Efficient long-lasting graphene anti-ultraviolet fabric and preparation method thereof

A technology of graphene and graphene fiber, applied in fabric surface trimming, textile material treatment, liquid/gas/steam textile material treatment, etc., can solve the problems of poor anti-ultraviolet performance and durability, and achieve anti-ultraviolet effect High, novel material, high-efficiency and long-term anti-ultraviolet effect

Inactive Publication Date: 2017-09-01
NANTONG QIANGSHENG GRAPHENE TECH CO LTD
View PDF9 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention mainly uses the long-lasting super-ultraviolet resistance of graphene fibers after adding graphene fibers to solve the problems of anti-ultrav

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Efficient long-lasting graphene anti-ultraviolet fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0036] Example 1

[0037] This embodiment provides a high-efficiency and long-lasting graphene anti-ultraviolet fabric, the fabric is woven from warp yarns and weft yarns; the weft yarns are graphene yarns; the graphene yarns include the following components by mass percentage : Graphene graphene nylon blended yarn 40%; cotton fiber 60%. In the graphene-graphene nylon blended yarn, the mass content of graphene is 3%; the graphene raw material used is graphene. The graphene fiber is made by melt spinning method. The warp yarn is polyester yarn.

[0038] The preparation method of the high-efficiency and long-lasting graphene anti-ultraviolet fabric includes the following steps:

[0039] A1. Prepare the warp and weft, and use the loom to weave; when weaving, the width of the upper machine is 147cm, the weft density of the upper machine is 152 / in, and the brown method is used to pass through 1-12 pages. The text plate is made of plain weave.

[0040] A2. Desizing after weaving.

[0041]...

Example Embodiment

[0047] Example 2

[0048] This embodiment provides a high-efficiency and long-lasting graphene anti-ultraviolet fabric, the fabric is woven from warp yarns and weft yarns; the weft yarns are graphene yarns; the graphene yarns include the following components by mass percentage : Graphene polyester filament 45%; viscose fiber 55%. In the graphene polyester filament, the graphene mass content is 4.5%; the graphene raw material used is graphene oxide. The graphene fiber is made by dry spinning method. The warp yarn is nylon yarn.

[0049] The preparation method of the high-efficiency and long-lasting graphene anti-ultraviolet fabric includes the following steps:

[0050] A1. Prepare the warp and weft, and use the loom to weave; when weaving, the width of the upper machine is 147cm, the weft density of the upper machine is 152 / in, and the brown method is used to pass through 1-12 pages. The text plate is made of plain weave.

[0051] A2. Desizing after weaving.

[0052] A3. Keep the te...

Example Embodiment

[0058] Example 3

[0059] This embodiment provides a high-efficiency and long-lasting graphene anti-ultraviolet fabric. The fabric is woven from warp yarns and weft yarns; both weft yarns and warp yarns are graphene yarns; and the graphene yarns include the following mass percentages Each component: graphene nylon blended yarn 50%; silk fiber 40%. In the graphene nylon blended yarn, the mass content of graphene is 5%; the graphene raw material used is amino-modified graphene. The graphene fiber is prepared by solution spinning method. The warp yarns are acrylic yarns.

[0060] The preparation method of the high-efficiency and long-lasting graphene anti-ultraviolet fabric includes the following steps:

[0061] A1. Prepare the warp and weft, and use the loom to weave; when weaving, the width of the upper machine is 147cm, the weft density of the upper machine is 152 / in, and the brown method is used to pass through 1-12 pages. The text plate is made of plain weave.

[0062] A2. Desiz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an efficient long-lasting graphene anti-ultraviolet fabric and a preparation method thereof. The fabric is obtained by spinning warp yarns and weft yarns; at least one of the warp yarns and weft yarns is a graphene yarn; the graphene yarn is prepared from, by mass, 40-50% of graphene fibers and 50-60% of other fibers. The invention also provides the preparation method of the fabric which breaks through a traditional anti-ultraviolet performance fabric manufacturing method; novel graphite fiber materials are adopted to further strengthen anti-ultraviolet absorbing performance, thus the fabric does not use anti-ultraviolet shielding agent in the dyeing process, is not affected by the number of washing, and the layer processing is not performed on the fabric, which achieves the permanent anti-ultraviolet performance. Therefore, the efficient long-lasting graphene anti-ultraviolet fabric has the advantages of having the permanent anti-ultraviolet effect; being novel in materials, strong in practicability; being capable of being widely used in sports, swimwear, sanitation, tents, military projects, civil and the like.

Description

technical field [0001] The invention relates to the technical field of new materials, in particular to a high-efficiency and long-lasting graphene anti-ultraviolet fabric and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, the progress of industrial modernization, the development of textile functional textiles, and the reduction of available arable land, it is required that the direction of textile development tends to be functional and healthy, energy-saving and environmentally friendly, and fashionable and beautiful. Therefore, during the "Twelfth Five-Year Plan" period, regenerated fibers have been widely used, and the defects of natural fibers are made up for by regenerated fibers, and the function and health of regenerated fibers have been our research topics in the textile field in recent years. Functional fibers can effectively increase the added value of its textile products, enhance the function and grad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D13/00D03D15/00D06B3/10D06C7/02D06C15/00
CPCD03D13/008D03D15/00D06B3/10D06C7/02D06C15/00D10B2101/02D10B2101/10D10B2101/12D10B2201/01D10B2201/02D10B2201/24D10B2321/10D10B2331/02D10B2331/04D03D15/47
Inventor 沙嫣沙晓林
Owner NANTONG QIANGSHENG GRAPHENE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap