Poly lactate geycollic acid and polycaprolactone complex fiber, preparation method and application thereof, and operation suture line

A technology of polylactide and polycaprolactone, which is applied in the direction of surgery, fiber treatment, and conjugated synthetic polymer artificial filaments, etc., can solve the problems that polylactide is expensive and restricts its wide application , to achieve the effect of increasing flexibility and good hand feeling

Active Publication Date: 2017-08-18
CHINESE TEXTILE ACAD
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, the polyethylene lactide used for biodegradable materials is difficult to be accepted by ordinary consumers clinically due to its expensive microscopic price. Therefore, its wide application is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Poly lactate geycollic acid and polycaprolactone complex fiber, preparation method and application thereof, and operation suture line
  • Poly lactate geycollic acid and polycaprolactone complex fiber, preparation method and application thereof, and operation suture line
  • Poly lactate geycollic acid and polycaprolactone complex fiber, preparation method and application thereof, and operation suture line

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0058] See attached figure 2 , the preparation method of polyethylene lactide and polycaprolactone composite fiber provided by the invention comprises the following steps:

[0059] Step 1: Obtain slices of polyethylene lactide and slices of polycaprolactone respectively;

[0060] Step 2: Carry out composite spinning for polylactide slices and polycaprolactone slices, so that polylactide is in the core layer of the composite fiber, and polycaprolactone wraps polylactide to form the core layer of the composite fiber Cortex, obtain polyethylene lactide and polycaprolactone composite fiber.

[0061] Among them, the process of composite spinning for polyethylene lactide chips and polycaprolactone chips includes:

[0062] Vacuum drying is carried out under the condition of 80° C. to 100° C., and the vacuum degree of vacuum drying ranges from -0.08 MPa to 0.09 MPa.

[0063] Wherein, in step 1, the method for obtaining polycaprolactone slices comprises the following steps:

[006...

Embodiment 1

[0093] The cross-sectional area ratio of the skin layer to the core layer (with PGLA as the core of the composite fiber and PCL as the skin of the composite fiber) is 20:80, and the spare PGLA / PCL are vacuum-dried separately at a drying temperature of 80°C. Vacuum degree-0.09MPa. The composite fiber described adopts spinning-stretching one-step method, and the draw ratio is 5 times. The monofilament fineness is 2.2dtex (50D / 24f). The spinning process conditions are: the temperature range of the core layer component is 220-240°C, the screw pressure is 9.8MPa, the spinning speed is 240m / min, the temperature range of the skin layer component is 150-180°C, the screw pressure is 8.0MPa, the spinning The yarn speed is 240m / min, air cooling, and the side blowing rate is 3m / min, and the PGLA / PCL composite fiber can be obtained.

[0094] The performance parameters of PGLA / PCL composite fiber are: the tensile strength reaches 4.5CN / dtex, the elongation at break is 27%, the handle is go...

Embodiment 2～20

[0096]

[0097]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Sticky numberaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a poly lactate geycollic acid and polycaprolactone complex fiber, a preparation method and application thereof, and an operation suture line. The complex fiber comprises a poly lactate geycollic acid fiber and a polycaprolactone complex fiber, wherein the poly lactate geycollic acid fiber is used as a core layer of the complex fiber, and the polycaprolactone fiber is used as a skin layer of the complex fiber. The preparation method comprises the following steps: obtaining poly lactate geycollic acid slices and polycaprolactone slices respectively; and performing composite spinning on the poly lactate geycollic acid slices and the polycaprolactone slices, wherein the poly lactate geycollic acid is used as the core layer, and the polycaprolactone covers the poly lactate geycollic acid to form the skin layer of the complex fiber so as to obtain the poly lactate geycollic acid and polycaprolactone complex fiber. The composite fiber can be used for the operation suture line. The operation suture line is prepared from the complex fiber. The complex fiber can not only alleviate the characteristic of easy degradation of the poly lactate geycollic acid fiber, but also can enhance the flexibility of the poly lactate geycollic acid fiber.

Description

technical field [0001] The invention relates to the technical field of composite fibers, in particular to a composite fiber of polyethylene lactide and polycaprolactone, its preparation method, application and surgical suture. Background technique [0002] The production process of polylactide is non-polluting, and the product can be biodegraded to realize the cycle in nature, so it is an ideal green polymer material. Polyethylene lactide is obtained by copolymerization of glycolide and lactide in different proportions. It has good biocompatibility, no resistance to the human body and good degradability. The degradation product is CO 2 and H 2 O, it is especially suitable for suturing wounds in the body, such as liver, spleen, gastrointestinal anastomosis, obstetrics and gynecology, fascial suture and plastic surgery, ophthalmology, microsurgery and general surgery, etc. Polycaprolactone is formed by ring-opening polymerization of ε-caprolactone under the condition of meta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F8/14A61L17/06A61L17/10D01D5/34D02G3/44
Inventor 刘伯林黄庆金剑
Owner CHINESE TEXTILE ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com