Steel structure water-based fireproof coating

A technology for fire-resistant coatings and steel structures, applied in fire-resistant coatings, anti-corrosion coatings, anti-fouling/underwater coatings, etc., can solve the problems of tensile and elastic modulus decline, and achieve good adhesion, heat insulation, flame retardant and fire resistance Excellent, good foaming effect

Inactive Publication Date: 2017-07-07
FUJIAN NAN FENG FIREPROOF TECH
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, as a building material, steel has some unavoidable defects in fire prevention. Its mechanical properties such as yield point, tensile strength and elastic modulus will drop sharply due to the increase of temperature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0064] The steel structure water-based fireproof coating is specifically composed of the following components by weight:

[0065] Water: 200, HEC Cellulose 2, AMP-95 Amine Neutralizer 2;

[0066] MC preservative 2, antifreeze 8, CF-10 wetting agent 2;

[0067] NXZ defoamer 2, 2400 dispersant 8, film-forming aid 15;

[0068] Titanium dioxide 25, barite powder 50;

[0069] Ammonium polyphosphate 250-300, melamine 88, pentaerythritol 90;

[0070] BLJ-660MV emulsion 200-250, 345 defoamer 2;

[0071] Leveling agent 3, thickener 1;

[0072] The sum of the parts by weight of the above-mentioned components is 1000 parts.

specific Embodiment 2

[0074] The steel structure water-based fireproof coating is specifically composed of the following components by weight:

[0075] Water: 200, HEC Cellulose 2, AMP-95 Amine Neutralizer 2;

[0076] MC preservative 2, antifreeze 8, CF-10 wetting agent 2;

[0077] NXZ defoamer 2, 2400 dispersant 8, film-forming aid 15;

[0078] Titanium dioxide 25, barite powder 50;

[0079] Ammonium polyphosphate 260, melamine 88, pentaerythritol 90;

[0080] BLJ-660MV emulsion 240, 345 defoamer 2;

[0081] Leveling agent 3, thickener 1;

[0082] The sum of the parts by weight of the above-mentioned components is 1000 parts.

specific Embodiment 3

[0084] The steel structure water-based fireproof coating is specifically composed of the following components by weight:

[0085] Water: 200, HEC cellulose 2.1, AMP-95 amine neutralizer 2.1;

[0086] MC preservative 2, antifreeze 8, CF-10 wetting agent 2;

[0087] NXZ defoamer 2.1, 2400 dispersant 8, film-forming aid 15;

[0088] Titanium dioxide 25, barite powder 50;

[0089] Ammonium polyphosphate 270, melamine 90, pentaerythritol 93;

[0090] BLJ-660MV emulsion 225, 345 defoamer 1.8;

[0091] Leveling agent 3, thickener 0.9;

[0092] The sum of the parts by weight of the above-mentioned components is 1000 parts.

[0093] This case also provides a preparation method of a steel structure water-based fireproof coating, the process steps are as follows:

[0094] (1) Put water into the mixing tank, start the mixer at 400-600 rpm, slowly add HEC cellulose, and stir until there is no powder on the surface;

[0095] (2) Accelerate the mixer to 1000-1200 rpm, put in AMP-95 am...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a steel structure water-based fireproof coating. The steel structure water-based fireproof coating is prepared from the following components in parts by weight: 180 to 220 parts of water, 1.8 to 2.2 parts of HEC cellulose, 1.8 to 2.2 parts of AMP-95 amine neutralizing agent, 1.8 to 2.2 parts of MC preservative, 7 to 9 parts of anti-freezing agent, 1.8 to 2.2 parts of CF-10 wetting agent, 1.8 to 2.2 parts of NXZ defoaming agent, 7.2 to 8.8 parts of 2400 dispersing agent, 13 to 17 parts of film forming aid, 22 to 28 parts of titanium dioxide, 45 to 55 parts of barite powder, 250 to 300 parts of ammonium polyphosphate, 80 to 96 parts of melamine, 80 to 100 parts of pentaerythritol, 200 to 250 parts of BLJ-660 MV emulsion, 1.5 to 2.5 parts of 345 defoaming agents, 2.5 to 3.5 parts of flatting agent and 0.9 to 1.1 parts of thickening agent. The steel structure water-based fireproof coating has the advantages of excellent heat insulation and flame-retardant fire resistance, excellent adhesiveness, good anticorrosion effect, antirust effect and mildew-proof effect, non-toxicity, no smoke, good safety and the like.

Description

technical field [0001] The invention relates to the technical field of fireproof coatings, in particular to a water-based fireproof coating for steel structures. Background technique [0002] Fire retardant coating is a special coating used to improve the fire resistance limit of the coated material. According to the different types of materials to be coated, fire retardant coatings are roughly divided into decorative fire retardant coatings, wood fire retardant coatings, steel structure fire retardant coatings, and so on. Steel is a non-combustible building material, which has the characteristics of earthquake resistance, bending resistance and so on. In practical applications, steel can relatively increase the load capacity of buildings, meet the needs of architectural design aesthetics, and avoid the defects of concrete and other building materials that cannot be bent and stretched. Therefore, steel has been favored by the construction industry. However, as a building m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D5/18C09D5/08C09D5/14C09D7/00C09D7/12
CPCC09D201/00C08L2201/02C09D5/08C09D5/14C09D5/18C09D7/20C09D7/44C09D7/61C09D7/63C08L1/02C08K13/02C08K2003/323C08K5/34922C08K5/053C08K2003/2241
Inventor 刘清良刘清凤郭春娥
Owner FUJIAN NAN FENG FIREPROOF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap