Breaking-resistant shadow blue glaze porcelain bowl and preparation method thereof

A ceramic bowl and green glaze technology, applied in the field of porcelain bowl manufacturing, can solve the problems of not meeting practical application requirements, low mechanical strength, poor heat insulation performance, etc., to improve grade and market competitiveness, beautiful appearance, and improve insulation The effect of thermal performance

Inactive Publication Date: 2017-08-08
HEFEI HUAGAI BIOTECH CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, some physical and chemical performance indicators of porcelain tableware are insufficient at present, such as easy qualitative change, odor, excessive dissolution of trace elements and other factors that are not conducive to human health, and poor heat insulation performance and low mechanical strength cannot meet the actual application requirements. Therefore, , needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A drop-resistant blue-glazed ceramic bowl includes a base glaze, a surface glaze and a blank.

[0031] 1. Selection and preparation of bottom glaze raw materials

[0032] The bottom glaze of the shadow blue glaze ceramic bowl includes the following raw materials: feldspar 50kg, quartz 30kg, calcite 40kg, spodumene 30kg, burnt talc 25kg, charroite 30kg, flint 20kg, attapulgite clay 25kg;

[0033] Components required for the bottom glaze: SiO 2 9kg, Al 2 o 3 9kg, CaO 7kg, K 2 O 6kg, Na 2 O 6kg, MnO 2 5.5kg, B 2 o 3 4.5kg, MgO 4kg, Li 2 O 3kg, where the unavoidable impurity content is ≤1.0%;

[0034]The preparation of the bottom glaze: after the above-mentioned raw materials are analyzed by X-ray fluorescence, they are composed in proportion to meet the requirements of the material composition, and then the raw materials and water are mixed in a ratio of 1:1, and ball milled by a ball mill. When the fineness of the glaze slurry reaches 300 When the mesh sieve res...

Embodiment 2

[0048] A drop-resistant blue-glazed ceramic bowl includes a base glaze, a surface glaze and a blank.

[0049] 1. Selection and preparation of bottom glaze raw materials

[0050] The bottom glaze of the shadow blue glaze ceramic bowl includes the following raw materials: feldspar 55kg, quartz 35kg, calcite 45kg, spodumene 35kg, burnt talc 30kg, charroite 35kg, flint 25kg, attapulgite clay 30kg;

[0051] Components required for the bottom glaze: SiO 2 10kg, Al 2 o 3 9.5kg, CaO 8kg, K 2 O 7kg, Na 2 O 7kg, MnO 2 6kg, B 2 o 3 5.0kg, MgO 4.5kg, Li 2 O 3.5kg, of which unavoidable impurities ≤ 0.8%;

[0052] The preparation of the bottom glaze: after the above-mentioned raw materials are analyzed by X-ray fluorescence, they are composed in proportion to meet the requirements of the material composition, and then the raw materials and water are mixed in a ratio of 1:1, and ball milled by a ball mill. When the fineness of the glaze slurry reaches 300 When the mesh sieve residu...

Embodiment 3

[0066] A drop-resistant blue-glazed ceramic bowl includes a base glaze, a surface glaze and a blank.

[0067] 1. Selection and preparation of bottom glaze raw materials

[0068] The bottom glaze of the shadow blue glaze ceramic bowl includes the following raw materials: feldspar 60kg, quartz 40kg, calcite 45kg, spodumene 35kg, burnt talc 30kg, charroite 35kg, flint 25kg, attapulgite clay 30kg;

[0069] Components required for the bottom glaze: SiO 2 11.4kg, Al 2 o 3 9.7kg, CaO 8.4kg, K 2 O 7.6kg, Na 2 O 7.6kg, MnO 2 6.3kg, B 2 o 3 5.2kg, MgO 4.8kg, Li 2 O 3.7kg, of which unavoidable impurities ≤ 0.5%;

[0070] The preparation of the bottom glaze: after the above-mentioned raw materials are analyzed by X-ray fluorescence, they are composed in proportion to meet the requirements of the material composition, and then the raw materials and water are mixed in a ratio of 1:1, and ball milled by a ball mill. When the fineness of the glaze slurry reaches 300 When the mesh si...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a breaking-resistant shadow blue glaze porcelain bowl and a preparation method thereof, belonging to the porcelain bowl manufacturing field. The porcelain bowl comprises ground glaze, cover glaze and a preform body, wherein the ground glaze is prepared from the following chemical components: SiO2, Al2O3, CaO, K2O, Na2O, MnO2, B2O3, MgO and Li2O; the cover glaze is prepared from the following chemical components: SiO2, Fe2O3, ZnO, CaO, B2O3, K2O, Na2O, TiO2, BaO and MgO; and the preform body is prepared from the following raw materials: clay produced in Datong, Shanxi, attapulgite clay, purple sand, spodumene, hsianghualite, polypropylene, carbon fiber, cobalt oxide, zirconium oxide and polyethylene oxide. The preparation method comprises the steps of putting a preform body raw material into a ball grinder so as to be subjected to ball-milling firstly, then adopting a slurry ejection or plastic pressing flow compression method to prepare a semi-finished product, adding the ground glaze and the cover glaze on the semi-finished product by using a glaze dipping or glaze pouring method after bisque firing, and finally roasting again. The shadow blue glaze porcelain bowl is gentle in color and luster, excellent in texture, strong in heat-insulating property, high in mechanical strength, nonhazardous and non-residual, and does not cause harm to a human body.

Description

technical field [0001] The invention belongs to the field of porcelain bowl manufacture, and in particular relates to a shadow-resistant blue-glazed ceramic bowl and a preparation method thereof. Background technique [0002] Ceramic bowls are a large category of ceramic tableware. The traditional concept of ceramics refers to all artificial industrial products that use inorganic non-metallic minerals such as clay as raw materials. It includes various products made of clay or a mixture containing clay through kneading, shaping, and calcination. The firing and application of ceramic tableware has a long history in our country. Its various shapes, colorful colors, cool and smooth feel, easy to wash, are deeply loved by Chinese people. However, some physical and chemical performance indicators of porcelain tableware are insufficient at present, such as easy qualitative change, odor, excessive dissolution of trace elements and other factors that are not conducive to human healt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/02C03C8/04C04B33/13C04B33/36C04B41/86C04B41/89
CPCC03C8/02C03C8/04C04B33/13C04B33/36C04B35/63408C04B35/63452C04B41/009C04B41/52C04B41/86C04B41/89C04B2235/3224C04B2235/3427C04B2235/3472C04B2235/5248C04B41/504C04B41/5022
Inventor 张安育
Owner HEFEI HUAGAI BIOTECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com