which is applied in explosives, explosive processing equipment, non-explosive/non-thermal agent components, etc., to achieve sufficient detonation energy, stable product quality, and stable quality
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0049] After the central controller 404 raises the temperature of the third temperature controller 403 to 30°C, the second temperature controller 402 to 45°C, and the first temperature controller 401 to 48°C, add the sensitized mixed material, mass ratio: emulsification Substrate 3kg, glass microspheres 1.243kg, titanium hydride 0.013kg; first add semi-emulsion matrix, 1 / 3 glass microspheres, control the stirring shaft 102 at 40 rpm, mix for 2min, add the remaining matrix and remaining glass microspheres , mix for 3 minutes, then add titanium hydride and mix for 2-3 minutes, open the conveying device and the pelletizing device until the material is discharged.
[0050] The detonation velocity of the prepared emulsion explosive is 2830m / s. Use this explosive to make explosives of the shape required for explosive welding. It is non-sticky, accurate in dosage, easy to control, even in laying, and high in efficiency. Welding, after the explosion, the titanium-aluminum composite in...
Embodiment 2
[0052] Raise the temperature of the third temperature controller 403 to 28°C through the central controller 404, raise the temperature of the second temperature controller 402 to 42°C, and raise the temperature of the first temperature controller 401 to 50°C, then add the sensitized mixed material, mass ratio: emulsification Substrate 3kg, glass microspheres 1.345kg, titanium hydride 0.066kg, first add half of the emulsified matrix, 1 / 2 glass microspheres, control the stirring shaft at 102 rpm and mix for 2 minutes, add the remaining emulsified matrix and the remaining glass microspheres , mixed for 3 minutes, then added titanium hydride and mixed for 2-3 minutes, after mixing, open the conveying device and the pelletizing device until the material is discharged.
[0053] The detonation velocity of the prepared emulsion explosive is 2900m / s. Use this explosive to make the explosive of the shape required for explosive welding. It is not sticky, accurate in dosage, easy to contro...
Embodiment 3
[0055] Raise the temperature of the third temperature controller 403 to 26°C through the central controller 404, raise the temperature of the second temperature controller 402 to 40°C, and raise the temperature of the first temperature controller 401 to 48°C, then add the sensitized mixed material, mass ratio: emulsification Matrix 2.8kg, glass microspheres 1.49kg, titanium hydride 0.175kg. First add half of the emulsified matrix, 1 / 3 glass microspheres, control the stirring shaft at 102 rpm and 42 rpm, mix for 2 minutes, add the remaining emulsified matrix and the remaining glass microspheres, mix for 3 minutes, then add titanium hydride and mix for 2- 3min, after mixing, turn on the conveying device and pelletizing device until the material is discharged.
[0056] The detonation velocity of the prepared explosive is 2780m / s. Use this explosive to make explosives of the shape required for explosive welding. It is not sticky, accurate in dose, easy to control, even in laying, ...