Terylene cleanroom clothes fabric coating adhesive and preparation method thereof

A technology of clean clothes and coating glue, which is applied in the fields of biochemical fiber treatment, fiber type, textiles and papermaking, etc., to achieve the effects of improving dust filtration, enhancing film-forming performance, and excellent washing resistance

Active Publication Date: 2017-08-18
DANDONG UNIK TEXTILE
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After modification, the fabric has good antistatic properties, except for this, the fabric has no other properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Add diphenylmethane diisocyanate (MDI) 50, polyethylene glycol 10 with an average molecular weight of 1450, polyethylene glycol 15 with an average molecular weight of 1000, and polybutadiene glycol 50 with an average molecular weight of 2000. 75°C, react for 2.5 hours, then cool down to 50°C, add styrene 10, neoprene rubber 10, methacryloyloxyethyltrimethylammonium chloride 5, deionized water 150, heat up to 75°C, add dropwise The mixed solution containing the initiator 2,2'-azodiisobutylamidine dihydrochloride 1 and deionized water 10 was added dropwise for 2 hours, then kept at 80°C for 1 hour, cooled to 45°C and discharged. Acrylic modified polyurethane emulsion;

[0028] The acrylic modified polyurethane emulsion 100 prepared above was added with polyurethane leveling rheology agent 2 and blocked isocyanate crosslinking agent 2, stirred evenly, and filtered to obtain a product with a viscosity of 3500 mPa·s.

Embodiment 2

[0030] Add diphenylmethane diisocyanate (MDI) 60, polyethylene glycol 12 with an average molecular weight of 1450, polyethylene glycol 16 with an average molecular weight of 1000, and polybutadiene diol 55 with an average molecular weight of 2000. 70 ° C, react for 2.6 hours, then cool down to 55 ° C, add styrene 12, neoprene rubber 15, methacryloyloxyethyl trimethyl ammonium chloride 6, deionized water 180, heat up to 70 ° C, add dropwise The mixed solution containing initiator 2,2'-azodiisobutylamidine dihydrochloride 1.5 and deionized water 15 was added dropwise for 2.2 hours, then kept at 81°C for 1 hour, cooled to 45°C and discharged to obtain Acrylic modified polyurethane emulsion;

[0031] The acrylic modified polyurethane emulsion 100 prepared above was added with polyurethane leveling rheology agent 3 and blocked isocyanate crosslinking agent 2.5, stirred evenly, and filtered to obtain a product with a viscosity of 3650 mPa·s.

Embodiment 3

[0033] Add diphenylmethane diisocyanate (MDI) 65, polyethylene glycol 14 with an average molecular weight of 1450, polyethylene glycol 18 with an average molecular weight of 1000, and polybutadiene glycol 58 with an average molecular weight of 2000. 78°C, react for 2.8 hours, then cool down to 56°C, add styrene 16, neoprene rubber 17, methacryloyloxyethyltrimethylammonium chloride 8, deionized water 190, heat up to 78°C, add dropwise The mixed solution containing initiator 2,2'-azobisisobutylamidine dihydrochloride 1.8 and deionized water 18 was added dropwise for 2.3 hours, then kept at 83°C for 1 hour, cooled to 45°C and discharged to obtain Acrylic modified polyurethane emulsion;

[0034] The acrylic modified polyurethane emulsion 100 prepared above was added with polyurethane leveling rheology agent 4 and blocked isocyanate crosslinking agent 3, stirred evenly, and filtered to obtain a product with a viscosity of 3800 mPa·s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a terylene cleanroom clothes fabric coating adhesive and a preparation method thereof. The terylene cleanroom clothes fabric coating adhesive is prepared by compounding 100 parts of acrylic acid modified polyurethane emulsion, 2 to 5 parts of a polyurethane flatting and rheological agent and 2 to 5 parts of an end-capped isocyanate cross-linking agent, wherein the acrylic acid modified polyurethane emulsion is prepared from the following raw materials in parts by weight: 50 to 70 parts of diphenylmethane diisocyanate, 10 to 15 parts of polyethylene glycol of which the average molecular weight is 1450, 15 to 20 parts of polyethylene glycol of which the average molecular weight is 1000, 50 to 60 parts of polybutadiene diol of which the average molecular weight is 2000, 10 to 20 parts of styrene, 10 to 20 parts of chloroprene rubber, 5 to 10 parts of methyl acrylyl ethyl trimethyl ammonium chloride, 150 to 200 parts of deionized water, and 1 to 2 parts of 2,2'-azobis(isobutylamidine dihydrochloride). Terylene conductive cloth finished by the coating adhesive has excellent antibacterial, anti-static, moisture permeable, air permeable and dust filtration performances, and excellent washing resistance.

Description

technical field [0001] The invention relates to a coating adhesive for textile fabrics, in particular to a coating adhesive for polyester clean clothing fabrics with functions of durable antibacterial, moisture permeability, antistatic, dust filtering and air permeability and a preparation method thereof. Background technique [0002] At present, the processing methods of clean clothing fabrics are mainly made by increasing the weaving density of the fabrics, inlaying conductive fibers and laminating PTFE on the fabrics to minimize the fabric voids. However, the products prepared by the above methods have high cost, antistatic Low air permeability, poor air and moisture permeability, and decreased mechanical properties. [0003] In 2009, the 22nd issue of "Printing and Dyeing" published "Wet Coating to Prepare Polyester Cleansing Clothing Fabric", which uses vinylidene chloride, polyethylene glycol, dimethylacetamide, dimethyl sulfoxide, lithium chloride, chlorine The coati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/356D06M15/564D06M13/395C08F283/00C08F212/08C08F220/34C08G18/76C08G18/69C08G18/48D06M101/32
CPCC08F283/006C08G18/4808C08G18/698C08G18/7671D06M13/395D06M15/356D06M15/564D06M16/00D06M2101/32C08F212/08
Inventor 张悦陈丽颖李喆孟雅贤
Owner DANDONG UNIK TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products