Plate glass highly doped with broken glass and preparation method of plate glass

A flat glass and broken glass technology, applied in the field of chemical metallurgy, can solve the problems of mechanical strength decline, glass brittleness, glass reduction, etc., and achieve the effects of reducing melting temperature, avoiding stones, and increasing the addition amount

Active Publication Date: 2017-08-04
HUNAN JUQIANG RENEWABLE RESOURCES SCI & TECH DEV CO LTD
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the mixing ratio of waste cullet is also different. If the mixing amount is too large, the quality of the glass will be reduced, the glass will become brittle, and the mechanical strength will decrease; if the mixing amount is too small, the effect of mixing will not be achieved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A flat glass highly mixed with cullet, including cullet and auxiliary materials, the mass-number ratio of which is 70:30, and the mass parts of each auxiliary material are 17.8 parts of silica sand, 0.6 parts of fluorite, 5.6 parts of dolomite, limestone 0.6 parts, 4.3 parts of soda ash, 0.3 parts of Glauber's salt, 0.4 parts of crystallization agent, 0.4 parts of coal powder; 0.4 parts of crystallization agent contains 0.03% of La lanthanum element, 0.02% of Er2O3 erbium oxide and other elements, among which La lanthanum element can be Improve gloss and improve the mechanical properties of glass; Er2O3 erbium oxide can enhance the ductility of glass.

[0028] A method for preparing flat glass highly mixed with cullet, comprising the following steps:

[0029] A. Pretreatment, and then the fine powder after being crushed by the rollers is lifted by the elevator to the hexagonal sieve. After the sieve, the coarse cullet returns to the rollers for secondary crushing. The f...

Embodiment 2

[0035] A flat glass highly mixed with cullet, including cullet and auxiliary materials, the mass-number ratio of cullet and auxiliary materials is 80:20, and the auxiliary materials include 14.1 parts of silica sand, 0.3 parts of fluorite, 3.2 parts of dolomite, 0.2 parts of limestone, soda ash 1.1 parts, 0.3 parts of Glauber's salt, 0.4 parts of crystallization agent, 0.4 parts of coal powder; 0.4 parts of crystallization agent contains 0.03% of La lanthanum element, 0.02% of Er2O3 erbium oxide and other elements, among which La lanthanum element can improve gloss and increase The mechanical properties of glass; Er2O3 erbium oxide can enhance the ductility of glass.

[0036] Its preparation method refers to embodiment 1.

Embodiment 3

[0038] A flat glass highly mixed with cullet, including cullet and auxiliary materials, the mass-number ratio of cullet and auxiliary materials is 90:10, and the auxiliary materials include 4.9 parts of silica sand, 1.2 parts of fluorite, 1.1 parts of dolomite, 0.6 parts of limestone, soda ash 1.1 parts, 0.3 parts of Glauber's salt, 0.4 parts of crystallization agent, 0.4 parts of coal powder; 0.4 parts of crystallization agent contains 0.03% of La lanthanum element, 0.02% of Er2O3 erbium oxide and other elements, among which La lanthanum element can improve gloss and increase The mechanical properties of glass; Er2O3 erbium oxide can enhance the ductility of glass.

[0039] Its preparation method refers to embodiment 1.

[0040] Ratio of cullet and accessories Heat consumption to generate 1kg glass molten silicate (KJ) Heat of formation (KJ) Heat consumption at 1500°C (KJ) Water evaporation heat consumption (KJ) Heat consumption of 1kg glass liquid (KJ) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a plate glass highly doped with broken glass. The plate glass contains broken glass and auxiliaries in a mass fraction ratio of (70 to 30)-(90 to 10), wherein the auxiliaries include silica sand, fluorite, dolomite, limestone, calcined soda, mirabilite, a crystallization agent and coal powder. By substantially increasing the adding amount of the broken glass, the efficient utilization of waste is realized, and meanwhile, the problem of clarifying of the glass in a secondary re-melting process can be solved. Meanwhile, the invention further discloses a preparation method of the plate glass highly doped with the broken glass. The preparation method comprises the following steps: preprocessing, examination, mixing, smelting, forming and the like. The preparation method is applied to cooperative preparation of the plate glass highly doped with the broken glass, the highest melting temperature of the plate glass is decreased, the service life of a kiln is prolonged, and the melting efficiency is improved.

Description

technical field [0001] The invention belongs to the field of chemical metallurgy, in particular to flat glass highly mixed with cullet and a preparation method thereof. Background technique [0002] With the development of science and technology and the progress of society, a large amount of cullet will be produced in the process of glass production, processing and use, and the waste of glass in society will also produce a large amount of waste cullet. According to the survey, there are hundreds of glass production enterprises in my country, and the damage of daily-use glass alone is about 2 million tons every year, while the recycling rate of cullet in my country is only about 20%. In recent years, with the mature development of glass production process control means and the fierce competition in the glass market. Reducing production costs and improving market competitiveness are issues that every enterprise must face squarely. There are many ways to reduce production cos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/02C03C6/06C03C6/04C03B18/02
CPCC03B18/02C03C1/00C03C1/002C03C1/004Y02P40/57
Inventor 冯朝辉
Owner HUNAN JUQIANG RENEWABLE RESOURCES SCI & TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap