Kieselguhr board based on two to three-level kieselguhr and preparation method thereof

A technology of diatomite and diatom, applied in the field of building materials, can solve the problem of unable to replace decorative boards, etc., and achieve the effects of excellent humidity control, low density and low thermal conductivity

Active Publication Date: 2017-09-01
临江市绿苑环保科技有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to raw material problems, this kind of material can only be used as inner and outer wall materials, and cannot replace other decorative panels, such as furniture panels, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Kieselguhr board based on two to three-level kieselguhr and preparation method thereof
  • Kieselguhr board based on two to three-level kieselguhr and preparation method thereof
  • Kieselguhr board based on two to three-level kieselguhr and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] The preparation method of the above-mentioned diatomite board based on two or three grades of diatomite comprises the following steps:

[0042] Step 1, batching according to the proportioning ratio, stirring and mixing evenly to obtain the mixed material;

[0043] Among them, the stirring speed is generally 1200-1500r / min, and the time is 10-20min;

[0044]Step 2. After diluting the mixed material with water, stir evenly, pave and shape, remove moisture under negative pressure, and after heat balance, stand and solidify to obtain a slab;

[0045] Among them, the stirring speed is generally 1100 ~ 1300r / min, the time is 5 ~ 10min, the removal of moisture is generally under vacuum -0.05 ~ -0.1MPa for 10 ~ 60min, and the water content reaches 6 ~ 10%; the heat balance is preferably maintained at room temperature 5-6 days; static curing time is generally more than 24h;

[0046] Step 3, forming the slab by hot pressing to obtain a rough slab;

[0047] The pressure of hot ...

Embodiment 1

[0052] The diatomite board based on two or three grades of diatomite consists of two or three grades of diatomite (fineness 200 mesh, whiteness 80) of 40 parts by weight, pulp of 12 parts by weight, bisphenol A of 4 parts by weight, 25 parts by weight Parts by weight of expanded polystyrene, 7 parts by weight of sodium bicarbonate, 0.3 parts by weight of diatomaceous earth white carbon black loaded nano-titanium dioxide composite photocatalytic material (whiteness is 85, the loading of nano-titanium dioxide is 40%) composition .

[0053] The preparation method of the diatomite board based on the above-mentioned secondary and tertiary diatomite:

[0054] Step 1, batching according to the above proportioning ratio, stirring and mixing evenly to obtain the mixed material;

[0055] Wherein, the stirring speed is 1200r / min, and the time is 10min;

[0056] Step 2. After diluting the mixed material with water, stir evenly, pave and shape, remove moisture under negative pressure, an...

Embodiment 2

[0077] The diatomite board based on two or three grades of diatomite consists of two or three grades of diatomite (fineness 200 mesh, whiteness 80) of 30 parts by weight, paper pulp of 10 parts by weight, bisphenol A of 3 parts by weight, 20 Parts by weight of expanded polystyrene, 5 to 8 parts by weight of azodicarbonamide, 0.1 parts by weight of diatomaceous earth white carbon black loaded nano-titanium dioxide composite photocatalytic material (the whiteness is 80, and the loading capacity of nano-titanium dioxide is 40%, grain size ≤ 15nm) composition.

[0078] The preparation method of the diatomite board based on the above-mentioned secondary and tertiary diatomite:

[0079] Step 1, batching according to the above proportioning ratio, stirring and mixing evenly to obtain the mixed material;

[0080] Wherein, the stirring speed is 1500r / min, and the time is 10min;

[0081] Step 2. After diluting the mixed material with water, stir evenly, pave and shape, remove moisture...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
crystal sizeaaaaaaaaaa
whitenessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a kieselguhr board based on two to three-level kieselguhr and a preparation method thereof, belongs to the technical field of building materials and solves the technical problem that an application range of kieselguhr boards in the prior art is limited. The kieselguhr board disclosed by the invention is prepared from 30 to 45 weight parts of two to three-level kieselguhr, 10 to 15 weight parts of plant fiber, 3 to 5 weight parts of bisphenol A, 25 to 30 weight parts of expansible polystyrene, 5 to 8 weight parts of foaming agent and 0.1 to 0.5 weight part of kieselguhr white carbon black loaded with nano titanium dioxide compound photocatalytic material. The kieselguhr board not only has necessary breaking strength, but also has light weight, heat insulation, water and moisture resistance and functions of automatically adjusting indoor humidity, adsorbing harmful gas, keeping indoor cleaning and the like, can obviously improve an indoor human settlement environment and improve crowd living quality and is suitable for being used as building indoor ceilings, decoration boards, light partition boards and the like.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a diatomite board based on secondary and tertiary diatomite and a preparation method thereof. Background technique [0002] With the rapid development of the national economy and the continuous improvement of living standards, urban and rural residents have put forward higher and higher requirements for the quality of living environment, especially the comfort and safety of living space. Now in the market, the commonly used decoration boards are wood boards and medium and high density fiberboards. Because of its high price, difficult maintenance, and easy deformation, planks should not be too cold or too hot, nor too wet or too dry, so they cannot be used universally. Medium and high-density fiberboards are widely used due to their excellent physical properties, but ordinary medium and high-density fiberboards have many defects, such as the ability to rele...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B30/02C04B38/02C04B38/08C04B14/08C04B16/08C04B111/20C04B111/40
CPCC04B30/02C04B2111/00025C04B2111/2092C04B2111/40C04B2201/32C04B14/08C04B16/08C04B18/241C04B24/02C04B22/10C04B14/06C04B14/305C04B20/008C04B38/02C04B24/129C04B24/16
Inventor 王秀宝
Owner 临江市绿苑环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap